Highly Cis-1,4 Selective Polymerization of Conjugated Dienes Catalyzed by N-heterocyclic Carbene-ligated Neodymium Complexes
Shu Zhang,Na Wu,Yi-Xian Wu
DOI: https://doi.org/10.1007/s10118-020-2460-4
2020-07-27
Chinese Journal of Polymer Science
Abstract:Neodymium complexes containing <i>N</i>-heterocyclic carbene (NHC) ligands, NdCl<sub>3</sub>[1,3-R<sub>2</sub>(NCH=)<sub>2</sub>C:]·THF<sub><i>x</i></sub><b>(Nd1:</b> R = 2,6-<sup><i>i</i></sup>Pr<sub>2</sub>C<sub>6</sub>H<sub>3</sub>, <i>x</i> = 0; <b>Nd2:</b> R = 2,6-Et<sub>2</sub>C<sub>6</sub>H<sub>3</sub>, <i>x</i> = 1; <b>Nd3:</b> R = 2,4,6-Me<sub>3</sub>C<sub>6</sub>H<sub>2</sub>, <i>x</i> = 1) were synthesized and employed as precatalysts for the coordination polymerization of conjugated dienes (butadiene and isoprene). In combination with triisobutylaluminium (TIBA), <b>Nd1</b> promoted butadiene polymerization to produce extremely high <i>cis</i>-1,4 (up to 99.0%) polybutadienes with high molecular weight (<i>M</i><sub>w</sub> = 250–780 kg·mol<sup>−1</sup>). The <b>Nd1</b>/TIBA catalytic system also exhibited both high catalytic activity and <i>cis</i>-1,4 selectivity (up to 97.8%) for isoprene polymerization. The catalytic activity, molecular weight and molecular weight distribution of resulting polydienes were directly influenced by Al/Nd molar ratio, aging method, and polymerization temperature. Very interestingly, the high <i>cis</i>-1,4 selectivity of the catalyst towards butadiene and isoprene kept almost unchanged under different reaction conditions. The <i>cis</i>-1,4 polyisoprenes with high molecular weight (<i>M</i><sub>w</sub> = 210–530 kg·mol<sup>−1</sup>) and narrow molecular weight distribution (<i>M</i><sub>w</sub>/<i>M</i><sub>n</sub> = 1.9–2.7) as well as high <i>cis</i>-1,4 selectivity (~97%) could be synthesized by using the aged <b>Nd1</b>/TIBA catalytic system in the presence of isoprene (100 equivalent to Nd) at low Al/Nd molar ratios of 6–10. Polyisoprenes with low molecular weights (<i>M</i><sub>w</sub> = 12–76 kg·mol<sup>−1</sup>) and narrow molecular weight distributions (<i>M</i><sub>w</sub>/<i>M</i><sub>n</sub> = 1.7–2.6) were obtained by using <b>Nd2</b> and <b>Nd3</b> as precatalysts, indicating that the molecular weight of resulting polyisoprenes can be adjusted by changing the substitutes of ligand in Nd complex.
polymer science