Preparation and Analysis of Porous PAN/CS/BCP/PLGA Composite Scaffolds

ZHU Jianhua,MA Shanshan,WANG Jingyan,LI Muqin,LIU Jiguang,YANG Hongbo,YANG Qingling

DOI: https://doi.org/10.13505/j.1007-1482.2011.03.018

2011-01-01

Abstract:Objective To investigate the feasibilty of porous clear polypropylene-based carbon fiber/chitosan/biphasic calcium phosphate/poly lactic acid-glycolic acid(PAN/CS/BCP/PLGA) composite scaffold material for bone tissue engineering.Methods The biphasic calcium phosphate was prepared by wet synthesis method,and the porous PAN/CS /BCP/PLGA composite scaffold was prepared by vacuum freeze-drying technology.The compressive strength and porosity were measured by Archimedes method,and the biological activity was also determined.The phase structure and morphology were analyzed using X-ray difraction(XRD) and scaning electron microscopy(SEM).Results After adding 4wt% PAN to PAN/CS/BCP/PLGA composite scaffold,the average rate was more than 85% porosity,the compressive strength was increased 6-fold greater than 5.9 MPa,and the biodegradable rate was lower than 9.5%.It presented a porous penetration appearance,and the average pore diameter was 400～500 μm.PAN was well distributed.In vitro simulation experiment showed that the surface of scaffolds produced bone-like apatite.Conclusions The porous PAN/CS/BCP/PLGA composite scaffold has good biological activity and biodegradability,as the scaffold material of bone tissue engineering provides theoretical basis.