Microstructure and Macrosegregation of 7050 Alloy Large Flat Billet in Ultrasonic Semi-Continuous Casting
Dingxin Chen,Xiaoqian Li,Dongzhu Guo,Ying Cui,Ripeng Jiang
2012-01-01
Abstract:The ultrasonic field was introduced into the casting process of the aluminum alloy 7050 flat billet with the size of 500 mm × 1320 mm. The microstructure, distribution of grain and the macrosegregation were investigated comparatively under conventional casting and ultrasonic casting. The results show that, after ultrasonic treatment (UST), the grain size is refined, and the growth of coarse-dendrites is restrained, meanwhile, the distribution of microstructure of the billet becomes more uniform. The level of macrosegregation along different direction is reduced under ultrasonic field, where the segregation index of Zn, Mg and Cu, along the symmetry axis in the direction of length and width, is decreased from 0.1013, 0.1117, 0.1260 and 0.1119, 0.1113, 0.1281 to 0.0835, 0.0790, 0.1027 and 0.0743, 0.0725, 0.0841, respectively. With the effects of ultrasonic cavitation and ultrasonic flows, the temperature field and the flow field in the liquid pool are changed, which improves the circumstance of grains formation and promotes the uniform distribution of solute elements, so refining the grain size and weakening macro-segregation behavior.