Microwave-assisted synthesis and magnetic properties of size-controlled CoNi/MWCNT nanocomposites
Huaqiang Wu,Peipei Cao,Wenting Li,Na Ni,Lulu Zhu,Xiaojun Zhang
DOI: https://doi.org/10.1016/j.jallcom.2010.09.209
IF: 6.2
2011-01-01
Journal of Alloys and Compounds
Abstract:Research highlights ▶ Size-controlled CoNi alloy nanoparticles with quasi-spherical and face-centered cubic structure attached uniformly on the surface of multi-walled carbon nanotubes were prepared by microwave-assisted method. ▶ The size of CoNi alloy nanoparticles with average diameters in the range of 15–48 nm can be controlled though adjusting the atomic ratios of metals to carbon nanotubes in the mixed acetate solution. ▶ Magnetic measurement shows that both the coercivity and the saturation magnetization increase with the increase of the particle size from 15 nm to 37 nm, and decrease from 37 nm to 48 nm. Abstract Size-controlled CoNi alloy nanoparticles with average diameters in the range of 15–48 nm attached on the multi-walled carbon nanotubes (MWCNTs) were prepared to form CoNi/MWCNT nanocomposites by microwave-assisted method. The size of CoNi alloy nanoparticles can be controlled through adjusting the atomic ratios of metals to carbon nanotubes in the mixed acetate solution. The as-prepared nanocomposites have been characterized by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), selected area electron diffraction (SAED), energy-disperse X-ray spectroscopy (EDS) and vibrating sample magnetometer (VSM). The results show that CoNi alloy nanoparticles are face-centered cubic structure, quasi-spherical and disperse uniformly on the surface of MWCNTs. Magnetic measurement shows that both the coercivity and the saturation magnetization of the samples increase with the increase of the particle size from 15 to 37 nm, and decrease from 37 to 48 nm. Keywords CoNi alloy Carbon nanotubes Magnetic properties Microwave 1 Introduction Magnetic nanoparticles have important applications as catalysts, magnetic fluids, and high-density recording media. As important transition metal alloys, CoNi alloys have been widely used for decoration, corrosion resistance and magnetic recording devices, and catalysts, etc. [1–5] . In such applications, composition of CoNi alloy nanoparticles is considered the key characteristic affecting their magnetic properties and has been investigated by different methods [6–9] . In addition to the composition, the shape and size of the magnetic nanoparticles are also key factors in the applications mentioned above. Recently, shape- and size-controlled synthesis of the magnetic nanoparticles has been an active research area owning to their shape- and size-dependent electrical, optical and magnetic properties [10–12] . For example, magnetic recording density is remarkably enhanced as the size of magnetic particles decreases. CoNi alloy nanoparticles with different shapes and sizes have been prepared such as nanowires [13,14] , bracelet-like [15] , chain-like [16] , handkerchief-like [6] , and film [3,17] , etc. The multi-walled carbon nanotubes (MWCNTs) have been widely applied as a promising support material in many areas of science and technology due to their specific characteristics such as large surface area to volume ratio, good adsorption, unique structure, and high thermal and chemical stability. As is well-known, there have been various approaches to deposit monometal magnetic nanoparticles such as Ni [18] , Co [19] , Fe [20] , Fe 2 O 3 [21] and Fe 3 O 4 [22] on the surface of MWCNTs by microwave irradiation heating method, chemical precipitation and deoxidization method, pyrolysis of ferrocene, chemical precipitation, and by using ethylene glycol as reductant, respectively. In these methods, microwave-assisted synthesis has remarkable advantages of short reaction time, small particle size, narrow particle size distribution, high purity of the products and eco-friendly. In our previous work [23,24] , we found that microwave-assisted synthesis in the deposition of nanoparticles onto MWCNTs is a very useful and powerful method to directly control the size, morphology, structure, and loading of nanoparticles. In this work, we attempted to extend this microwave-assisted method to prepare size-controlled CoNi alloy nanoparticles attached on the outer surface of the MWCNTs and to study the effect of the change in the size of CoNi alloy nanoparticle on the magnetic properties. Experimental results demonstrated that CoNi alloy nanoparticles with quasi-spherical and face-centered cubic structure have been attached on the MWCNTs. The size of CoNi alloy nanoparticles with an average diameter of 15–48 nm can be controlled through adjusting the atomic ratios of metals to carbon nanotubes (3, 7, 12, and 18 at%, respectively) in the mixed acetate solution. Magnetic measurement confirmed that both the coercivity ( H c) and the saturation magnetization ( M s) of the samples first increase with the increase of the size, then decrease with the increase of the size of CoNi alloy nanoparticles on the MWCNTs. Moreover, a possible mechanism of formation was discussed. 