Abstract:Summary form only given. Polycrystalline samples La2/3Caι/3(Mnι_xCox)θ3 with x=0.1, 0.2, 0.3, 0.4, and 0.5 were synthesized by standard solid-state reaction. X-ray diffraction results show that they are of single phase for the specimens with x<;0.3. Rietveld refinement of X-ray diffraction data shows Mn-O-Mn angle decreases from 178.8° for x=0.1 to 128.8° for x=0.3. A metal-to-insulator transition was only observed in sample with x=0.1. The different transport properties of these samples were attributed to the different Jahn-Teller distortion. The temperature dependence of reisitivity at low and high temperature can be described by the small polaron model and Kondo-like effect. In the present work, effect of Co doping at B-site of La2/3Caι/3Mnθ3 (LCMO) is discussed. The spin configuration of Co is very complex. The Co ions are in their low-spin (LS) tg6e2g0 (S=0) state at the low temperature (T<;35 K) and high-spin (HS) tg4e2g2 (S=2) state at high temperature (300 K<;T<;600 K). There maybe a intermediate-spin (IS) tg5e2gl (S=l) state or a mixture of HS and LS of Co3+ in the interval 35 K<;T<;100 K. The structure and properties are close dependent on the Co dopant as discussed below. Polycrystalline samples La,/3Ca2/3(Mnι_xCox)θ3 (LCMCO) with x=0.1, 0.2, 0.3, 0.4, and 0.5 were synthesized by standard solid-state reaction. The analytical purity materials La203, CaC03, Mn02 and Co203 were well mixed in stoichiometric proportions and pestle for 30 minutes before calcined at 1000 °C for 6 hours. The calcined powder was pressed into slices and then sintered at 1400°C for 32 hours in air. All the specimens were slowly-cooled to room temperature in air for about 15 hours. The structure of the samples was characterized by X-ray diffraction (XRD), which was performed at a Rigaku Dmax-γB diffractometer at room temperature with step scanning model. The struct- ral parameters were obtained from a standard Rietveld program GSAS. The resistivity with/without magnetic field were measured by the standard four-probe method at a Quantum Design PPMS. Measurements of x-ray diffraction at room temperature show that samples within x<;0.3 are of single phase which can be well refined in orthorhombic symmetry with the space group of Prima (Rwp<;15%). The lattice parameters of a, b, and c are almost independent of the Co dopant which indicates the unit cell is unchanged after Co was doped in LCMO. The bond angle of Mn-Ol-Mn decreases largely from 178.8° for x=0.1 to 128.8° for x=0.3. It will induce the large change of electric transport properties as discussed below.

Transport Characteristic in Current-in-plane (CIP) Geometry of La0.8Sr0.2MnO3/Co Heterostructure

Transport Properties in the La0.8Sr0.2MnO3/Co Heterostructure

Magnetically and Electrically Tunable Transport Property of the Heterojunction Composed of La0.9Ca0.1MnO3+δand Nb-doped SrTiO3

Crossover Effect of Inter-Granular Transport and Quantum Correction in Co-doping La2/3Ca1/3MnO3 Manganites

Intrinsic inhomogeneity and non-linear conduction in charge-ordered Bi0.5Ca0.4Sr0.1MnO3

Magnetic and transport properties of the Co-doped manganite La0.7Sr0.3Mn1-xCoxO3 (0 ≤x ≤ 0.5)

Structure and Transport Properties of La(1-X)Sr(X)Coo(3) (0 <= X <= 0.5) System

Voltage-modulated Negative and Positive Magnetoresistance in La0.7Sr0.3MnO3/Si Heterostructure

Transport property at low and high temperatures in La-(Ca-Ba-Sr)-Mn-O manganite perovskite

The Significant and Temperature-Insensitive Magnetoresistance Observed in Co-doped (la0.7sr0.3)mno3 Thin Films

Effect of Co doping at the B-site on the structure and tranport properties in La2/3Ca1/3MnO3

Transport properties and laser-induced effect of the La0.5Sr0.5MnO3 film

Ionic Liquid Gating and Phase Transition Induced Semiconducting to Metallic Transition in La 0.67 Sr 0.33 MnO 3 /BaTiO 3 Heterostructures

Resistivity Variation In Heteroepitaxial La0.7ca0.3mno3/Gd0.67sr0.33mno3 Multilayers With Different Thicknesses Of The La0.7ca0.3mno3 Layers

Current-Voltage Characteristics Of La2-Xsrxcuo4/Nb-Doped Srtio3 Heterojunctions

Transport and Stability Properties of the Charge Ordered State for Sm1−xCaxMnO3 (0.4⩽X⩽0.8)

Transport and magnetic properties in perovskite compound La0.7Sr0.3Mn1-xCoxOy

Transport Properties and Laser-Indued Effect of the La0.5Sr0.5MnO3 Film

Electrical transport properties of heteroepitaxial p–n junction of charge-ordered La7/16Ca9/16MnO3 and 0.5 wt% Nb doped SrTiO3

Transport and magnetic properties of La1.48Nd0.4Sr0.12CuO4/La0.67Sr0.33MnO3 bilayer

Magnetic and Transport Properties of Cobalt Doped La0.7Sr0.3MnO3