Abstract:To ascertain the crack growth behavior and coalescence mechanism in thermal barrier coatings (TBCs) is beneficial for understanding the failure of TBCs and proposing the probable optimization methods. In this work, a novel lamellar structure model with real interface morphology is developed to explore the crack growth behavior and the failure mechanism of TBCs during thermal cycling. Three typical defects which include pore, inter-splat crack, and intra-splat are incorporated in the model. To simulate the oxidation process of the bond coat (BC) realistically, The oxidation growth process is simulated via changing the BC properties to thermally grown oxide (TGO) properties layer by layer. The effects of the lateral growth strain distribution through TGO thickness on the stress states are executed. Moreover, the influences of BC creep on the crack growth and coating lifetime are further elaborated. The results show that the larger the lateral growth strain gradient, the smaller the residual tensile stress. The irregular interface morphology results in the redistribution of residual stresses. Although the pores and cracks can alleviate the tensile stress near the valley, large stress concentration will occur near them. At the early phase of thermal cycling, the cracks grow steadily. After more cycles, the cracks propagate rapidly and merge with others. The simulated delamination path is in agreement with the experiment results. Not only does BC creep change the crack coalescence mechanism, it also decreases the thermal cyclic lifetime of TBCs. The coating optimization method proposed in this study provides another option for developing advanced TBCs with longer lifetime.

Finite element analysis of anti-spallation thermal barrier coatings

Simulation of Residual Stresses and Their Effects on Thermal Barrier Coating Systems Using Finite Element Method

Influence of “Island-Like” Oxides in the Bond-Coat on the Stress and Failure Patterns of the Thermal-Barrier Coatings Fabricated by Atmospheric Plasma Spraying During Long-Term High Temperature Oxidation

Thermal Fatigue of Atmospheric Plasma Sprayed Thermal Barrier Coatings

Assessment of Stress Characteristic and Interfacial Delamination in Thermal Barrier Coatings Considering the Connected Crack Network

Interfacial peeling loads in the TBC with an air hole: Analytical solutions and viscoplasticity modelling

Nondestructive Measurements of Residual Stress in Air Plasma‐sprayed Thermal Barrier Coatings

Dynamic-stiffening-induced Aggravated Cracking Behavior Driven by Metal-Substrate-constraint in a Coating/substrate System

Analysis on Thermal Stress of Optimized Functionally Graded Coatings During Thermal Shock Based on Finite Element Simulation

Numerical and Experimental Investigation of Residual Stress in Thermal Barrier Coatings During Aps Process

Stress Distribution in the Vicinity of Thermally Grown Oxide of Thermal Barrier Coatings

Stress States and Crack Behavior in Plasma Sprayed TBCs Based on a Novel Lamellar Structure Model with Real Interface Morphology

Research Progress of Failure Mechanism of Thermal Barrier Coatings at High Temperature via Finite Element Method

SEM-Guided Finite Element Simulation of Thermal Stresses in Multilayered Suspension Plasma-Sprayed TBCs

Evaluation of Localized Spallation of TBCs via a Combination of Conjugate Heat Transfer Numerical and Experimental Analysis

Strategies for improving the lifetime of air plasma sprayed thermal barrier coatings

Failure Behavior Study of EB-PVD TBCs under Salt Spray Corrosion and Thermal Shock Cycles

An Innovative Model Coupling TGO Growth and Crack Propagation for the Failure Assessment of Lamellar Structured Thermal Barrier Coatings

Stress Development in Thermal Barrier Coatings with Morphology-Controlled Thermally Grown Oxide

Finite Element Simulations of Thermal Stress Distribution in Thermal Barrier Coatings with Different Mullite Whisker Arrangements

Progress Update on Extending the Durability of Air Plasma Sprayed Thermal Barrier Coatings