2 Experimental The MWCNTs with a purity of about 95% were provided by Shenzhen Nanoport Company, which were produced via catalytic decomposition of hydrocarbon. For the better anchoring of the nanoparticles, the MWCNTs were refluxed in concentrated nitric acid for 4 h, then purified by distilled water, and finally dried at 100 °C for 24 h. All chemicals were of analytical grade and used as received without further purification. In a typical synthesis, 0.0300 g of the acid-treated MWCNTs was mixed with 0.0187 g of Co(Ac) 2 ·4H 2 O and 0.0187 g of Ni(Ac) 2 ·4H 2 O (Co:Ni = 1:1 atomic ratio) in ethylene glycol (25 mL). After stirring the mixture for 24 h, an appropriate NaOH solution was added to the mixture to adjust the pH to 10. Simultaneously, several drops of hydrazine hydrate were added as a reducing agent. Subsequently, the mixture was added in a 100 mL round-bottom bottle, which was placed in a microwave refluxing system (National N-S570MFS microwave oven, 2450 MHz, 900 W, Sanle General Electric Corp. Nanjing, China) at 600 W for 2 min. The as-obtained samples were washed with distilled water and absolute ethanol several times to remove possible residual impurities. The products were dried at 60 °C in a vacuum oven before being further characterized. By varying the atomic ratios of the metals to carbon nanotubes, different atomic ratios (3, 7, 12 and 18 at%) of CoNi/MWCNT nanocomposites were prepared according to the above methods. The as-obtained samples were characterized by X-ray powder diffraction (XRD) on an XRD-6000 (Japan) X-ray diffractometer with Cu-K α radiation ( λ = 0.154060 nm) at a scanning rate of 0.05° s −1 in the 2 θ range from 20° to 80°. The morphology and size of as-obtained products were observed by transmission electron microscopy (TEM) carried out on a Hitachi H-800 transmission electron microscope and scanning electron microscopy (SEM) operated on a Hitachi S-4800 scanning electron microscope. High-resolution transmission electron microscopy (HRTEM) and selected area electron diffraction (SAED) were performed using JEM 2010F field emission microscope operated at optimum defocus with accelerating voltages of 200 kV. Energy-dispersive X-ray spectrometry (EDS) was carried out with spectroscope attached to HRTEM, which was used for elemental analysis. The magnetic hysteresis loop of sample was measured by vibrating sample magnetometer (VSM, BHV-55, Japan) with an applied field ± 10 kOe at room temperature. 3 Results and discussion 3.1 Characterization of the samples Fig. 1 shows the XRD patterns of different atomic ratios of metals to carbon nanotubes (3, 7, 12 and 18 at%) samples at room temperature. The peak at 2 θ value of 26.13° arising from the carbon nanotubes corresponds to its (0 0 2) crystal plane. The peaks at 2 θ values of 44.38°, 51.48°, and 76.45° correspond to the crystal planes of the (1 1 1), (2 0 0), and (2 2 0) of face-centered cubic (fcc) CoNi nanoparticle, which are in good accordance with reported literature value [6] . The cell parameters were calculated from the XRD pattern and the results were displayed in Fig. 2 . It can be seen that the cell parameter of CoNi nanoparticle is nearly a consent (0.35416 nm) and larger than that of fcc Ni (0.35238 nm) and smaller than that of fcc Co (0.35447 nm) [25] , this confirms that CoNi nanoparticle is fcc phase. And there were no observable peaks in the XRD spectra corresponding to those of pure cobalt and nickel, so the homogeneous solid solution of CoNi should have been formed. These facts confirm that Co and Ni formed an alloy, rather than separate grains [16] . The average crystallite size for different atomic ratios (3, 7, 12, and 18 at%) of CoNi/MWCNTs, calculated using the Debye–Scherrer formula based on the full width at half-maximum of the (1 1 1) diffraction peak, was 12.1, 21.2, 36.9, and 42.5 nm, respectively. Fig. 3 shows the morphology and microstructure of the different atomic ratios of CoNi/MWCNTs examined by SEM and TEM. It can be seen that the quasi-spherical CoNi alloy nanoparticles are attached uniformly on the surface of carbon nanotubes. As a whole, the loading of the CoNi alloy nanoparticles attached on the carbon nanotubes increases with increasing the atomic ratios of metals to carbon nanotubes. The average size of the alloy nanoparticles from the TEM images were 15, 25, 37, and 48 nm, which corresponds to 3, 7, 12, and 18 at%, respectively, which is consistent with the trend of the change in the crystallite size calculated from the Debye–Scherrer formula. The size of CoNi alloy nanoparticles increases with increasing the atomic ratios of metals to carbon nanotubes (listed in Table 1 ), and the loading of CoNi alloy nanoparticles increased, even with a denser layer of CoNi nanospheres when the atomic ratio was 18 at% as shown in Fig. 3 (g) and (h). HRTEM is employed to investigate the inner structure of CoNi/MWCNT nanocomposites ( Fig. 4 (a) ), showing well-defined lattice fringes of CoNi nanoparticles. The measured spacing of the crystallographic planes is 0.204 nm and 0.342 nm from the HRTEM images, corresponding to the (1 1 1) and (0 0 2) plane separations of CoNi and MWCNTs, respectively. The SAED ( Fig. 4 (b)) can reveal details of the local CoNi structure, which can be indexed to polycrystalline CoNi. The concentric rings could be assigned as diffractions from the (1 1 1), (2 0 0), and (2 2 0) planes of fcc CoNi, and the centermost ring is assigned as diffractions from the (0 0 2) plane of MWCNTs, which is consistent with the XRD results. The EDS spectrum ( Fig. 4 (c)) shows the presence of Co, Ni, Si and C, which confirms the existence of CoNi on MWCNTs. It is obvious that the silicon peak is caused by the silicon chip used to clamp the nanoparticles. The carbon comes from the carbon nanotubes. The oxygen peak in the spectrum probably originates from the unavoidable surface-adsorption of oxygen onto the samples from exposure to air during sample processing. The atomic ratio of Co to Ni for the majority of CoNi alloy nanoparticle is 0.47:0.53 according to EDS quantitative microanalysis, which is close to the stoichiometry of CoNi. 3.2 Possible formation mechanism In our experiments, the morphology and size of the samples were found to be strongly depended on the experimental conditions such as the microwave power, the reaction time and the atomic ratios of CoNi/MWCNTs. By adjusting