Abstract:The Co(OH)2,Co2(OH)2CO3 and CoC2O4 precursors were prepared by precipitation method using Co(CH3COO)2.4H2O as cobalt source,polyethylene glycol(PEG) 20 000 as surfactant,water?n-butanol as solvent system,and KOH,(NH4)2CO3 and H2C2O4.2H2O as precipitating agent,respectively.The nanocubic Co3O4 was synthesized through Co(OH)2 precursor at 160 ℃ by hydrothermal oxidation method.The catenuliform-like and rod-like Co3O4 powders were obtained when Co2(OH)2CO3 and CoC2O4 precursors were calcined at 450 ℃ and 400 ℃ for 3 h by hydrothermal?thermal decomposition method,respectively.The morphology and structure of precursor and Co3O4 product were characterized by thermogravimetry(TG),infrared(IR) spectrum,X-ray diffractometry(XRD) and transmission electron microscopy(TEM).The electrochemical performance of as-prepared Co3O4 with different morphologies was tested.The results show that the morphologies of Co3O4 change with the precursors prepared using different precipitating agents and methods.The cubic Co3O4 with particle size of 15 nm can be obtained using Co(OH)2 as precursor,and catenuliform-like Co3O4 with about 40 nm in diameter and 100 nm in length and rod-like Co3O4 with about 0.1 μm in diameter and 1 μm in length can be obtained using Co2(OH)2CO3 and CoC2O4 as precursors,respectively.The electrochemical performance of nano-Co3O4 is superior to that of micro-Co3O4.The cubic Co3O4 shows the best electrochemical performance in all the as-prepared Co3O4 samples,and its specific charge capacity retains 406 mA.h/g after 10 discharge-charge cycles.

Study on Thermo-Decomposition Process of the Precursor in the Preparation of Nano CoFe_2O_4

Thermo-Decomposition Process of Preparation of Nanometer Cobalt Ferrite Oxides and Their Doped into Peg-20000

The Characterization and Preparation of Nano-Scale Fe Doping Tio2 by Sol-Gel Method (I) - the Crystallization and Thermal Decomposition Process of Fe Doping Tio2 Xerogel Powders Using Thermal Tg-Ir Spectrometry

Study of CoFe2O4/CoFe2 nanostructured powder

HYDROTHERMAL SYNTHESIS AND MAGNETIC PROPERTIES OF CoFe2O4 NANO-POWDER

Comparative Study of CoFe2O4 Ferrite Nanosized Powders by the Sol-gel Method and Microwave Combustion Method

Thermal Decomposition Process of Oxalate Coprecipitation Precursor

Novel Preparation and Physicochemical Characterization of a Nanocrystalline Cobalt Ferrite System

Synthesis and Characterization of CoFe 2 O 4 Nanoparticles

Analysis on Calcination Process of WC–Co Precursor Powder

Study of preparation of cobalt cerium complex oxides catalyst by sol-gel method

Preparation of Cofe2o4 Nanocrystallite by Sol-Gel Combustion Synthesis and Evaluation of Its Reaction Performance

The Preparation and Haracterization of Nanograined soft Magnetic Mn-Zn Ferrite

Influence of precursor on morphology of Co_3O_4 and characterization

Studies on the magnetism of cobalt ferrite nanocrystals synthesized by hydrothermal method

Preparation of nanosized CoAl2O4 powders by sol–gel and sol–gel-hydrothermal methods

Synthesis and Characterization of Cobalt Ferrite through Co-Precipitation Technique

Preparation and characterization of Co_3O_4 by thermal decomposition from Co_2(OH)_2CO_3

Effect of preparation method on the surface properties and activity of Ni0.7Cu0.3Fe2O4 nanoparticles

Preparation of Core-Shell Ni (cu, Co)/Al Micron-Nano Composites and Characteristics of Thermite Reactions with Fe2o3

Preparation of Nano-CoFe2 O4,Al/CoFe2 O4 and Their Effects on Thermal Decomposition Performance of RDX