Abstract:One of the methods of making traditional polymers more environmentally friendly is to modify them with natural materials or their biodegradable, synthetic equivalents. It was assumed that blends with polylactide (PLA), polysaccharides: chitosan (Ch) and starch (St) of branched polyurethane (PUR) based on synthetic poly([R,S]-3-hydroxybutyrate) (R,S-PHB) would degrade faster in the processes of hydrolysis and oxidation than pure PUR. For the sake of simplicity in the publication, all three modifiers: commercial PLA, Ch created by chemical modification of chitin and St are called bioadditives. The samples were incubated in a hydrolytic and oxidizing environment for 36 weeks and 11 weeks, respectively. The degradation process was assessed by observation of the chemical structure as well as the change in the mass of the samples, their molecular weight, surface morphology and thermal properties. It was found that the PUR samples with the highest amount of R,S-PHB and the lowest amount of polycaprolactone triol (PCLtriol) were degraded the most. Moreover, blending with St had the greatest impact on the susceptibility to degradation of PUR. However, the rate of weight loss of the samples was low, and after 36 weeks of incubation in the hydrolytic solution, it did not exceed 7% by weight. The weight loss of Ch and PLA blends was even smaller. However, a significant reduction in molecular weight, changes in morphology and changes in thermal properties indicated that the degradation of the samples should occur quickly after this time. Therefore, when using these polyurethanes and their blends, it should be taken into account that they should decompose slowly in their initial life. In summary, this process can be modified by changing the amount of R,S-PHB, the degree of cross-linking, and the type and amount of second blend component added (bioadditives).

The Study of Starch polypropylene Foams

Degradation of Polystyrene by Liquid Phase Catalysis Oxidation

Effects of polyvinyl alcohol content and hydrolysis degree on the structure and properties of extruded starch-based foams

Optimization of Reaction Conditions for Polyurethane Foam Synthesis with Liquefied Corn Stalk by Response Surface Methodology

Strategy for the Preparation of PBAT/Starch Blended Foam with High Resilience and Shrinkage Resistance

Pore structure and cushioning properties of waste paper pulp-reinforced starch-based foams

Mechanical Properties of Polyurethane Foams Prepared from Liquefied Corn Stover with PAPI.

Degradability of Polyurethanes and Their Blends with Polylactide, Chitosan and Starch

Susceptibility to Degradation in Soil of Branched Polyesterurethane Blends with Polylactide and Starch

Development of biodegradable wood fiber foam packaging material

Preparation and properties of novel poly(propylene oxide)-block- polylactide-based polyurethane foams

Humidity Resistant Biodegradable Starch Foams Reinforced with Polyvinyl Butyral (PVB) and Chitosan

Fungal degradation of reprocessed PP/PBAT/thermoplastic starch blends

Reinforcing a Thermoplastic Starch/Poly(butylene adipate-co-terephthalate) Composite Foam with Polyethylene Glycol under Supercritical Carbon Dioxide

Study of Cellulose and Starch-Based Biodegradable Foam Production Technology as Enviromentally Packaging Materials

Study on the Structure and Properties of Thermoplastic Starch Modified with Polyurethane

Comprehensive understanding of the aging and biodegradation of polystyrene-based plastics

Chemical and Physical Mechanism and Method of Preparation of Thermoplastic Starch

Effects of silylated starch structure on hydrophobization and mechanical properties of thermoplastic starch foams made from potato starch

Enhancing properties of biodegradable starch-based foams: Influence of polymer coating dissolution solvents in dip coating process

Study on morphological, mechanical, thermal, barrier, rheological, and biodegradation properties of poly(butylene adipate‐co‐terephthalate)/thermoplastic starch/poly(propylene carbonate)‐g‐polyurethane biodegradable films