these experimental parameters suitably, the size of CoNi alloy nanoparticles will be controlled. It has been found that when the reaction time is less than 2 min, the MWCNTs are coated with fewer CoNi nanoparticles unevenly. When the reaction time is longer than 2 min, the severely aggregated CoNi nanoparticles on the MWCNTs are obtained. The size of CoNi alloy nanoparticles increased with increasing the microwave power. Therefore, we chose the proper condition that the microwave power was 600 W and the reaction time was 2 min, CoNi alloy nanoparticles were dispersed uniformly on the surface of MWCNTs under this condition. Except for the factors above, the atomic ratio of CoNi/MWCNTs was a crucial factor for the size of CoNi alloy nanoparticles, we found that the size of CoNi alloy nanoparticles increased with increasing the atomic ratios of CoNi/MWCNTs. Based on our experimental results, a possible formation and growing mechanism of CoNi/MWCNT nanocomposites can be proposed as follows: the positive metal ions Co 2+ and Ni 2+ can be adsorbed effectively onto the surface of the acid-treated MWCNTs via electrostatic attraction, then positive metal ions Co 2+ and Ni 2+ were reduced by hydrazine hydrate due to the microwave irradiation, metallic cobalt and nickel formed CoNi alloy nanoparticles. The reactions can be expressed as Eqs. (1) , (2) , and (3) . (1) 2Ni 2+ + N 2 H 4 + 4OH − →2Ni + N 2 ↑ + 4H 2 O (2) 2CO 2+ + N 2 H 4 + 4OH − →2Co + N 2 ↑+4H 2 O (3) Co + Ni→CoNi The microwave heating can improve the nucleation rate to form CoNi alloy nuclei around the sites, CoNi alloy nuclei formed on the shell of MWCNTs grows through the continuous surface to form CoNi alloy nanoparticles. With the increasing atomic ratios of CoNi/MWCNTs, CoNi alloy nuclei formed on the shell of MWCNTs increases, a large amount of CoNi alloy nanoparticle aggregates are formed, which leads to the quasi-spherical CoNi alloy nanoparticle over the entire external MWCNT surface, as shown in parts (b) and (c) of Fig. 5 . 3.3 Magnetic measurement Magnetic properties of the samples were investigated at room temperature using a VSM with an applied field −10 kOe ≤ H ≤ 10 kOe. Fig. 6 shows the hysteresis loops for samples with 3, 7, 12 and 18 at%. The values of the coercivity ( H c) and the saturation magnetization ( M s) of field for all samples were listed in Table 1 . It can be seen that the H c increases with increase of the particle size from 15 nm to 37 nm, and decreases with increase of the particle size from 37 nm to 48 nm. According to the theory of the magnetic domain [26] , there is a critical size d s of single domain particles. When the particle size ( D ) is smaller than d s, the magnetic particles are single domain particles. When D is larger than d s, the magnetic particles are multi-domain particles. The H c of single domain particles increases with the increase of D , while the H c of the multi-domain particles decreases with the increase of D . The critical size d s of CoNi alloy nanopaticle is about 40 nm reported in literature [27] . So when the particle size of CoNi alloy nanoparticle increased from 15 nm to 48 nm, the single domain turned to multi-domain, the coercivity increased and reached to maximum at the size of 37 nm, and then decreased. The M s of CoNi/MWCNT nanocomposites shown in Table 1 also increases with the increase of the particle size from 15 nm to 37 nm, this is mainly related to the increase of the content of CoNi alloy nanoparticle in the composites, and the surface disorder contribution is lower with the largest particles duo to their lower surface/volume ratio, then their magnetiazation is higher. While the M s decreases when the particle size increases to 48 nm, which maybe results from domain wall displacement in the multi-domain structure, magnetic anisotropy of crystals, the surface-to-volume ratio and the surface defect of the nanocrystals [28,29] . 4 Conclusions CoNi alloy nanoparticles with average diameters in the range of 15–48 nm attached on the carbon nanotubes were synthesized by microwave-assisted method. CoNi alloy nanoparticles were fcc structure, quasi-spherical and dispersed uniformly on the surface of MWCNTs. The size of the nanoparticles can be controlled through adjusting the atomic ratio of metal to carbon in the mixed acetate solution. Magnetic measurement shows that the coercivity and the saturation magnetization vary with the change of the particle size. Both the H c and the M s of the samples increased with the increase of the particle size from 15 nm to 37 nm, and decreased from 37 nm to 48 nm. These results demonstrate that the microwave-assisted method is promising for preparation of size-controlled magnetic alloy nanoparticles attached on MWCNTs for magnetic storage and the ultra high-density magnetic recording applications. Acknowledgments We thank Anhui Provincial Natural Science Foundation (No. 070414179 ) and National Natural Science Foundation (No. 20901003 ) of the People's Republic of China for financial support. References [1] S. Pane E. Gomez J. Garcia-Amoros D. Velasco E. Valles Appl. Surf. Sci. 253 2006 2964 2968 [2] S.L. Pan Z.G. An J.J. Zhang G.Z. Song Mater. Chem. Phys. 124 2010 342 346 [3] A. Foyet A. Hauser W. Schafer J. Solid State Electrochem. 12 2008 47 55 [4] Y. Rheem B.Y. Yoo W.P. Beyermann N.V. Myung Nanotechnology 18 2007 125204 125209 [5] L.F. Sun J.M. Mao Z.W. Pan B.H. Chang W.Y. Zhou G. Wang L.X. Qian S.S. Xie Appl. Phys. Lett. 74 1999 644 646 [6] M. Wen Y.F. Wang F. Zhang Q.S. Wu J. Phys. Chem. C 113 2009 5960 5966 [7] P. Toneguzzo G. Viau O. Acher F. Guillet E. Bruneton F. Fievet-Vincent F. Fievet J. Mater. Sci. 35 2000 3767 3784 [8] N. Galvez E. Valero M. Ceolin S. Trasobares M. Lopez-Haro J.J. Calvino J.M. Domınguez-Vera Inorg. Chem. 49 2010 1705 1711 [9] P. Elumalai H.N. Vasan M. Verelst P. Lecante V. Carles P. Tailhades Mater. Res. Bull. 37 2002 353 363 [10] L. Pei K. Mori M. Adachi Langmuir 20 2004 7837 7843 [11] E. Hao R.C. Bailey G.C. Schatz J.T. Hupp S. Li Nano Lett. 4 2004 327 330 [12] Y. Ramaye S. Neveu V. Cabuil J. Magn. Magn. Mater. 