Abstract:Research highlights ▶ Ca(AlH 4 ) 2 can be synthesized by ball-milling NaH/Al and CaCl 2 instead of NaAlH 4 and CaCl 2 . ▶ Introducing CeAl 4 catalyst can accelerate the synthetic process of Ca(AlH 4 ) 2 and improve its dehydrogenation performance. ▶ The CeAl 4 -doped Ca(AlH 4 ) 2 can desorb more than 5.5 wt.% hydrogen below 200 °C. Abstract CeAl 4 -doped Ca(AlH 4 ) 2 was synthesized by reactive ball-milling NaH/Al and CaCl 2 with a few moles of CeAl 4 catalyst under hydrogen atmosphere. Its synthesis mechanism and dehydriding behavior were systematically investigated by XRD, FTIR, TG/DSC and TPD analyses. These results show that the synthetic process of Ca(AlH 4 ) 2 can be divided into two steps: the first step is ball-milling NaH/Al with CeAl 4 under hydrogen atmosphere to form CeAl 4 -doped NaAlH 4 , the second step is ball-milling the as-synthesized CeAl 4 -doped NaAlH 4 and CaCl 2 to form CeAl 4 -doped Ca(AlH 4 ) 2 . The CeAl 4 -doped Ca(AlH 4 ) 2 can desorb more than 5.5 wt.% hydrogen below 200 °C with an acceptable reaction kinetics, and shows attractive dehydriding behavior better than that of Ca(AlH 4 ) 2 directly prepared by primary NaAlH 4 and CaCl 2 . Keywords Complex hydride Ca(AlH 4 ) 2 Hydrogen storage Reactive ball-milling CeAl 4 -doped 1 Introduction Hydrogen is considered as an environmental friendly energy carrier because the produces almost zero pollution emitted from hydrogen fuel equipments. The lack of suitable high density storage hydrogen material remains one of the important problems for the development of hydrogen energy utilization [1] . Complex metal hydrides show much promise, but their hydriding/dehydriding kinetics need to be improved under moderate temperature and pressure [2,3] . Since the breakthrough work by Bogdanović and Schwickardi who showed that NaAlH 4 doped with Ti alkoxides or chlorides could reversibly desorb and absorb hydrogen below 150 °C, sodium alanate has been investigated intensively [4–6] . However, utilization of such Ti-compounds as dopants generally gives birth to nonvolatile byproduct (sodium-chloride) that occupies a significant weight percentage [4,5] . Recently, our investigations found that directly doping catalytic active species (CeAl 4 ) instead of catalytic precursor (CeCl 3 ) into NaAlH 4 can enhance its kinetics without decrease of hydrogen capacity [7] . It is believed that CeAl 4 may also have similar catalyzing effects on other complex aluminum hydrides (such as Li AlH 4 , Ca(AlH 4 ) 2 ). So far the hydrogen storage capacity of catalyzed NaAlH 4 system was difficult to break through 5.5 wt.%. Besides NaAlH 4 , other alkaline complex aluminum hydrides with higher mass and volume densities of hydrogen have also attracted attention in the past few years [8–10] . Among these, Ca(AlH 4 ) 2 has a total hydrogen capacity of 7.8 wt.%. The decomposition of Ca(AlH 4 ) 2 can mainly divided into four steps [9] , the first two decomposition steps (Ca(AlH 4 ) 2 first decomposes into CaAlH 5 , Al and H 2 ; and then CaAlH 5 decomposes into CaH 2 , Al and H 2 ) release 5.9 wt.% H 2 , which could be considered for practical applications. Currently, investigations about Ca(AlH 4 ) 2 were mainly concentrated on the synthetic method and theoretical calculation [10–13] . It was reported that the Ca(AlH 4 ) 2 and CaAlH 5 can be synthesized using AlH 3 and CaH 2 as primary material [14,15] . CaAlH 5 can hydrogenate/dehydrogenate reversibly by the DSC measurement and DFT calculation [11,16] . However, the rehydrogenation of CaAlH 5 to form Ca(AlH 4 ) 2 is the endothermic reaction, indicating the Ca(AlH 4 ) 2 system is a non-reversible hydrogen storage material. It is well known that the metal element contents of earth crust are 7.73 wt.% for Al, 3.45 wt.% for Ca and 2.74 wt.% for Na, respectively. So it seems that Ca(AlH 4 ) 2 is the promising off-board hydrogen storage candidate. It was ever reported that the decompositions of Ca(AlH 4 ) 2 and CaAlH 5 are kinetically stabilized with rather high activation energy [14] , resulting in slow dehydrogenation process. The catalytic modification and dehydriding performance of Ca(AlH 4 ) 2 system were studied much less than those of NaAlH 4 system. In this work, we synthesized CeAl 4 -doped Ca(AlH 4 ) 2 by reactive ball-milling NaH/Al and CaCl 2 with a few moles of CeAl 4 catalyst. The synthesis mechanism of CeAl 4 -doped Ca(AlH 4 ) 2 was investigated. Moreover, for comparison, the dehydrogenation processes of synthesized Ca(AlH 4 ) 2 doped with and without CeAl 4 catalyst were characterized and compared by simultaneous thermogravimetry, differential scanning calorimetry. The CeAl 4 -doped Ca(AlH 4 ) 2 can desorb more than 5.5 wt.