Abstract:Novel slight yellow CeO2single/multiwall hollow microspheres were synthesized by the hydrothermal method without any surfactant and characterized by x-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), field-emission scanning electron microscopy (FESEM), and x-ray photoelectron spectra (XPS). The results showed that the products were CeO2single/multiwall hollow microspheres, the shells of which were composed of CeO2nanoparticles with a mean size of 70 nm. The effect of the preparation conditions, the reaction temperature, the reaction time, and the molar ratios of urea to Ce(NO3)3·6H2O on the morphology of the products, was investigated. The optimal preparation conditions are determined as follows: the reaction temperature of 230 °C, the reaction time of 6 to 10 h, and the molar ratios of urea to Ce(NO3)3·6H2O of 3:1 to 6:1. The formation mechanism of CeO2single/multiwall hollow microspheres was proposed. The ultraviolet-visible (UV-VIS) diffuse reflectance spectra of the samples were measured. The results showed that the absorption edges of the samples were red-shifted compared with that of bulk CeO2, and that the red-shift of the absorption edges and the yellow of the samples enhanced with increasing the yield of CeO2single/multiwall hollow microspheres. The catalytic activity and the recycling performance of the sample on CO oxidation were tested and theT100%(the temperature at which CO 100% conversion) was 230 °C in the first run and decreased by 270 and 205 °C compared with that of bulk CeO2and CeO2nanocrystal, respectively.

Self-Assemblage of Single/Multiwall Hollow Ceo2 Microspheres Through Hydrothermal Method

Self-assembled Flower-Like Hierarchical Spheres and Nanobelts of Manganese Oxide by Hydrothermal Method and Morphology Control of Them

Study of the Preparation and Properties of CeO2single/multiwall Hollow Microspheres

Hydrothermal Synthesis, Characterization and Formation Mechanism of Self-Assembled Mesoporous SrTiO3 Spheres Assisted with Na2SiO3·9H2O

Facile Synthesis of Well-Defined CeO2 Hollow Spheres with a Tunable Pore Structure

Facile One-Step Synthesis of Double-Shelled CeO2 Hollow Spheres and Their Optical and Catalytic Properties

Self-template hydrothermal synthesis of CeO2 hollow nanospheres

Mesoporous-shelled CeO2 hollow nanospheres synthesized by a one-pot hydrothermal route and their catalytic performance

Template-Free Synthesis Of Single-Crystalline-Like Ceo2 Hollow Nanocubes

Facile Synthesis of Novel Hierarchical Hollow ZnO Microspheres

Self-Assembly of Monodispersed Silica Nano-Spheres with A Closed-Pore Mesostructure

Mesoscale organization of nearly monodisperse flowerlike ceria microspheres.

Hydrothermal synthesis and characterization of hollow SnO2 microsphere with open structure

Hierarchical Strontium Carbonate Submicron Spheres Self‐assembled under Hydrothermal Conditions

Hydrothermal synthesis and characterization of core/shell ALOOH microspheres

Hierarchical mesoporous SrCO3 submicron spheres derived from reaction-limited aggregation induced “rod-to-dumbbell-to-sphere” self-assembly

Solvthermal synthesis of CeO 2 hollow nanospheres

Novel CuS Hollow Spheres Fabricated by a Novel Hydrothermal Method

Hierarchical porous structures by using zeolite nanocrystals as building blocks

Synthesis and Characterization of Hollow Zeolite Microspheres with a Mesoporous Shell by O/W/O Emulsion and Vapor-Phase Transport Method

Hydrothermal Synthesis of Cerium Fluoride Hollow Nanostructures in a Controlled Growth Microenvironment