289 2005 28 31 [13] S. Thongmee H.L. Pang J.B. Yi J. Ding J.Y. Lin L.H. Van Acta Mater. 57 2009 2482 2487 [14] D. Ung G. Viau C. Ricolleau F. Warmont P. Gredin F. Fievet Adv. Mater. 17 2005 338 344 [15] M.J. Hu Y. Lu S. Zhang S.R. Guo B. Lin M. Zhang S.H. Yu J. Am. Chem. Soc. 130 2008 11606 11607 [16] L.P. Zhu H.M. Xiao S.Y. Fu Eur. J. Inorg. Chem. 2007 3947 3951 [17] S. Pane E. Gomez J. Garcıa-Amoros D. Velasco E. Valles J. Electroanal. Chem. 604 2007 41 47 [18] X.J. Zhang W. Jiang D. Song J.X. Liu F.S. Li Mater. Lett. 62 2008 2343 2346 [19] Z.P. Dong K. Ma J.G. He J.J. Wang R. Li J.T. Ma Mater. Lett. 62 2008 4059 4061 [20] Q.F. Liu W.C. Ren Z.G. Chen B.L. Liu B. Yu F. Li H.T. Cong H.M. Cheng Carbon 46 2008 1417 1423 [21] H.Q. Cao M.F. Zhu Y.G. Li J. Solid State Chem. 179 2006 1208 1213 [22] D. Shi J.P. Cheng F. Liu X.B. Zhang J. Alloys Compd. 502 2010 365 370 [23] H.Q. Wu Q.Y. Wang Y.Z. Yao C. Qian X.J. Zhang X.W. Wei J. Phys. Chem. C. 112 2008 16779 16783 [24] H.Q. Wu Q. Wang Y.Z. Yao C. Qian P.P. Cao X.J. Zhang X.W. Wei Mater. Chem. Phys. 113 2009 539 543 [25] G. Viau F. Fievet-Vincent F. Fievet Solid State Ionics 84 1996 259 270 [26] G.D. Tang D.L. Hou M. Zhang L.H. Liu L.X. Yang C.F. Pan X.F. Nie H.L. Luo J. Magn. Magn. Mater. 251 2002 42 49 [27] C. Luna M.P. Morales C.J. Serna M. Vazquez Nanotechnology 14 2003 268 272 [28] M.A. Gonzalez-Fernandez T.E. Torres M. Andres-Verges R. Costo P. Presa C.J. Serna M.P. Morales C. Marquina M.R. Ibarra G.F. Goya J. Solid State Chem. 182 2009 2779 2784 [29] H. Li H.Z. Wu G.X. Xiao Powder Technol. 198 2010 157 166
What problem does this paper attempt to address?
-
Size- and Structure-Controlled Synthesis and Characterization of Nickel Nanoparticles
Yuanzhi Chen,Xiaohua Luo,Houde She,Guang-Hui Yue,Dong-Liang Peng
DOI: https://doi.org/10.1166/jnn.2009.1206
2009-01-01
Journal of Nanoscience and Nanotechnology
Abstract:Nearly monodisperse face-centered cubic (fcc) and hexagonal close-packed (hcp) nickel nanoparticles have been prepared via the thermal decomposition of nickel organometallic precursors in a reaction mixture containing alkylamine, and characterized by powder X-ray diffraction, transmission electron microscopy and magnetic measurement. The employed alkylamine can serve as both solvent and reducing agent. The as-synthesized nickel nanoparticles are air-stable, and their sizes can be readily tuned by the variation of surfactant concentration and reaction temperature. The crystalline phase control was achieved by adjusting alkylamine concentration, heating rate and reaction temperature. Magnetic measurements showed that hcp Ni nanoparticles have quite different magnetic properties compared to fcc Ni nanoparticles.
-
Controlled Synthesis and Magnetic Properties of Co1−xNix/MWCNT Nanocomposites by Microwave Irradiation
Ning Zhang
DOI: https://doi.org/10.1016/j.materresbull.2011.10.016
IF: 5.6
2012-01-01
Materials Research Bulletin
Abstract:Co1−xNix alloy nanoparticles (x=0.2, 0.5, 0.6, and 0.8) with the diameter 15–28nm attached on the surface of multi-walled carbon nanotubes (MWCNTs) were prepared to form Co1−xNix/MWCNT nanocomposites by microwave irradiation. Experimental results demonstrated that Co1−xNix alloy nanoparticles with quasi-spherical and face-centered cubic structure had been attached on the MWCNTs, the composition and size of Co1−xNix alloy nanoparticles could be controlled through adjusting the atomic ratios of metal Co to Ni in the mixed acetate solution, the microwave power and microwave irradiation time, respectively. Both the coercivity and the saturation magnetization of Co1−xNix alloy nanoparticles increased with increasing Co concentration from x=0.8 to 0.5, and decreased when Co concentration was increased from x=0.5 to 0.2. These confirm that microwave synthesis is promising for fabricating alloy nanoparticles attached on MWCNTs for magnetic storage and ultra high-density magnetic recording applications.
-
Controllable Synthesis and Magnetic Properties of Fe–Co Alloy Nanoparticles Attached on Carbon Nanotubes
Hua-Qiang Wu,Pin-Shi Yuan,Hong-Yan Xu,Dong-Mei Xu,Bao-You Geng,Xian-Wen Wei
DOI: https://doi.org/10.1007/s10853-006-0935-5
IF: 4.5
2006-01-01
Journal of Materials Science
Abstract:Fe–Co alloy nanoparticles with different size were attached on the carbon nanotubes through adjusting the ratio of the metal to carbon in the mixed solution of nitrate with Fe:Co = 1:1 (molar ratio) via wet chemistry. X-ray powder diffraction (XRD), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM) and energy-dispersive X-ray spectrometry (EDX) indicated that the Fe–Co alloy nanoparticles attached on the surface of carbon nanotubes has body-centered cubic (bcc) structure, with sizes in the range of 13–25 nm and in the shape of spheroids. Magnetization measurements indicated that both the coercivities and the saturation magnetizations altered with size changes of the Fe–Co alloy nanoparticles. The saturation magnetization decreases with decreasing the Fe–Co alloy nanoparticles’ sizes. A decrease in coercivity with increasing Fe–Co size together with a local maximum coercivity at size of ca. 15 nm is visible. A linear relationship between the inverse particle diameter and the coercivity was found for larger particles. These demonstrated that the chemical method here is promising for fabricating Fe–Co alloy nanoparticles coated on carbon nanotubes for magnetic storage applications.