% hydrogen below 200 °C. 2 Experimental The starting materials of NaH powder (purity 95%), Al powder (purity 99%), NaAlH 4 (purity >95%) and CaCl 2 (purity ≥96%) which purchased from Sigma–Aldrich Corp. were used as received. CeAl 4 catalyst (purity 99%) was prepared by induction melting stoichiometric mixtures of pure Ce (purity 99%) and Al (purity 99.9%) metals, which detail can be found in our previous paper [7] . The samples were handled and stored in a glove box with a dry argon atmosphere to prevent any contact with oxygen or moisture. The CeAl 4 -doped Ca(AlH 4 ) 2 was synthesized by two-step process. First, about 2.5 g mixture of NaH, Al and CeAl 4 in a mole ratio of 1:1:0.02 was milled in the Planetary mill for 0–90 h under a hydrogen pressure of 3 MPa. The CeAl 4 -doped NaAlH 4 was synthesized when the milling time increases to 90 h. Second, mixture of CeAl 4 -doped NaAlH 4 and CaCl 2 (NaAlH 4 and CaCl 2 with a mole ratio of 2:1) according to the reaction: 2NaAlH 4 + CaCl 2 → Ca(AlH 4 ) 2 + 2NaCl with a total amount of 2.08 g was milled in the Planetary mill for 0–20 h under a hydrogen pressure of 2 MPa. The ball-to-powder weight ratio was around 40:1. The structural characteristics of the as-synthesized samples were determined by means of by X-ray diffractometer (XRD, X’Pert Pro) with Cu Kα radiation at 40 kV and 40 mA. A special plastic tape was used to prevent the XRD sample from contacting with water air and moisture. A–H vibrations in the samples were identified using a Fourier infrared spectrometer (FTIR, Bruker Tensor27). The powder sample was mixed uniformly with KBr powder at a weight ratio of about 1:30 and then the mixture was cold pressed into a pellet of 13 mm diameter for testing. The heat decomposition features of samples were also measured by a synchronous thermal analyses thermogravimetry and differential scanning calorimetry (TG/DSC, Netzsch STA 449F3). The heating rate was 3–10 °C/min and the flow rate of argon protective gas was 40 ml/min. Thermal programmed desorption (TPD) of CeAl 4 -doped Ca(AlH 4 ) 2 sample was carried out on a Sievert's type apparatus and heated to the assigned temperature at a rate of 2 °C/min. The hydrogen capacity was calculated in weight percent and normalized to the weight of Ca(AlH 4 ) 2 with CeAl 4 catalyst, but the weight of NaCl was excluded. 3 Results and discussions Ca(AlH 4 ) 2 was generally synthesized by a metathesis reaction of NaAlH 4 and CaCl 2 [12,17] . However, as a raw material of hydride, NaH and Al are cheap than NaAlH 4 . So we chose NaH/Al and CaCl 2 instead of NaAlH 4 and CaCl 2 as raw materials to synthesize Ca(AlH 4 ) 2 . To investigate the mechanics of synthesis, the XRD patterns of NaH/Al + 0.02 CeAl 4 ball-milled under 3.0 MPa initial hydrogen pressure for different milling-times are shown in Fig. 1 . It can be found that the NaH and Al diffraction peaks become weaker and broader when milling-time increases to 30 h, indicating the average crystallite size is strongly reduced. At the same time, the Na 3 AlH 6 diffraction peaks are detected in Fig. 1 (b). After ball-milled for 60 h, some Na 3 AlH 6 and broader Al diffraction peaks together with NaAlH 4 diffraction peaks can be detected in Fig. 1 (c), indicating that NaH and Al are completely hydrogenated to form Na 3 AlH 6 , and some Na 3 AlH 6 and Al are further hydrogenated to form NaAlH 4 . When the milling-time increases to 90 h, Na 3 AlH 6 and Al diffraction peaks are almost disappeared, suggesting they completely transform to the NaAlH 4 in Fig. 1 (d). The above results indicate that the NaAlH 4 can be synthesized according to reactions (1) and (2) [6,7] . Moreover, it is remarkable to note that the CeAl 4 diffraction peaks remain unchanged in the whole ball-milling process. Here, the CeAl 4 catalyst plays a critical role in the formation of NaAlH 4 from NaH and Al [7] . (1) 3 NaH + Al + 1.5 H 2 ↔ N a 3 AlH 6 (2) N a 3 AlH 6 + 2 Al + 3 H 2 ↔ 3 NaAlH 4 The XRD patterns of mixtures of as-synthesized CeAl 4 -doped NaAlH 4 and CaCl 2 (NaAlH 4 and CaCl 2 with a mole ratio of 2:1) ball-milled for different milling-times under 2.0 MPa initial hydrogen pressure are also shown in Fig. 1 . After ball-milled for 5 h, the sample consists of NaAlH 