Abstract:Under various compressive strain rates, sea ice fails in different modes and behaves a brittle-ductile transition. To investigate the mechanism behind the transition, a fieldwork of uniaxial compression tests were performed on the level ice collected from Northeast of the Bohai Sea. The ice owns a typical h2 columnar structure, whose salinity varies from 5.5% to 7.4% while temperature ranges from -15 degrees C to -18.3 degrees C. In the experiments, the samples with uniform dimension of 50 mmx50 mmx107 mm were applied compressive load across to the grain columns. The data shows that the maximum failing stress is 4.7MPa appears at 2.8x10(-3) s(-1) while the lowest value is 1.5 MPa at 4.7x10(-5) s(-1). During the compression tests, the samples failed in three different modes over a wide range of strain rate (4.5x10(-5)-7.5x10(-3) s(-1)). When the failing stress is further categorized by failure mode, the stain rate-stress relation shows a consistent trend in each mode. Under low strain rate, the compressive strength has positive correlation with strain rate. The crack propagation is limited due to the stress concentration at crack tip is relaxed by creep, which leads to a ductile failure. When stain rate is between 9x10(-4) and 5x10(-3) s(-1), the crack was able to develop stably through the specimen along the loading direction and formed a splitting failure. The crack development became unstable and inclined cracks were preferred under high strain rate, where ice failed in a spalling mode. From ductile failure to splitting, the transition is terms of the competition between crack-tip creep and propagation. With sufficient confinement, the spalling dominates the global failure as splitting is suppressed. For both failure mode transitions, the condition is triggered by stain rate. From the measurements, it shows that each failure mode owns an according stress-strain rate relation, which is believed to explain the Brittle-ductile transition. Moreover, the influence of stain rate on the effective elastic modulus is discussed.

Experimental Study of the Fracture Toughness of Natural Freshwater Ice

Experimental Technique for Ice under Dynamic Compressive Loading

Experimental Study on Mixed-Mode (I–II) Fracture Toughness of Freshwater Ice

Experimental study of tearing toughness KIIIC for fresh water ice

The Experiment of Fracture Mechanics Characteristics of Yellow River Ice

Method for Testing Shear and Tensile Strengths of Freshwater/Seawater Ice

Study of the influence of thickness on the fracture toughness of fresh water ice by compact compression test specimen (CCTS)

Flexural Strength and Effective Modulus of Large Columnar-Grained Freshwater Ice

Uniaxial Compressive Strength and Fracture Mode of Lake Ice at Moderate Strain Rates Based on a Digital Speckle Correlation Method for Deformation Measurement

Laboratory-scale mixed-mode I/II fracture tests on columnar saline ice

Experimental investigation on mechanical properties and failure mechanism of rock-like specimens containing an arc-shaped ice-filled flaw under uniaxial compression

Experimental Study on the Mechanical Properties of the Songhua River Ice

The Study On Brittle-Ductile Transition Mechanism And Failure Mode Of Sea Ice Under Uniaxial Compression

Simulation Analysis of Three-Point Bending Fracture Process of Yellow River Ice

Experimental Study on Uniaxial Compressive Strength of Reservoir Ice

Experiments on Sea Ice Fracture Toughness in the Bohai Sea

A New Fracture Model for Reservoir Ice Layers in the Northeast Cold Region of China

Summary of the Test Methods for Icing Strength of Freshwater and Seawater

Bending Strength and Effective Modules of Songhua River Ice

Thickness-independent fracture in columnar freshwater ice: An experimental study

An Experimental Study of the Dynamic Friction Coefficient between Freshwater Ice and Structural Materials