-
Microstructure and Local Magnetic Induction of Segmented and Alloyed Pd/Co Nanocomposites Encapsulated Inside Vertically Aligned Multiwalled Carbon Nanotubes
Yasuhiko Hayashi,T. Fujita,T. Tokunaga,K. Kaneko,M. Tanemura,T. Butler,N. Rupesinghe,J. D. Carey,S. R. P. Silva,K. B. K. Teo,G. A. J. Amaratunga
DOI: https://doi.org/10.1016/j.diamond.2008.03.012
IF: 3.806
2008-01-01
Diamond and Related Materials
Abstract:We have successfully synthesized the Co/Pd magnetic and nonmagnetic multisegment nanowires encapsulated inside multiwalled carbon nanotubes (MWCNTs) by using Co and Pd thin-layers deposited on Si substrate by microwave plasma enhanced chemical vapor deposition. Energy dispersive X-ray spectroscopy revealed that MWCNTs were encapsulated with Co and Pd nanowires, separately, at the tube top and the bottom of Co nanowire, respectively. The face-centered-cubic (fcc) structure of Co nanowires was confirmed by a selected area diffraction pattern. We proposed a fruitful description for the encapsulating mechanisms of both Co and Pd multisegment nanowires. The component of magnetic induction from Co region, not Pd region, was then estimated to be 1.2 +/- 0.1 T, based on results of off-axis electron holography, which is lower than the expected saturation magnetization of fcc bulk Co of 1.7 T. We proposed a fruitful description for the mechanisms of reduced magnetic induction from Co nanowires. (c) 2008 Elsevier B.V. All rights reserved.
-
Synthesis and Magnetic Properties of Size-Controlled FeNi Alloy Nanoparticles Attached on Multiwalled Carbon Nanotubes
Huaqiang Wu,Cheng Qian,Yunjie Cao,Peipei Cao,Wenting Li,Xiaojun Zhang,Xianwen Wei
DOI: https://doi.org/10.1016/j.jpcs.2009.12.079
IF: 4.383
2010-01-01
Journal of Physics and Chemistry of Solids
Abstract:FeNi alloy nanoparticles with controllable sizes were attached on the multiwalled carbon nanotubes by adjusting the atomic ratio of metal to carbon in the mixed solution of nitrate with Fe:Ni=1:1 (atomic ratio) via wet chemistry. Transmission electron microscopy (TEM) and high-resolution TEM indicated that quasi-spherical FeNi alloy nanoparticles with sizes in the range 12–25nm are obtained. FeNi alloy composed of major face center cubic (fcc) and minor body center cubic (bcc) structures, which is proved by the X-ray powder diffraction (XRD). Magnetization measured by vibrating sample magnetometer demonstrated that both the coercive force and saturation magnetizations decrease as the size of the FeNi alloy nanoparticles decreased. The chemical method is promising for fabricating FeNi alloy nanoparticles attached on carbon nanotubes for magnetic storage and ultra high-density magnetic recording applications.
-
Synthesis, thermal stability, magnetic properties, and microwave absorption applications of CoNi-C core-shell nanoparticles with tunable Co/Ni molar ratio
Lizhen Hou,Xing Zhen,Linlin Liu,Daitao Kuang,Yangyang Gao,Heng Luo,Lianwen Deng,Chuansheng Chen,Shiliang Wang
DOI: https://doi.org/10.1016/j.rinp.2021.103893
IF: 4.565
2021-03-01
Results in Physics
Abstract:<p>Magnetic alloy-C core-shell nanoparticles with tunable elemental components are highly expected for their controllable magnetic, catalytic, and electromagnetic properties, and high air stability. Here we present a simple one-step metal organic chemical vapor deposition for the synthesis of CoNi-C core-shell nanoparticles with tunable Co/Ni molar ratio. The as-synthesized nanoparticles have core sizes of 5 - 50 nm, shell thicknesses of ∼ 5 nm, and tunable Co/Ni molar ratio determined by the molar ratio of Co(acac)<sub>3</sub>/Ni(acac)<sub>2</sub> used in the precursor. The core-shell nanoparticles are very stable in ambient atmosphere at the temperature below 200 <sup>o</sup>C, and exhibit a slight oxidation in the temperature range of 200 to 400 <sup>o</sup>C. The core-shell nanoparticles with Co/Ni molar ratios of 1.27:1, 0.64:1, and 0.30:1 exhibit saturation magnetization values of 41, 31, and 24 emu/g, and coercivity values of 483, 346, and 362 Oe, respectively. It is demonstrated that the microwave absorption parameters of the as-synthesized nanoparticles can be tuned by the Co/Ni molar ratio, which provides a practical strategy to regulate the microwave absorption properties of nanostructured absorbers.</p>
physics, multidisciplinary,materials science
-
Synthesis, Morphology, and Magnetic Properties of NiCo/carbon Nanocomposites
Nanjing University of Technology,Zhong Wei,Au Chaktong,Lv Liya,Du Youwei
DOI: https://doi.org/10.1557/jmr.2011.374
IF: 2.7
2011-01-01
Journal of Materials Research
Abstract:Depending on the Ni:Co molar ratio, composites of NiCo/carbon nanorods and NiCo/carbon nanotubes can be synthesized through catalytic decomposition of benzene at 500 °C over NiCo nanoparticles derived from sol–gel synthesis followed by hydrogen reduction. According to x-ray diffraction results, the average grain size of NiCo31 is 11.2 nm, whereas that of NiCo13 and NiCo22 is 24.9 nm. Field-emission scanning electron microscopic and high-resolution transmission electron microscopic images reveal that over NiCo13 and NiCo22, the carbon nanomaterials are mainly in the form of nanorods, whereas over NiCo31, they are in the form of nanotubes. The composites of carbon and NiCo alloy are highly stable in air and show soft magnetic property and almost equal coercivity. It is observed that the saturation magnetization is affected by the composition of NiCo alloy.