4 and CaCl 2 main phases together with CeAl 4 minor phase. Except the CaCl 2 ·(H 2 O) 4 comes from the impure phase of CaCl 2 reactant, no new phase has been found in Fig. 1 (e). Some NaAlH 4 and CaCl 2 diffraction peaks are disappeared as the milling-time increases to 10 h, while the Ca(AlH 4 ) 2 and NaCl diffraction peaks are present in the sample. When the milling-time increases to 20 h, the NaAlH 4 and CaCl 2 phases are disappeared completely, and the Ca(AlH 4 ) 2 phase can be detected obviously in Fig. 1 (g). The CeAl 4 phase is almost unchanged in the whole synthetic process. These results suggest that the Ca(AlH 4 ) 2 can be synthesized according to reaction (3) [12,17] : (3) 2 ( 0.02 CeAl 4 -doped NaAlH 4 ) + CaCl 2 → 0.04 CeAl 4 -doped Ca ( AlH 4 ) 2 + 2 NaCl The synthetic process of Ca(AlH 4 ) 2 can be mainly divided into two steps: the first step was ball milling NaH/Al with CeAl 4 under hydrogen to form CeAl 4 -doped NaAlH 4 , and the second step was ball milling the as-synthesized CeAl 4 -NaAlH 4 and CaCl 2 to form CeAl 4 -doped Ca(AlH 4 ) 2 . To further identify the chemical reactions occurring during the ball milling process, the FTIR spectra of the as-synthesized CeAl 4 -doped NaAlH 4 and Ca(AlH 4 ) 2 are shown in Fig. 2 . It is well known that the characteristic band of Al–H bond changes with different chemical environment. The as-synthesized 0.02CeAl 4 -doped NaAlH 4 exhibits two infrared active vibration peaks in 1640 and 1675 cm −1 , the as-synthesized 0.04CeAl 4 -doped Ca(AlH 4 ) 2 also exhibits two vibration peaks in 1640 and 1797 cm −1 . The vibration peak at 1640 cm −1 can be associated to water bending vibration visible [18] , it may be due to the moisture present in test system during the characterization of the as-synthesized samples. It can be found that, the band at 1675 cm −1 corresponds to a Al–H stretching vibration for NaAlH 4 , and the band at 1797 cm −1 corresponds to a Al–H stretching vibration for Ca(AlH 4 ) 2 [19] . This result suggests further that the as-synthesized NaAlH 4 and CaCl 2 have transformed completely to Ca(AlH 4 ) 2 according to reaction (3) . Fig. 3 presents the TG/DSC profiles of the as-synthesized 0.02CeAl 4 -doped NaAlH 4 , primary Ca(AlH 4 ) 2 and as-synthesized 0.04CeAl 4 -doped Ca(AlH 4 ) 2 . The primary Ca(AlH 4 ) 2 was directly synthesized from primary NaAlH 4 and CaCl 2 without doping catalyst. It can be found that two weight loss signals about 2.56 wt.% at the first endothermic peak of 172 °C, and 1.68 wt.% at the second endothermic peak of 200 °C appear in the TG curve of 0.02CeAl 4 -doped NaAlH 4 , which are in agreement with previous reports [6] . Moreover, 0.04CeAl 4 -doped Ca(AlH 4 ) 2 desorbs 2.46 wt.% hydrogen at the first exothermic peak of 76.9 °C, and desorbs 2.36 wt.% hydrogen at the second endothermic peak of around 205 °C, which total dehydriding capacities in first two stages are high than that of 0.02CeAl 4 -doped NaAlH 4 . This result indicates that Ca(AlH 4 ) 2 system is a potential candidate for off-board hydrogen storage material with large capacity. Moreover, although the 0.04CeAl 4 -doped Ca(AlH 4 ) 2 shows a slight decrease of dehydriding capacity, compared to that of primary Ca(AlH 4 ) 2 . The dehydriding temperature of CeAl 4 -doped Ca(AlH 4 ) 2 is much lower than that of primary Ca(AlH 4 ) 2 . It indicates that the CeAl 4 catalyst can improve the dehydrogenation performance of Ca(AlH 4 ) 2 effectively, which catalysis may be similar to that in the NaAlH 4 system [7] . In order to gain the insight of the improved dehydrogenation of CeAl 4 -doped Ca(AlH 4 ) 2 , the reaction kinetics parameters (activation energy E a and pre-exponential factor A ) were measured by the Kissinger relation of reaction (4) [14,20] : (4) ln β T p 2 = − E a R T p + ln A R E a where β is the heating rate, T p is the transformation peak temperature that changed with different heating rate, E a is the activation energy, R is the gas constant, and A is the pre-exponential factor. A series of DSC measurements were conducted at different heating rates of 3, 5, 8 and 10 °C/min for the as-synthesized 0.04CeAl 4 -doped Ca(AlH 4 ) 2 in Fig. 4 (a) . With increasing the heating rate, T p shifts towards the higher temperature side [14] . It is important to note that, the first weak exothermic peak between 72 and 96 °C can be attributed to the decomposition of Ca(AlH 4 ) 2 into CaAlH 5 , Al and H 2 , the second endothermic peak between 198 and 217 °C can be attributed to the decomposition of CaAlH 5 into CaH 2 , Al and H 2 [9] . The relation of ln ( β / T p 2 ) vs. 1/ T p was plotted in Fig. 4 (b), the activation energy E a and pre-exponential factor A can be calculated from the slope − E a / R and the intercept ln( AR / E a ) according to reaction (4) . The values of E a and A of the primary Ca(AlH 4 ) 2 were also determined and compared in Table 1 for comparison. It is found that the E a values of Ca(AlH 4 ) 2 and CaAlH 5 are reduced, and their A values are enhanced obviously after doped with CeAl 4 catalyst. The changes of E a and A also agree with the TG/DSC results in Fig. 3 . The reduction of activation energy is associated with the change in the rate-limiting step [21] , which finally improves the dehydriding kinetics of CeAl 4 -doped Ca(AlH 4 ) 2 . However, further investigation on the reaction path of dehydrogenation and its rate-limiting step in CeAl 4 -doped Ca(AlH 4 ) 2 system are needed in the future. Fig. 5 is the TPD curve of as-synthesized 0.04CeAl 4 -doped Ca(AlH 4 ) 2 . The sample was heated from 30 to 200 °C with a heating rate of 2 °C/min. Hydrogen desorption starts at about 70 °C, and increases noticeably with increasing the temperature from 100 to 200 °C. In the temperature ranges of 70–140 °C and 140–200 °C, two dehydrogenation steps take place one after the other to desorb 2.74 and 2.79 wt.% hydrogen (equivalent to about 1.5 and 1.5 mol H atoms vs. Ca(AlH 4 ) 2 ). It is important to point out that the CeAl 4 -doped Ca(AlH 4 ) 2 can desorb more than 5.5 wt.% H 2 below 200 °C with acceptable dehydriding kinetics. 4 Conclusion As a summary, the CeAl 4 -doped Ca(AlH 4 ) 2 was successfully synthesized by ball-milling NaH/Al and CaCl 2 instead of NaAlH 4 and CaCl 2 . Introducing a few moles of CeAl 4 catalyst can accelerate the synthetic process of Ca(AlH 4 ) 2 and improve its dehydrogenation performance. The activation energies of Ca(AlH 4 ) 2 and CaAlH 5 are reduced after doped with CeAl 4 catalyst, resulting in the enhancement of dehydriding kinetics of calcium alanate hydride. The dehydrogenation of CeAl 4 -doped Ca(AlH 4 ) 2 starts at 77 °C, and desorb more than 5.5 wt.% H 2 below 200 °C. Acknowledgments This work was financially supported by the National Basic Research Program of China under Grant No. 2007CB209701 and 2010CB631300 , the National Natural Science Foundation of China under Grant No. 51001090 , 50871099 and 50631020 , the China Postdoctoral Science Foundation under Grant No. 20080440196 and 200902622 , and the University Doctoral Foundation of the Ministry of Education under Grant No. 20090101110050 . References [1] L. Schlapbach A. Züttel Nature 414 2001 353 358 [2] J. Yang S. Hirano Adv. Mater. 21 2009 3023 3028 [3] B. Bogdanović U. Eberle M. Felderhoff F. Schüth Scripta Mater. 56 2007 813 816 [4] B. Bogdanović M. Schwickardi J. Alloys Compd. 253–254 1997 1 9 [5] B. Bogdanović R.A. Brand A. Marjanovic M. Schwickardi J. Tölle J. Alloys Compd. 302 2000 36 58 [6] X.Z. Xiao L.X. Chen X.L. Fan X.H. Wang C.P. Chen Y.Q. Lei Q.D. Wang Appl. Phys. Lett. 94 2009 041907-1 041907-3 [7] X.L. Fan X.Z. Xiao L.X. Chen K.R. Yu Z. Wu S.Q. Li Q.D. Wang Chem. Commun. 44 2009 6857 6859 [8] Q.A. Zhang Y. Nakamura K. Oikawa T. Kamiyama E. Akiba Inorg. Chem. 41 2002 6547 6549 [9] M. Mamatha C. Weidenthaler A. Pommerin M. Felderhoff F. Schüth J. Alloys Compd. 416 1–2 2006 303 314 [10] A. Marashdeh T.J. Frankcombe J. Chem. Phys. 128 23 2008 234505-1 234505-5 [11] C. Wolverton V. Ozolins Phys. Rev. B 75 6 2007 064101 064115 [12] K. Komiya N. Morisaku Y. Shinzato K. Ikeda S. Orimo Y. Ohki K. Tatsumi H. Yukawa M. Morinaga J. Alloys Compd. 446 2007 237 241 [13] T. Sato M.H. Sorby K. Ikeda S. Sato B.C. Hauback S. Orimo J. Alloys Compd. 487 1–2 2009 472 478 [14] V. Iosub T. Matsunaga K. Tange M. Ishikiriyama Int. J. Hydrogen Energy 34 2 2009 906 912 [15] H. Kabbour C.C. Ahn S.J. Hwang R.C. Bowman Jr. J. Graetz J. Alloys Compd. 446 2007 264 266 [16] A. Mamatha B. Bogdanović M. Felderhoff A. Pommerin W. Schmidt F. Schüth C. Weidenthaler J. Alloys Compd. 407 1–2 2006 78 86 [17] T.N. Dymova M. Mukhidin N.G. Eliseeva Zh. Neorg. Khim. 15 9 1970 2318 2320 [18] K. Bukka J.D. Miller J. Shabtai Clay Clay Miner. 40 1 1992 92 102 [19] M. Fichtner C. Frommen O. Fuhr Inorg. Chem. 44 10 2005 3479 3484 [20] H.E. Kissenger Anal. Chem. 29 1957 1702 1706 [21] X.B. Yu Y.H. Guo H. Yang Z. Wu D.M. Grant G.S. Walker J. Phys. Chem. C 113 13 2009 5324 5328

