Remarkably Improved Electrode Performance of Bulk MnS by Forming a Solid Solution with FeS – Understanding the Li Storage Mechanism
Liang Zhao,Xiqian Yu,Juezhi Yu,Yongning Zhou,Steven N. Ehrlich,Yong-Sheng Hu,Dong Su,Hong Li,Xiao-Qing Yang,Liquan Chen
DOI: https://doi.org/10.1002/adfm.201400934
IF: 19
2014-01-01
Advanced Functional Materials
Abstract:Transition metal compounds based on conversion reactions are promising electrode materials for lithium‐ion batteries due to their higher lithium storage capacity compared with currently available commercial battery electrodes. Most of the studies on these materials in the literature focus on transition metal oxides and fluorides, and not much work on transition metal sulphides has been reported, partially due to their relatively poor electrochemical performance. Here, synthesis and characterization of a series of solid solution Fe x Mn 1‐ x S ( x = 0.2, 0.5, 0.8) monosulphide compounds is reported. Interestingly, hexagonal FeS and cubic MnS can form a solid solution of Fe x Mn 1‐ x S ( x < 0.57). It is demonstrated that the lithium storage voltage can be tuned by changing the Fe concentration in the Fe x Mn 1‐ x S matrix; meanwhile, the discharge‐charge coulombic efficiency and cycle stability of Fe x Mn 1‐ x S are greatly enhanced in comparison with that of pure MnS. A half cell using Fe 0.5 Mn 0.5 S as electrode material achieves a high first cycle coulombic efficiency of 78.0% and a high reversible capacity of ca. 477 mAh g −1 after 35 cycles, while for pure MnS the first cycle coulombic efficiency is only 45.9% and the capacity rapidly fades to ≈200 mAh g −1 after 15 cycles. Although the solid solution state of Fe 0.5 Mn 0.5 S cannot be retained during conversion reaction as indicated by X‐ray diffraction (XRD), X‐ray absorption spectroscopy (XAS), and transmission electron microscopy (TEM), the initial discharge “polarization”, which has been considered as one of the major hurdles for conversion reaction, can be significantly reduced by this type of material design. In addition, the size and distribution of the nucleated nanophases might also be altered by the initial solid solution state of Fe 0.5 Mn 0.5 S, contributing to the improved electrochemical performance reported here.