Abstract:Materials and Methods: Polycaprolactone (PCL) and polycaprolactone-hydroxyapatite (PCL-HA) scaffolds with 600-mu m pore size were fabricated by drop-on-demand printing (DDP) structured porogen method followed with injection molding. Specimens with special dimensions of 4.2x4.2x5.4 mm(3) and 6.6x6.6x13.8 mm(3) were designed and fabricated for compression and tensile tests, respectively. The mechanical study was performed on both solid and porous PCL and PCL-HA samples. The effect on mechanical properties of the HA content ratio in PCL-HA composites was investigated. Results: Porous scaffold made of 80/20 PCL-HA composite had an ultimate compressive strength of 3.7 +/- 0.2 MPa and compression modulus of 61.4 +/- 3.4 MPa, which is in the range of reported trabecular bone's compressive strength. Increasing the concentration of HA in the composites raised compressive properties and stiffness significantly (P<0.05), which demonstrates that PCL-HA composites have the potential for application in bone regeneration. Tensile test of solid PCL and PCL-HA composites showed that the ultimate tensile strength and tensile modulus increased with increases of the concentration of HA in the composites. The tensile test was also conducted on PCL porous scaffold; the result indicated that the scaffold was slightly softer and weaker in tension compared with compression. Conclusions: Combining compression and tensile test results, our study may guide the possible application of these biomaterials in bone tissue engineering and support further development of microstructure-based models of scaffold mechanical properties.

Preparation of Porous Biphasic Calcium Phosphate/Polylactide Scaffolds

Preparation and Performance of Silk Sericin/Hydroxyapatite Composite Bone Scaffold

Preparation of Porous Poly(Lactic Acid)/Tricalcium Phosphate Composite Scaffolds for Tissue Engineering

Preparation of Porous Hydroxyapatite-Zirconia Composite Scaffolds by Combination of Gel-Casting and Polymer Sponge Methods

Mechanical study of polycaprolactone-hydroxyapatite porous scaffolds created by porogen-based solid freeform fabrication method.

Preparation and Evaluation of Porous Poly(3-hydroxybutyrate-co-3-hydroxyhexanoate)— Hydroxyapatite Composite Scaffolds

Preparation And Characterization Of Porous B-Tcp/Plla Composites With High Beta-Tcp Content

Preparation and Characterization of Porous β-TCP/PLLA Composites with High β-TCP Content

Preparation and characterization of a novel polylactic acid/hydroxyapatite composite scaffold with biomimetic micro-nanofibrous porous structure

Preparation, characterization and cytocompatibility of porous ACP/PLLA composites.

Production of Poly(ε-Caprolactone)/Hydroxyapatite Composite Scaffolds with a Tailored Macro/Micro-Porous Structure, High Mechanical Properties, and Excellent Bioactivity

Preparation And Morphology Of Porous Nanocalcium Phosphate/Poly(L-Lactic Acid) Composites

Preparation and characterization of interpenetrating phased TCP/HA/PLGA composites

Fabrication, Characterization and Cellular Biocompatibility of Porous Biphasic Calcium Phosphate Bioceramic Scaffolds with Different Pore Sizes

Preparation and performance of poly (vinyl alcohol)/polylactic acid/hydroxyapatite composite scaffolds based on 3D printing

Preparation Of Bioactive Beta-Tricalcium Phosphate Scaffold With Bone-Like Structure

Morphology, Wettability, and Mechanical Properties of Polycaprolactone/hydroxyapatite Composite Scaffolds with Interconnected Pore Structures Fabricated by a Mini‐deposition System

The Preparation and Characterization of Porous Scaffold Made of Nano-Hydroxyapatite/chitosan Composite for Bone Tissue Engineering

Preparation and Properties of Calcium Sulfate Dihydrate/beta-Tricalcium Phosphate/Polylactide Composite

Porous Morphology, Porosity, Mechanical Properties Of Poly(Alpha-Hydroxy Acid)-Tricalcium Phosphate Composite Scaffolds Fabricated By Low-Temperature Deposition

Solid Freeform Fabrication of Polycaprolactone∕Hydroxyapatite Tissue Scaffolds