Abstract:A novel catalyst TiB 2 is used in preparing TiB 2 -doped sodium aluminium hydride under a low hydrogen pressure. NaAlH 4 can be directly synthesized by using TiB 2 as catalyst in about 5 h at 2 MPa hydrogen pressure. It shows that TiB 2 has a remarkable catalytic effect and can enhance the performance of hydrogen release. The highest hydrogen desorption capacity of the sample doped with 8 mol% TiB 2 is 5.02 wt.%. Thus, TiB 2 particles synthesized is a promising catalyst for synthesizing and catalysing the hydrogen absorption and desorption in light-metal complex hydrides. Keywords Metal hydrides TiB 2 Hydrogen storage material Catalysis 1 Introduction Owing to the limited supply of fossil fuels, hydrogen has attracted massive attention as an alternative energy carrier [1–5] . A key technical challenge for hydrogen application is how to develop a viable on-board storage medium. In the past few decades, lots of efforts have been made to explore on-board hydrogen storage systems, such as compressed hydrogen gas, cryogenic and liquid hydrogen, metal hydrides [6–14] . However, all of them lack efficiency for commercial applications. Recently, light metal complex hydrides are the focus of research for vehicular hydrogen storage. Among various metal complex hydrides [15–20] , sodium aluminium hydride (NaAlH 4 ) is considered as one of the most suitable solid-state hydrogen storage materials since Bogdanović and Schwickardi [21] found that Ti-catalyzed NaAlH 4 exhibited reversible hydrogen storage together with enhanced kinetics. Recently, great attention has been paid to prepare NaAlH 4 by milling NaH/Al with catalysts under hydrogen atmosphere, because this method could effectively reduce the cost and improve the hydrogen absorption and desorption of NaAlH 4 . J.M. Bellosta von Colbe synthesized NaAlH 4 by milling NaH/Al with TiCl 3 under hydrogen atmosphere with an initial pressure of 83 bar [22] . Later, Bitter [23] reported the synergistic effect on dehydrogenation kinetics of NaAlH 4 with doping Ti-catalyst. They discovered that the kinetics of NaAlH 4 had been improved greatly with doping 2 mol% Ti-catalyst. Moreover, Xiao et al. [24] reported that it was possible to achieve direct synthesis of NaAlH 4 by milling NaH/Al with TiF 3 catalyst for 50 h at 25 bar hydrogen pressure during the in situ hydrogenation process. However, there are many problems about the synthesis of NaAlH 4 by milling the NaH/Al mixture: long time of milling, high hydrogen pressure and byproduct. Therefore, it is necessary to explore a novel catalyst on the direct synthesis of NaAlH 4 from NaH and Al. In this paper, NaAlH 4 was synthesized by dry ball milling NaH/Al with novel TiB 2 catalyst under 1–2 MPa hydrogen pressure at ambient temperature. The hydrogen desorption performance of NaAlH 4 was also tested. 2 Experimental 2.1 Synthesis of NaAlH 4 The mixture of NaH(97%, Alfa Aesar)/Al(99.5%, Alfa Aesar) and 8 mol% TiB 2 (synthesized by solid state reaction) was introduced into a stainless steel vessel with stainless steel balls and milled in a planetary ball mill. The ball-to-powder weight ratio was 40:1, the mixture was milled (450 rpm) under Ar atmosphere for 15 h, and then milled (450 rpm) under 1–2 MPa hydrogen pressure for 0–40 h at ambient temperature. The different milling conditions of the samples are listed in Table 1 . All the operations were carried out in the glove box (Super 1220/750/900) under purified argon atmosphere (H 2 O: <10 ppm; O 2 : <10 ppm). 