Preparation, morphology and properties of acid and amine modified multiwalled carbon nanotube/polyimide composite

Siu-Ming Yuen,Chen-Chi M. Ma,Yao-Yu Lin,Hsu-Chiang Kuan

DOI: https://doi.org/10.1016/j.compscitech.2006.12.006

IF: 9.1

2007-01-01

Composites Science and Technology

Abstract:The precursor of polyimide, polyamic acid, was prepared by reacting 4,4′-oxydianiline (ODA) with 3,3′,4,4′-benzophenone tetracarboxylic dianhydride (BTDA). Unmodified, acid-modified and amine-modified multiwall carbon nanotubes (MWCNT) were separately added to the polyamic acid and heated to 300°C to produce polyimide/carbon nanotube composite. Scanning electron microscopic (SEM) and transmission electron microscopic (TEM) microphotographs reveal that acid-modified MWCNT and amine-modified MWCNT were dispersed uniformly in the polyimide matrix. The effect of the acid and amine-modified MWCNTs on the surface and volume electrical resistivities of MWCNT/polyimide composites were investigated . The surface electrical resistivity of the nanocomposites decreased from 1.28×1015Ω/cm2 (neat polyimide) to 7.59×106Ω/cm2 (6.98wt% unmodified MWCNT content). Adding MWCNTs influenced the glass transition temperatures of the nanocomposites. Modified MWCNTs significance enhanced the mechanical properties of the nanocomposites. The tensile strength of the MWCNT/polyimide composite was increased from 102MPa (neat polyimide) 134MPa (6.98wt% acid modified MWCNT/polyimide composites).