-
Fe-Co Alloy Nanoparticles Dispersed in Polymer-Derived Carbon Support: Effect of Initial Polymer Nature on the Size, Structure and Magnetic Properties
Andrey Vasilev,Mikhail Efimov,Dmitry Muratov,Petr Chernavskii,Kirill Cherednichenko,Ella Dzidziguri,Galina Karpacheva
DOI: https://doi.org/10.3390/ma16206694
IF: 3.4
2023-10-15
Materials
Abstract:Fe-Co alloy nanoparticles with different sizes, supported by carbon derived from several polymers, namely polyacrylonitrile, polyvinyl alcohol and chitosan, have been synthesized by a one-pot method involving simultaneous metal nanoparticle formation and polymer carbonization. The method involves the joint dissolution of metal salts and a polymer, followed by annealing of the resulting dried film. Detailed XRD analysis confirmed the formation of Fe-Co alloy nanoparticles in each sample, regardless of the initial polymer used. Transmission electron microscopy images showed that the Fe-Co nanoparticles were all spherical, were homogeneously distributed within the carbon support and varied by size depending on the initial polymer nature and synthesis temperature. Fe-Co nanoparticles supported by polyacrylonitrile-derived carbon exhibited the smallest size (6–12 nm), whereas nanoparticles on chitosan-derived carbon support were characterized by the largest particle size (13–38 nm). The size dependence of magnetic properties were studied by a vibrating sample magnetometer at room temperature. For the first time, the critical particle size of Fe-Co alloy nanoparticles with equiatomic composition has been experimentally determined as 13 nm, indicating the transition of magnetic properties from ferromagnetic to superparamagnetic.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
-
Controlled Synthesis, Structure and Magnetic Properties of Fe1−xNix Alloy Nanoparticles Attached on Carbon Nanotubes
HQ Wu,YJ Cao,PS Yuan,HY Xu,XW Wei
DOI: https://doi.org/10.1016/j.cplett.2005.02.117
IF: 2.719
2005-01-01
Chemical Physics Letters
Abstract:Fe1−xNix alloy nanoparticles (x=0.25, 0.50, 0.75), with diameters in the range of 12–15nm were uniformly attached on the surface of carbon nanotubes by wet chemistry, which were characterized by transmission electron microscopy, high-resolution transmission electron microscopy and X-ray powder diffraction. When x=0.25, fcc and bcc structure coexist obviously, while when x=0.50, 0.75, most of Fe1−xNix alloy nanoparticles have fcc structure. Fe1−xNix alloy nanoparticles attached on carbon nanotubes have soft magnetic in nature, and the coercivity decreases with increasing Ni concentration and with decreasing the nanoparticles size, the saturation magnetization varies with the Ni concentration changes. These demonstrate that the chemical method here is promising for fabricating Fe–Ni alloy nanoparticles coated on carbon nanotubes for magnetic storage applications.
-
Growth and Nanoscale Magnetic Properties of Ferromagnetic Nanowire Encapsulated Inside Carbon Nanotubes
Yasuhiko Hayashi,T. Fujita,T. Toicunaga,B. Jang,M. Tanemura,G. A. J. Amaratunga
DOI: https://doi.org/10.1109/tmag.2009.2018668
IF: 1.848
2009-01-01
IEEE Transactions on Magnetics
Abstract:We synthesize ferromagnetic Co nanowire, and Co/Pd multisegment nanowires encapsulated inside multi-walled carbon nanotubes CNTs (MWCNTs) by plasma-enhanced chemical vapor deposition (PECVD). High-resolution transmission electron microscopy (HR-TEM), selected area electron diffraction (SAED) patterns and energy dispersive X-ray spectroscopy (EDS) were used to characterize the microstructures and elemental analyses of the nanowires. Quantitative magnetization measurements of Co nanowires encapsulated inside MWCNTs were experimentally established by TEM off-axis electron holography at room temperature. The MWCNTs grew up to 100-110 nm in diameter and 1.5-1.7 mu m in length. The typical bright-field TEM images revealed both Co nanowire and Co/Pd multisegment nanowires encapsulated inside vertically aligned MWCNTs on the same substrate. The composition of metal encapsulated inside MWCNTs were characterized by EDS. Experimental results revealed that the Co nanowire encapsulated inside MWCNT was always presented as the face-centered-cubic (fcc) Co structure. The component of magnetic induction was then measured to be 1.2 +/- 0.1 T based on TEM off-axis electron holography results, which is lower than the expected saturation magnetization of fcc Co bulk of 1.7 T. The partial oxidation of the ferromagnetic metal during the process and the magnetization direction may play an important role in the determination of the quality of the remanent states. The ferromagnetic metal nanowires encapsulated inside CNTs demonstrate very high potential in providing the required magnetic properties, low dimensionality, and small volume for future nanoscale devices.
-
Microwave-polyol Controlled Synthesis and Magnetic Properties of Monodisperse CoxNi1−xFe2O4/MWCNT Nanocomposites
Huaqiang Wu,Tingting Li,Lingling Xia,Xiaojun Zhang
DOI: https://doi.org/10.1016/j.materresbull.2013.08.025
IF: 5.6
2013-01-01
Materials Research Bulletin
Abstract:Ni1−xZnxFe2O4/MWCNT nanocomposites (x=0, 0.2, 0.4, 0.5, 0.6, 0.8 and 1) with controllable composition have been successfully synthesized via microwave-assisted polyol process using triethylene glycol solution (TREG) as solvent. Experimental results demonstrated that monodisperse face-centered cubical Ni1−xZnxFe2O4 nanoparticles with average size (6nm) had been attached on the MWCNTs. The composition of ferrite nanoparticles can be controlled through adjusting the atomic ratios of the nickel and zinc salts in the mixed nitrate solution. The magnetic properties of nanocomposites with different Zn contents were measured by vibrating sample magnetometer (VSM). The saturation magnetization (Ms) of Ni1−xZnxFe2O4/MWCNT nanocomposites gradually increases when the x is less than 0.5 while decreases when the x is larger than 0.5. Ms reached maximum value when the x is 0.5. The coercivity (Hc) of nanocomposites is low at room temperature, which exhibits characteristic of superparamagnetic.
-
Functionalization of carbon nanotubes with magnetic nanoparticles: general nonaqueous synthesis and magnetic properties.