2.2 Characterization Phase compositions of the samples were studied by X-ray diffraction (XRD, Rigaku D/Max PC2500, Cu Kα radiation) and refined by GSAS program [25] . The dehydrogenation rates of the samples were measured at atmospheric pressure in flowing argon (about 35.3 ml/min) in a temperature programmed desorption (TPD, PX200) mode at a ramping rate of 2 °C/min. The weight loss percentage of the samples was calculated according to the weight of NaAlH 4 in the reactor. 3 Results and discussion 3.1 Effect of milling time Fig. 1 shows the X-ray diffraction patterns of as-prepared samples. Detailed preparation conditions for those samples are given in Table 1 . As shown in Fig. 1 a, the diffraction peaks of NaH and Al are broad and weak, and some peaks of Na 3 AlH 6 appear in sample S1-5. In sample S1-10, Na 3 AlH 6 becomes the main phase. When the milling time increases to 20 h (S1-20) and 30 h (S1-30), the peak intensity of Na 3 AlH 6 gradually decreases and NaAlH 4 peaks become sharp. As the milling time increases to 40 h (S1-40), Na 3 AlH 6 diffraction peaks completely disappear, suggesting that Na 3 AlH 6 is completely hydrogenated to form NaAlH 4 . In addition, when the hydrogen pressure is 2 MPa ( Fig. 1 b) without ball-milling (S2-0), no new phase appears. And when the ball-milling time is 5 h (S2-5), the diffraction peaks of NaH almost disappear and some peaks of NaAlH 4 and Na 3 AlH 6 can be detected. This demonstrates that the hydrogenation reaction NaAlH 4 occurs in a relatively short ball milling time. The conversion of NaAlH 4 can be completed under the synthesis condition of sample S2-15, exhibiting a high kinetic of hydrogenation. GSAS refinement is used to analyse the phase composition of the S2-15 sample. The calculated curve agrees well with the observed XRD pattern as shown in Fig. 2 . It can be seen that NaAlH 4 , Al and TiB 2 phases are existed in the S2-15 sample. The GSAS refinement results shown in Table 2 show that the contents of the NaAlH 4 , Al and TiB 2 phases are 57.53 wt.%, 23.90 wt.% and 18.57 wt.%, respectively. 3.2 Effect of hydrogen pressure As shown in Fig. 1 a, when the hydrogen pressure is 1MPa, the peaks of NaH and Al become broad and weak, and some peaks of Na 3 AlH 6 appear in sample S1-5. And Na 3 AlH 6 is the main phase in sample S1-10. When the hydrogen pressure increases to 2 MPa ( Fig. 1 b), the diffraction peaks of NaH in sampe S2-5 almost disappear and some peaks of NaAlH 4 and Na 3 AlH 6 can be detected. And the diffraction peaks of Na 3 AlH 6 almost disappear and NaAlH 4 is the dominant phase in sample S2-10. Therefore, a higher hydrogen pressure is helpful for the conversion of Na 3 AlH 6 to NaAlH 4 . Moreover, variation of the relative abundance of the NaAlH 4 , Na 3 AlH 6 , Al, TiB 2 of S1-10, S1-20, S1-30 and S1-40 samples from GSAS refinement results are shown in Fig. 3 . It can be seen that the content of NaAlH 4 phase in sample S1-20 is about 11.20 wt.%, which increases to 31.26 wt.% in sample S1-30 and 57.27 wt.% in sample S1-40. It can be concluded that the amount of NaAlH 4 increases with the milling time. In addition, the weight percentage of Na 3 AlH 6 phase decreases gradually (27.44 wt.% in S1-10, 20.55 wt.% in S1-20, 12.39 wt.% in S1-30) and finally vanishes in S1-40 sample. 3.3 Thermal decomposition characteristics Fig. 4 displays the hydrogen desorption of the S2-5, S2-15 and S1-40 samples. All the TPD curves exhibite two characteristic plateau regions. It is suggested that there are two weight loss steps which are attributed to the dehydrogenation of the synthesized NaAlH 4 and Na 3 AlH 6 , respectively. The TPD curve of the S2-5 system exhibites two weight-loss steps of 0.878% and 1.93 wt.