Abstract:Nanocrystalline Ti1- x Crx O2 (0 ≤ x ≤ 0.20) samples were synthesised via acid-modified sol-gel process and characterised with various techniques, such as HRTEM, FESEM, Raman, XPS, DTA and VSM. The TEM image of TiO2 exhibits elongated nanoparticles with an average size of 10 nm. The HRTEM in combination with selected area electron diffraction (SAED) reveals the interplanar spacing and polycrystalline nature of the samples, respectively. FESEM micrographs divulge nonuniform morphologies and less aggregation of the particles in the doped sample. Raman spectra ensure the phase purity of the samples and a blue shift on Cr doping. X-ray photoelectron spectra (XPS) predict the chemical state of the elements and oxygen vacancies in the prepared samples. Room temperature magnetic measurements exhibit a significant variation in the magnetic parameters on Cr doping in TiO2 . The differential thermal analysis (DTA) shows the structural phase transition at ∼630°C. The photocatalytic performance is studied for the degradation of methylene blue (MB) dye under visible light irradiation. A higher photocatalytic efficiency is found for the 20% of Cr-doped TiO2 . These studies propose that the appropriate incorporation of Cr ions makes TiO2 very efficient for visible light-driven photocatalysts required for applications in wastewater treatment. LAY DESCRIPTION: In the present study, nanoparticles of TiO2 and Cr-doped TiO2 have been synthesised by a cost-effective acid-modified sol-gel process. The effect of Cr doping on the microstructure, thermal, magnetic and photocatalytic properties of TiO2 were explored in detail. The transmission electron microscopy (TEM) images exhibit the presence of elongated nanoparticles with an average size of 10 nm. Field emission scanning electron microscopy (FESEM) was used to study the surface morphology of the synthesised materials, which revealed nonuniform morphologies and less aggregation of the particles in the Cr-doped sample. Energy dispersive x-ray spectroscopy (EDS) confirms the elemental compositions with the appropriate stoichiometry of the elements. Raman spectra ensure the phase purity of the materials and also a blue shift with the incorporation of Cr ions in TiO2 . X-ray photoelectron spectra (XPS) predict the chemical state of the elements and oxygen vacancies in the prepared samples. The magnetic nature of all the synthesised samples was examined through the vibrating sample magnetometer (VSM) and revealed weak ferromagnetic behaviour of the samples. These results signify that the oxygen vacancies and defects play a crucial role in developing the ferromagnetic nature of oxide semiconductors. The differential thermal analysis (DTA) shows the structural phase transition at ∼630°C. The photocatalytic performance of the prepared samples was studied for the degradation of methylene blue (MB) dye under irradiation of visible light. A higher photocatalytic efficiency was found for the 20% of Cr-doped TiO2 . These studies propose that the appropriate incorporation of Cr ions makes TiO2 very efficient for visible light-driven photocatalysts required for applications in wastewater treatment.

Synthesis, Characterization of Cr-doped TiO 2 Nanotubes with High Photocatalytic Activity

Preparation and Photocatalytic Activities of TiO2 Nanotubes with Mixed Crystal Structure

Facile Fabrication of N-doped TiO2 Nanocatalyst with Superior Performance under Visible Light Irradiation

The Fabrication and Characterization of Novel Carbon Doped TiO2nanotubes, Nanowires and Nanorods with High Visible Light Photocatalytic Activity

Fabrication of V-Doped TiO2 Nanoparticles and Photocatalytic Studies under Visible Light

Physical properties and photocatalytic activity of Cr-doped TiO2 nanoparticles

Enhanced Optical Absorption and Photocatalytic Activity of Cu/N-Codoped Tio2 Nanocrystals

Preparation of Nanoparticle WO_3-doped TiO_2 and Research on Its Photocatalytic Activity

Synthesis and Photocatalysis Properties of Sulfur Doped Nanocrystalline TiO2 Photocatalyst

Surface roughening and top opening of single crystalline TiO2 nanowires for enhanced photocatalytic activity

Preparation of Iron and Chromium Co-Doped TiO2 Nanotubes and Study of Their Photoelectrochemical Properties

Characterization, Properties and Catalytic Application of TiO2 Nanotubes Prepared by Ultrasonic-Assisted Sol-Hydrothermal Method

PREPARATION OF IRON-DOPED TITANIA NANOCRYSTALLINE GRAINS AND ITS PHOTOCATALYTIC PROPERTY

Characterization and photocatalytic activity of Ni-doped tiO2 nano photocatalysts prepared by low temperature combustion synthesis]

Preparation of PW12O403−/Cr–TiO2 Nanotubes Photocatalysts with the High Visible Light Activity

Iron-doped TiO2 nanotubes with high photocatalytic activity under visible light synthesized by an ultrasonic-assisted sol-hydrothermal method

TiCr Alloy Anodization for Cr-doped TiO2 Nanotube Array with Improved Photocatalytic Activity

Preparation of Fe3+ Doped High-Ordered TiO2 Nanotubes Arrays with Visible Photocatalytic Activities

Coll 282-Photocatalytic Degradation Of Gaseous Toluene Over N-Doped Nanocrystalline Tio2 With Enhanced Activity Under Uv And Visible Light Irradiation

Effect of Calcination on Structure and Photocatalytic Property of N-TiO2/g-C3N4@diatomite Hybrid Photocatalyst for Improving Reduction of Cr(Ⅵ).

Preparation and Characterization of Ni、Co、Cr、V Doped TiO_2 Nanoparticles