Electrochemical properties and structure of TiNi alloy subjected by ion implantation with titanium and niobium
V. О. Semin,А. P. Chernova,А. V. Erkovich,M. G. Ostapenko,F. А. D’yachenko,K. P. Savkin,E. D. Khabibova,L. L. Meisner,,,,,,,,
DOI: https://doi.org/10.30791/0015-3214-2023-6-5-23
2023-01-01
Physics and Chemistry of Materials Treatment
Abstract:The surface morphology, structure of oxide layers and electrochemical properties in a physiological solution (0.9 wt. % NaCl) of nickel titanium (TiNi) alloy subjected by ion implantation were studied. It was found that an irradiation of the TiNi surface with titanium and niobium ions at an irradiation dose of 1·1017 cm–2 led to the increase of the surface roughness and improvement of corrosion properties. The corrosion performance of ion-beam modified alloy was associated with a higher charge transfer resistance and a lower anodic current. Comparative analysis of the oxide layer structure, performed by transmission electron microscopy, and electrochemical properties revealed that an inhibiting of anodic processes was related with the phase composition and electrical conductivity of the oxide layer. In particular, the ion-beam treatment with niobium resulted in formation of a thin (~ 2 nm) amorphous oxide film onto the TiNi surface, that effectively prevented an oxidation of nickel due to dielectric properties characterized by dielectric constant ε = 44.