%. And the two weight-loss steps of S2-15 sample obviously increase to 3.01% and 1.94 wt.%. It can be also seen obviously from Fig. 4 that the content of the NaAlH 4 phase increases with the milling time. In addition, the two weight-loss steps of S1-40 sample reach to about 3.12% and 1.90 wt.%. And the total dehydrogenation capacities observed are about 5.02 wt.%. These results show that TiB 2 plays an essential role in the synthesis and decomposition of NaAlH 4 . 4 Conclusions NaAlH 4 nanocrystalline is successfully obtained with TiB 2 catalyst via ball milling the mixture of commercial NaH and Al powder under hydrogen. With the increase of hydrogen pressure and milling time, the synthetic efficiency of NaAlH 4 increases significantly. And the highest dehydrogenation capacity observed is about 5.02 wt.%. It demonstrates that TiB 2 is a promising catalyst for enhancing hydrogen release in light-metal complex hydrides. Further investigations about the function of TiB 2 in the systhesis of sodium alanate hydride are on the way. Acknowledgements This work was financially supported by MOST projects ( 2007AA05Z149, 2007AA05Z108, 2010CB631303 ), NSFC ( 50631020, 50701025, 50971071 ) and MOE ( IRT-0927 ). References [1] L. Schlapbach A. Züttel Nature 414 2001 353 358 [2] W. Grochala P.P. Edwards Chem. Rev. 104 2004 1283 1315 [3] P. Chen Z.T. Xiong W.Z. Luo K. Lin K.L. Tan Nature 420 2002 302 304 [4] K. Yvon B. Bertheville J. Alloys Compd. 425 2006 101 108 [5] D. Chandra J.J. Reilly R. Chellappa JOM 58 2006 26 32 [6] H.W. Brinks C.M. Jensen S.S. Srinivasan B.C. Hauback D. Blanchard K. Murphy J. Alloys Compd. 376 2004 215 221 [7] V. Ozolins E.H. Majzoub T.J. Udovic J. Alloys Compd. 375 2004 1 10 [8] S. Satyapal J. Petrovic C. Read G. Thomas G. Ordaz Catal. Today 120 2007 246 256 [9] L.C.J. Rowsell O.M. Yaghi J. Am. Chem. Soc. 128 2006 1304 1315 [10] T. Ichikawa S. Isobe N. Hanada H. Fujii J. Alloys Compd. 365 2004 271 276 [11] K.A. Lokshin Y.S. Zhao Appl. Phys. Lett. 88 2006 131909 131911 [12] F. Fang S.Y. Zheng G.R. Chen G. Sang B. He S.Q. Wei D.L. Sun Acta Mater. 57 2009 1959 1965 [13] F.H. Wang Y.F. Liu M.X. Gao K. Luo H.G. Pan Q.D. Wang J. Phys. Chem. C 113 2009 7978 7984 [14] S.Y. Zheng F. Fang J. Zhang L.X. Sun B. He S.Q. Wei G.R. Chen D.L. Sun J. Phys. Chem. C 111 2007 14021 14025 [15] A. Züttle P. Wenger S. Rentsch P. Sudan Ph. Mauron C. Emmenegger J. Power Sources 118 2003 1 7 [16] S.C. Amendola S.L. Sharp-Goldman M.S. Janjua N.C. Spencer M.T. Kelly P.J. Petillo M. Binder Int. J. Hydrogen Energy 25 2000 969 975 [17] I.E. Malka T. Czujko J. Bystrzycki Int. J. Hydrogen Energy 35 2010 1706 1712 [18] P. Wang X.D. Kang H.M. Cheng Chem. Phys. Chem. 6 2005 2488 2491 [19] J.F. Mao Z. Wu T.J. Chen B.C. Weng N.X. Xu T.S. Huang Z.P. Guo H.K. Liu D.M. Grant G.S. Walker X.B. Yu J. Phys. Chem. C 111 2007 12495 12498 [20] X.D. Kang Z.Z. Fang L.Y. Kong H.M. Cheng X.D. Yao G.Q. Lu P. Wang Adv. Mater. 20 2008 2756 2759 [21] B. Bogdanović M. Schwickardi J. Alloys Compd. 253 1997 1 9 [22] J.M. Bellosta von Colbe M. Felderhoff B. Bogdanović F. Schüth C. Weidenthaler Chem. Commun. 37 2005 4732 4734 [23] C.P. Baldé B.P.C. Hereijgers J.H. Bitter K.P.D. Jong J. Am. Chem. Soc. 130 2008 6761 6765 [24] X.Z. Xiao L.X. Chen X.L. Fan X.H. Wang C.P. Chen Y.Q. Lei Q.D. Wang Appl. Phys. Lett. 94 2009 041907 041909 [25] B.H. Toby J. Appl. Cryst. 34 2001 210 213