Hui Zhang,Ning Du,Ping Wu,Bingdi Chen,Deren Yang
DOI: https://doi.org/10.1088/0957-4484/19/31/315604
IF: 3.5
2008-01-01
Nanotechnology
Abstract:A novel approach has been developed to synthesize magnetic nanoparticle and carbon nanotube (CNT) core-shell nanostructures, such as CoO/CNTs and Mn3O4/CNTs, by the nonaqueous solvothermal treatment of metal carbonyl on CNT templates using hexane as the solvent. The morphological and structural characterizations indicate that numerous cubic CoO or tetragonal Mn3O4 nanoparticles are deposited on the surfaces of the CNTs to form CNT-based core-shell nanostructures. It is revealed that the hydrophobic interaction between nanoparticles and CNTs in hexane plays the critical role for the formation of CNT-based core-shell nanostructures. A physical property measurement system (PPMS-9, Quantum Design) analysis indicates that the CoO/CNT core-shell nanostructures show weak ferromagnetic performance at 300 K due to the ferromagnetic Co clusters and the uncompensated surface spin states, while the Mn3O4/CNT core-shell nanostructures display ferromagnetic behavior at low temperature (34.5 K), which transforms into paramagnetic behavior with increasing temperature.
-
$\mathrm{Fe}_{1-x}\mathrm{Ni}_x$ Alloy Nanoparticles Encapsulated inside Carbon Nanotubes: Controlled Synthesis, Structure and Magnetic Properties
Rasha Ghunaim,Christine Damm,Daniel Wolf,Axel Lubk,Bernd Büchner,Michael Mertig,Silke Hampel
DOI: https://doi.org/10.48550/arXiv.1809.10500
2018-09-27
Materials Science
Abstract:In the present work, different synthesis procedures have been demonstrated to fill carbon nanotubes (CNTs) with $\mathrm{Fe}_{1-x}\mathrm{Ni}_x$ alloy nanoparticles (x = 0.33, 0.5). CNTs act as templates for the encapsulation of magnetic nanoparticles, and provide a protective shield against oxidation as well as prevent nanoparticles agglomeration. By variation of the reaction parameters, the purity of the samples, degree of filling, the composition and size of filling nanoparticles have been tailored and therefore the magnetic properties. The samples were analyzed by scanning electron microscopy (SEM), transmission electron microscopy (TEM), Bright-field (BF) TEM tomography, X-ray powder diffraction, superconducting quantum interference device (SQUID) and thermogravimetric analysis (TGA). The Fe1-xNix-filled CNTs show a huge enhancement in the coercive fields compared to the corresponding bulk materials, which make them excellent candidates for several applications such as magnetic storage devices.
-
Carbon Monoxide-Assisted Size Confinement Of Bimetallic Alloy Nanoparticles
Chunhua Cui,Lin Gan,Maximilian Neumann,Marc Heggen,Beatriz Roldan Cuenya,Peter Strasser
DOI: https://doi.org/10.1021/ja4124658
IF: 15
2014-01-01
Journal of the American Chemical Society
Abstract:Colloid-based chemical synthesis methods of bimetallic alloy nanoparticles (NPs) provide good monodispersity, yet generally show a strong variation of the resulting mean particle size with alloy composition. This severely compromises accurate correlation between composition of alloy particles and their size-dependent properties. To address this issue, a general CO adsorption-assisted capping ligand-free solvothermal synthesis method is reported which provides homogeneous bimetallic NPs with almost perfectly constant particle size over an unusually wide compositional range. Using Pt-Ni alloy NPs as an example, we show that variation of the reaction temperature between 160 and 240 degrees C allows for precise control of the resulting alloy particle bulk composition between 15 and 70 atomic % Ni, coupled with a constant mean particle size of similar to 4 nm. The size-confining and Ni content-controlling role of CO during the nucleation and growth processes are investigated and discussed. Data suggest that size-dependent CO surface chemisorption and reversible Ni-carbonyl formation are key factors for the achievement of a constant particle size and temperature-controlled Ni content. To demonstrate the usefulness of the independent control of size and composition, size-deconvoluted relations between composition and electrocatalytic properties are established. Refining earlier reports, we uncover intrinsic monotonic relations between catalytic activity and initial Ni content, as expected from theoretical considerations.
-
Diameter-Controlled Synthesis of Polycrystalline Nickel Nanowires and Their Size Dependent Magnetic Properties
Shaochun Tang,Sascha Vongehr,Hua Ren,Xiangkang Meng
DOI: https://doi.org/10.1039/c2ce25855b
IF: 3.756
2012-01-01
CrystEngComm
Abstract:Polycrystalline nickel nanowires (NWs) with a length reaching tens of micrometers were prepared in large quantities by a facile and rapid microwave-assisted polyol method. Characterization by X-ray diffraction and electron microscopy reveal that the NWs are uniform with a narrow size distribution. Their diameters (D) are controllable in a wide range via the concentration of precursor solutions. The diameters of the NWs as well as those of the contained grains increase surprisingly linearly with the concentration. The NWs have rough surfaces at low concentrations but become smoother at high ones. The growth mechanisms leading to the grain and wire diameters and the surface morphology are discussed. The coercivity (H-C) decreases with increasing diameter whereas the saturation magnetization increases to approach the bulk value, indicating a strong size dependence of the magnetic properties. Owing to the anisotropic shape and collective grain interactions, these Ni NWs exhibit enhanced H-C. At 70 nm, H-C reaches as high as 382 Oe at 5 K, which is more than two orders of magnitude higher than that of bulk Ni (0.7 Oe) and exceeds even that of NWs synthesized with strong magnetic fields. Temperature dependent magnetization shows a wide separation between the field-cooled and zero-field-cooled M(T) curves due to the strong nanowire shape anisotropy.
-
Structural study on Co-Ni bimetallic nanoparticles by X-ray spectroscopy
Hong Zhang,Tao Yao,Zhihu Sun,Yuanyuan Li,Qinghua Liu,Fengchun Hu,Zhiyun Pan,Bo He,Zhi Xie,Shiqiang Wei
DOI: https://doi.org/10.1021/jp105080t
2010-01-01
Abstract:The Co100-xNix (x = 0, 30, 50, and 70) bimetallic nanoparticles (NPs) synthesized by a solvothermal method show interesting shape changes from aggregated clusters to ordered nanorings with increasing Ni concentration. A comprehensive structural study of these Co100-xNix NPs is performed with X-ray diffraction and X-ray absorption fine structure spectroscopy. It is shown that the pure Co NPs consist of a majority of the fcc structure and a minority of the hcp phase. When 30% Ni is added, alloyed Co-Ni NPs with an inhomogenous atomic distribution are formed. The further addition of Ni to >= 50% could considerably improve the crystallinity and homogeneity of the alloyed NPs, as suggested by the fact that the disorder degree (sigma(2)) is gradually lowered and the coordination number ratios NCo-Co/NCo-Ni and NNi-Ni/NNi-Co gradually approach the stoichiometry of the NPs. The ordered and homogeneous fee structure helps to strengthen the magnetocrystalline anisotropic interactions, which may facilitate the head-to-tail assembly of the Co-Ni NPs.
