Study on the Thermal Stabilization Effect of Antioxidant F on Polyoxymethylene

ZHAO Xiao-wen,YE Lin,LI Hui-lin
DOI: https://doi.org/10.3321/j.issn:1001-9278.2005.10.016
2005-01-01
Abstract:The thermal stabilization effect of antioxidant F on polyoxymethylene (POM) was studied and compared with a conventional antioxidant, Irganox245, through the measurements of isothermal weight loss analysis at 220 ℃, isothermal weight loss rate analysis at 222 ℃, balance torque analysis, multiple processing, and long-term aging analysis. After five times of extrusion, the yellow index (YI), melt flow rate (MFR), and the increment of MFR for antioxidant F stabilized POM were all lower than those for Irganox245 stabilized. Meanwhile, higher notched charpy impact strength and elongation at break were also achieved for antioxidant F stabilized POM. After long-term aging, the retaining rate of MFR,YI and mechanical properties of antioxidant F stabilized POM were comparable with those of Irganox245 stabilized. It was demonstrated that the antioxidant F constituted a good substitutive of Irganox245.
What problem does this paper attempt to address?