Synthesis and dehydrogenation of CeAl4-doped calcium alanate

Investigation on Synthesis, Structure and Catalytic Modification of Ca(AlH4)2 Complex Hydride

Enhanced Hydriding−Dehydriding Performance of CeAl2-Doped NaAlH4 and the Evolvement of Ce-Containing Species in the Cycling

Direct synthesis of sodium alanate with novel catalytic TiB2

Remarkable Hydrogen Absorption/desorption Behaviors and Mechanism of Sodium Alanates In-Situ Doped with Ti-based 2D MXene

Sodium Alanate In-Situ Doped with Ti2C MXene with Enhanced Hydrogen Storage Properties

Synthesis of Nanoscale CeAl 4 and Its High Catalytic Efficiency for Hydrogen Storage of Sodium Alanate

Investigation on the nature of active species in the CeCl3-doped sodium alanate system

Ce/MgAl mixed oxides derived from hydrotalcite LDH precursors as highly efficient catalysts for ketonization of carboxylic acid

Improved de/hydrogenation properties and favorable reaction mechanism of CeH 2 + KH co-doped sodium aluminum hydride

Thermodynamics, Kinetics and Modeling Investigation on the Dehydrogenation of CeAl4-doped NaAlH4 Hydrogen Storage Material

Preparation and hydrogen storage characteristics of Ti-NaAlH4 complex hydride

Cerium hydride generated during ball milling and enhanced by graphene for tailoring hydrogen sorption properties of sodium alanate

Significantly Improved Hydrogen Storage Properties of Naalh4 Catalyzed by Ce-Based Nanoparticles

Ultrafine Nanocrystalline CeO2@C-Containing NaAlH4 with Fast Kinetics and Good Reversibility for Hydrogen Storage.

Synthesis and Hydriding/dehydriding Properties of Nanosized Sodium Alanates Prepared by Reactive Ball-Milling

The Hydrogen Storage Properties and Microstructure of Ti-Doped Sodium Aluminum Hydride Prepared by Ball-Milling

Directed Stabilization by Air-Milling and Catalyzed Decomposition by Layered Titanium Carbide Toward Low-Temperature and High-Capacity Hydrogen Storage of Aluminum Hydride

Dehydriding properties of γ-AlH3

Hydriding-dehydriding Kinetics and the Microstructure of La- and Sm-doped NaAlH4 Prepared Via Direct Synthesis Method

Active Species of CeAl(4) in the CeCl(3)-doped Sodium Aluminium Hydride and Its Enhancement on Reversible Hydrogen Storage Performance.