-
Microwave Synthesis and Magnetic Properties of Co(1-x)Nix/MWCNTs Nanocomposites
CAO Pei-pei,WU Hua-qiang,LI Wen-ting,QIAN Cheng
2011-01-01
Abstract:Co1-xNix/MWCNTs(x=0.2,0.5,0.6,0.8) nanocomposites with controllable composition were fabricated using microwave synthesis method.The samples were characterized by XRD,TEM,SAED,EDX spectroscopy and VSM.The results show that Co1-xNix alloy nanoparticles attached on MWCNTs are dispersed uniformly.When x=0.2,0.5,0.6 and 0.8,Co1-xNix alloy are all fcc structure.The magnetic properties of Co1-xNix/MWCNTs nanocomposites vary with alloy composition.Both Hc and Ms increase firstly and then decrease with increasing Co content.When x=0.5,both Hc and Ms of Co1-xNix /MWCNTs nanocomposites reach to the maximum.
-
Investigating phase and magnetic properties in Co-2 wt.% MWCNT nano-composites prepared by mechanical alloying
Pinjal Pandit,Swasata Ghosh,Goutam Roy,Arpita Chatterjee,Susmita Singh,Sumit Chabri
DOI: https://doi.org/10.1177/09544089241279156
2024-09-11
Proceedings of the Institution of Mechanical Engineers Part E Journal of Process Mechanical Engineering
Abstract:Proceedings of the Institution of Mechanical Engineers, Part E: Journal of Process Mechanical Engineering, Ahead of Print. MWCNT nano-composites with a cobalt content of 2 weight percent were created by mechanically alloying during different times. Modern techniques, including x-ray diffraction (XRD), differential thermal analysis (DTA), field emission scanning electron microscopy (FESEM), high-resolution transmission electron microscopy (HRTEM) and superconducting quantum interference device (SQUID), were used to examine the effects of CNT addition on the Co morphology and magnetic characteristics of the samples. It was shown that the characteristics of Co in 2 weight percent MWCNT nano-composites were retained in a sample that was milled for 60 min. Agglomerates of nanoparticles were the end result, with CNTs evenly distributed throughout the cobalt matrix 60 min after mechanical alloying. Analysis of magnetic hysteresis loops revealed that the inclusion of CNTs altered the magnetic characteristics of nano-composite samples. Analysis of magnetic hysteresis loops revealed that the inclusion of CNTs altered the magnetic characteristics of nano-composite samples. The well-developed interfacial structure in this work significantly improved the cobalt-MWCNT nano-composites' magnetic characteristics.
engineering, mechanical
-
Hierarchical CoNi alloys toward microwave absorption application: Chain-like versus particle-like
Mingtao Qiao,Jiaxin Li,Shunan Li,Dan Wei,Xingfeng Lei,Wanying Lei,Jian Wei,Qiuyu Zhang,Mingliang Ma
DOI: https://doi.org/10.1016/j.jallcom.2022.166854
IF: 6.2
2022-12-10
Journal of Alloys and Compounds
Abstract:CoNi alloys are well known as excellent magnetic microwave absorption materials, but their various structures greatly influence electromagnetic properties, especially chains versus particles. Hierarchical CoNi chains were prepared using the solvothermal method in conjunction with an external magnetic field, and hierarchical CoNi particles were obtained in the absence of the magnetic field. Changing the reaction time from 6 to 12 h can change the surface structures of hierarchical CoNi alloys, as seen in the SEM images. The lattice parameters of samples are determined by XRD results, which include crystalline structures, lattice constants, mean crystallite sizes, and internal strain. The investigation of magnetic properties indicates that CoNi chains possess a stronger saturation magnetization and higher coercivity than CoNi particles as a result of their higher aspect ratios and larger crystalline sizes. Furthermore, CoNi chains have a higher microwave absorption capacity than CoNi particles, with a minimum reflection loss value of −42.113 dB (16.5 GHz) and an effective absorption bandwidth of 3.5 GHz (13–16.5 GHz). Conductive loss, defect-induced polarization relaxation, eddy current effect, exchange resonance, N é el relaxations, multiple reflections, and scatterings all contribute to the excellent microwave absorption performance of the CoNi chains. This research establishes that a chain-like structure outperforms a particle-like structure for hierarchical CoNi alloys as microwave absorbers, and it will provide clear guidance for designing high-performance magnetic microwave absorption materials.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
-
Size-Dependent Structural and Magnetic Properties of Disordered Co2FeAl Heusler Alloy Nanoparticles
Aquil Ahmad,Srimanta Mitra,S. K. Srivastava,A. K. Das
DOI: https://doi.org/10.48550/arXiv.1909.13088
2019-09-28
Strongly Correlated Electrons
Abstract:Co2FeAl (CFA) nanoparticles (NPs) of different sizes were synthesized by chemical route. The effect of the size of NPs upon the structure and magnetization compared to its bulk counterpart was investigated. The structure and composition were determined from X-ray diffraction (XRD) and electron microscopy. XRD analysis shows that the samples are having single (A2-type) disordered phase. Magnetization measurements suggest that the samples are soft ferromagnetic in nature with very low coercivity. Enhanced magnetic properties like saturation magnetization, coercive force, retentivity, and Curie-temperature are observed with a decrease in particle size. The effect of particle size on hysteresis losses is also discussed. The smallest particles of size 16 nm exhibited the highest saturation magnetization and transition temperature of 180.73 emu/g and 1261 K, respectively. The origin of enhancement in the magnetization of Co2FeAl nano-alloy is attributed to the strong Co-Co exchange interaction due to disorder present in the systems.