Magnetic And Magnetooptical Properties Of Cu-Doped Bi, Al - Dyig Films Prepared By The Pyrolysis Method

Y Zhou,Df Shen,Fx Gan

DOI: https://doi.org/10.1016/0040-6090(93)90039-R

IF: 2.1

1993-01-01

Thin Solid Films

Abstract:Bi, Al: DyIG and Cu-doped Bi, Al: DyIG films on glass substrates have been prepared by the pyrolysis method. Magnetic and magneto-optical properties were investigated. Films were annealed at 650-degrees-C for 30 min, then quenched to room temperature within about 60 s. For Cu-doped Bi, Al: DyIG films, the coercive force (H(c)) was increased with the Cu content increasing. The H(c) value of 557.2 kA m-1 was obtained in Cu-doped Bi, Al: DyIG films, and the Faraday rotation angle was about 7-degrees mum - 1 at a wavelength of 500 nm. The increased H(c) was attributed to Cu entering lattice sites.