Upconversion luminescence of YLiF4:Er3+ synthesized by hydrothermal method

Suling Zhao,Yanbing Hou,Xiaojiang Jiang Pei,Zheng Xu

DOI: https://doi.org/10.3321/j.issn:1000-4343.2006.02.005

2005-01-01

Abstract:YLiF4:Er3+ was synthesized by hydrothermal method. Concentration of Er3+ is changed from 0 to 5 %. The absorption of Er3+ in all samples from 200 to 1200 nmwas measured at room temperature. The J-O parameters calculated from absorption spectrum are Omega(2) = 1.05 x 10(-20) cm(2), Omega(4) = 1.25 x 10(-20) cm(2) and Omega(6) = 1.35 x 10(-20) cm(2). Infrared-to-visible upconversion emission of YLiF4:Er3+ was observed when excited by 980 nm. The results show that the Er3+ content is less than 1.5%, excite-state absorption is the main mechanism of upeonversion emission. When Er3+ content is larger than 1.5%, both of the excite-state absorption and energy transfer lead to the upconversion luminescence. The upconversion intensity was enhanced with the increasing of Er3+ concentration. At room temperature, the lifetime of H-2(11/2) and S-4(3/2) is 205 mu s while that of F-4(9/2) is 188 mu s for sample Er-2. The transition rates and quantum efficiency were also calculated. The quantum efficiencies of S-4(3/2) and F-4(9/2) are 27.9% and 10.7%, respectively.