Enthalpy relaxation behaviour of Al-Si-Cr quasicrystalline and amorphous alloys upon annealing

A. Inoue,A. P. Tsai,H. M. Kimura,T. Masumoto

DOI: https://doi.org/10.1007/BF01174667

IF: 4.5

1988-01-01

Journal of Materials Science

Abstract:Annealing-induced enthalpy relaxation behaviour was examined calorimetrically in quasicrystalline Al62Si19Cr19 and amorphous Al60Si25Cr15 alloys. When both alloys annealed at temperatures belowTx are reheated, an excess endothermic reaction (enthalpy relaxation) occurs reversibly above the annealing temperature,Ta. The peak temperature of ?Cp,endo rises in a continuous manner with the logarithm of annealing time (ta). The magnitudes of ?Cp,endo and ?Hendo of the amorphous alloy increase with increasingTa while no appreciable change in ?Cp,endo and ?Hendo of the quasicrystal withTa is seen. The activation energy,Qm, for the enthalpy relaxation increases from 1.8 to 2.7 eV with the peak temperature of ?CpTm, for the amorphous alloy, whereas it remains constant (?1.3 eV) for the quasicrystal. The endothermic reaction with smallOm for the quasicrystal is thought to be attributable to the disappearance of short-range ordering of chromium and silicon atoms with stronger attractive interaction, which developed during annealing, i.e. the reversion phenomenon, in the unrelaxed localized regions with high free-energy isolately embedded in the more stable icosahedral structure. The similarity of the enthalpy relaxation behaviour between the quasicrystalline and amorphous phases allows us to infer that short-range atomic configuration is very similar between the quasicrystalline and amorphous phases.