Abstract:Ultrasonic velocity and attenuation measurements of a commercially available Ni-rich polycrystalline Ni–Ti alloy were simultaneously obtained upon cooling from room temperature (RT) down to 130 K. The anelastic spectra show multiple anomalies in both velocity and attenuation curves, which evidence a complex nature of structural rearrangements exhibited by Ni–Ti alloy, associated with relaxations and phase transformations. In particular, some evident anomalies at 285 and 180 K, not previously exploited using ultrasonic measurements on Ni-rich polycrystalline Ni–Ti alloy, were associated with austenite to pre-martensitic (B2 → R) and pre-martensitic to martensitic (R → B19’) phase transitions, respectively. The peculiar temperature separation between these transformations was interpreted based on chemical composition and the Ni–Ti alloy microstructure evolution. X-ray diffraction (XRD), scanning electron microscopy (SEM) and differential scanning calorimetry (DSC) were also used to add complementary results about phase transformations and thermal events exhibited by Ni–Ti alloy at low temperatures. XRD, Rietveld refinement, SEM and transmission electron microscopy (TEM) analyses confirm the coexistence of the austenite B2, martensite B19’, and Ni4Ti3 phases at RT. DSC measurements indicated reversible two-stage martensitic transitions involving B2 ↔ R ↔ B19’ phase transformations at similar temperatures than the observed from ultrasonic anomalies. Besides that, several anelastic relaxation events identified around the phase transitions reveal the occurrence of complex physical mechanisms, such as accommodation of the twinned R-phase and martensite domain walls, twinning boundaries mobility, and the coupling between stress-induced dislocation motion and interstitial diffusion, not reported simultaneously in the literature. The ferroelastic nature of martensite and pre-martensite phase transformations was confirmed for a commercially available Ni-rich polycrystalline Ni–Ti alloy studied in this work.

Comparison of the Two Relaxation Peaks in the Ti50ni48fe2 Alloy

In-situ Investigation Via High Energy X-ray Diffraction of Stress-Induced(0002)α→(110)β Transformation in a Ti-5.5Mo-7.2Al-4.5Zr-2.6Sn-2.1Cr Alloy

Analysis of Mechanical-Thermal Coupled Experiments of Single Crystal TiNi Alloys

Internal-Friction Analysis Of Ni-Ti Alloy Subjected To Temperature-Variation And Under Isothermal Conditions

A STUDY OF INTERNAL FRICTION ASSOCIATED WITH THE MARTENSITE TRANSFORMATION AT LOW FREQUENCY

Modulus Softening During the Γ→ɛ Martensitic Transformation in Fe–25Mn–6Si–5Cr–0.14N Alloys

High damping performances over wide temperature range in the B doped Ti-Ni shape memory alloys

High temperature internal friction in a Ti-46Al-1Mo-0.2Si intermetallic, comparison with creep behaviour

In-situ synchrotron high energy X-ray diffraction study of spontaneous reorientation of R phase upon cooling in nanocrystalline Ti50Ni45.5Fe4.5 alloy

Stress-assisted Atomic Diffusion in NiTiHf Shape Memory Alloys

Comparative study of physical properties of shape memory alloys after solution treating and aging at

THE BEHAVIOR OF INTERNAL FRICTION ASSOCIATED WITH THE PROCESS OF MARTENSITE-TYPE TRANSFORMATION

Effects of cooling rate on martensitic transformation behavior and shape memory property for Ni-rich NiTiHf-Nb high-temperature shape memory alloy

Mechanism of Mechanical Relaxation Associated with Precipitates

Effects of texture on the damping characteristics of cold-rolled and annealed Ti 50 Ni 40 Cu 10 shape memory alloy

RELAXATION PROCESS ASSOCIATED WITH INTERFACES IN SUPERHARD NANOCOMPOSITE FILMS

Strong influence of magnetic field and non-uniform stress on elastic modulus and transition temperatures of twinned Ni–Fe(Co)–Ga alloy

Prominent β-relaxation and stress relaxation decoupling phenomenon in Gd-Ni-Al metallic glasses

Transformation Behaviour with Thermal Cycling in Ti50Ni43Cu7 Shape Memory Alloy

Experimental assessment of low-temperature martensite transformations in Ni-rich polycrystalline Ni-Ti alloys

HREM Study on the Intervariant Structure of Ti-Ni-Hf B19′ Martensite