Abstract:By using chemical reduction-deposition method,a metallic nickel-decorated multi-walled carbon nanotube material,symbolized as x%Ni/CNTs,was prepared.TEM and XRD measurements demonstrated that the metallic nickel was evenly coated onto the carbon nanotube substrate,with granule-diameter of the Ni_x~0-crystallites at ～12 nm.The H_2-TPD and CO-TPD measurements showed that the modification of metallic nickel to the CNTs resulted not only in a significant increase in the total amounts of its adsorbing hydrogen and CO,but also in pronounced enhance of the proportion of the dissociatively adsorbed hydrogen H(a) and strongly chemisorbed CO(a) in their respective total amount of adsorption.With this composite nano-carbon material as an additive,a co-precipitated Cu_6Zn_3Al_1-12.5%(8%Ni/CNT) catalyst was prepared.The assay of its catalytic activity for methanol synthesis from syngas showed that under the reaction conditions of 2.0 MPa,V(H_2)/V(CO)/V(CO_2)/V(N_2)=62/30/5/3,GHSV=2 700 mL(STP)·h~(-1)·(g-catal.)~(-1),the observed CO conversion and methanol STY reached 34% and 442 mg·h~(-1)·(g-catal.)~(-1),which was about 38% and 17% higher than those over the Cu_6Zn_3Al_1 and Cu_6Zn_3Al_1-12.5%CNT catalysts, respectively,at the respective optimal operation temperature,513 K and 503 K.The results of the present work indicated that the nickel-modified CNTs could serve as a promoter more excellent than the simple CNTs.Its unique feature of promoting adsorption/spillover of hydrogen and CO would be beneficial to generating microenvironments with higher stationary-state concentration of active hydrogen-adspecies and chemisorbed CO(a) on surface of the functioning catalyst,and thus be favorable to increasing the rate of the CO hydrogenation reactions.

Preparation and magnetic property of the composite of nitrogen-doped carbon nanotubes decorated with nickel nanoparticles

Decorating carbon nanotubes with Cobalt nanoparticles

SYNTHESIS AND THE PERFORMANCE OF CARBON NANOTUBES-(Ni-P) COMPOSITES

Decoration of Multiwalled Carbon Nanotubes with CoO and NiO Nanoparticles and Studies of Their Magnetism Properties.

Synthesis, Morphology, and Magnetic Properties of NiCo/carbon Nanocomposites

Preparation and Electromagnetic Properties of Ni-Coated Multi-Wall Carbon Nanotubes

Influence on (Ni-P) Electroless Composite Plating with Carbon Nanotubes

Decorating Mg/Fe Oxide Nanotubes with Nitrogen-Doped Carbon Nanotubes

Synthesis, Morphology and Magnetic Properties of Graphite-Encapsulated Nickel Nanoparticles

Preparation and Magnetic Properties of Nano-nickel Coated Silicon Nitride Composite Powders

A study of the electrical properties of carbon nanotube-NiFe 2O4 composites: Effect of the surface treatment of the carbon nanotubes

Carbon Nanotubes with Nickel-Cobalt Alloy Coating

Preparation and Characterization of a Material of Carbon Nanotubes Decorated by Nickel

Synthesis and Properties of Magnetic Composites of Carbon Nanotubes/Fe Nanoparticle

Preparation and Magnetic Property of Multiwalled Carbon Nanotubes Decorated by Fe3O4 Nanoparticles

Study on Chemical Nickel-plating for CNTs and Its Electro-magnetic Behavior

Preparation and magnetic properties of iron oxide and carbide nanoparticles in carbon nanotube matrix

Preparation and magnetic property of Ni nanoparticles filled carbon nanotubes

Magnetic Nanoparticles Decorated Multi-Walled Carbon Nanotubes by Bio-Inspired Poly(dopamine) Surface Functionalization

Facile Preparation of Magnetic Composites Based on Carbon Nanotubes: Utilization for Removal of Environmental Pollutants.

Carbon Nanotubes Decorated with Noble Metal Nanoparticles