Abstract:TiAl alloy has broad application prospects in the aerospace field. In practical working environments, connecting with other materials is considered an important means of fully utilizing their excellent properties. This study employed a laser in-situ pre-scanning method to preheat the weld seam, achieving the connection between TiAl alloy and Ti-6Al-4V. On this basis, the microstructural evolution of the fusion zone (FZ), fusion line (FL), and heat-affected zone (HAZ) of the welded joint was analyzed in detail. By comparing with traditional welding processes, the effects of laser in-situ preheating on the microstructure and properties of the welded joints were studied. The results showed that the FZ area consists of alpha 2 and martensitic alpha-Ti, while the FL on the TiAl side features a transition layer of beta/B2 phases, providing plasticity and toughness to the welded joint. The in-situ scanning method reduced the cracks generated during welding, resulting in a more uniform distribution of the transition layer. The obtained FZ exhibited higher microhardness. The room temperature tensile strength of the welded joint reached 650 MPa. As the temperature increased, at 400 degrees C, the tensile strength and elongation reached 571 MPa and 3 %, respectively, significantly higher than the 450 MPa and 1.5 % achieved by conventional welding at the same temperature. When the temperature further increased to 500 degrees C and 600 degrees C, Ti6Al-4V experienced significant softening, becoming the weak point of the welded joint.

Application of low-power density laser welding on Ti-6Al-4V Alloy

Microstructure, Variant Selection, and Mechanical Properties of Laser-Welded Ti-4Al-2V Joints

Laser Welding of Dissimilar TiAl/Ti6-Al-4V Materials: Effects of Rapid In-Situ Laser Pre-Heating on Microstructure and Mechanical Properties of the Welding Joint

Microstructure and Mechanical Properties of Laser Welded Lap Joints of Ti-6Al-4V Alloy

Laser welding techniques for titanium alloy sheet

Microstructure and Mechanical Properties of Laser Narrow-Gap Multi-Pass Weld 20 Mm-Thick Ti-6Al-4V Alloy with Different Filling Layers

Research on the Low Power Laser Induced Arc Hybrid Welding of Titanium Alloy Thinsheet

Superplastic Tensile Behavior and Microstructure Evolution of Laser Welded Ti-6Al-4V Alloy

Lap Joining of Ti6Al4V Titanium Alloy by Vortex Flow-Based Friction Stir Welding

Mechanical Properties and Microstructure of a High-Power Laser-Welded Ti6Al4V Titanium Alloy

A Comparative Study of Pulsed Nd:YAG Laser Welding and TIG Welding of Thin Ti6Al4V Titanium Alloy Plate

Research on CO2 laser beam welding of Ti-6Al-4V

Study on Welding Characteristics of Combining Laser Welding and Resistance Seam Welding Joined Ti-6Al-4V Lap Joints

Microstructure and Properties of 6063/ti3al2.5v Dissimilar Alloys Joint with Laser Welding

Interlaminar Microstructure and Mechanical Properties of Narrow Gap Laser Welding of 40-Mm-thick Ti-6Al-4V Alloy

Multi-Component Evaporation and Uneven Aluminum Distribution during High-Power Vacuum Laser Welding of Ti-6Al-4V Titanium Alloy

Microstructural Characteristics and Mechanical Properties in Laser Beam Welds of Ti6al4v Alloy

Characteristics of Laser-TIG Double-Side Welding for Aluminum Alloys

Microstructure and Tensile Properties of Ti/Al Dissimilar Joint by Laser Welding-Brazing at Subatmospheric Pressure

Microstructure Characterization and Mechanical Properties of Linear Friction Welded Ti‐6Al‐4V Alloy

A Laser-Induced TIG Arc Narrow-Gap Welding Technique for TC4 Titanium Alloy Thick Plates Based on the Spatial Position Control of Laser, Arc and Filler Wire