Abstract:Ti-50.6 at.% Ni alloy samples were coated with tantalum by the arc ion plating method with the aim to improve their radiopacity. Surface characteristics and corrosion resistance properties were investigated in the present study. The results of XRD show that the film as-deposited was composed of a metastable tetragonal β-phase tantalum which can transform into α-phase tantalum after annealing at 700 °C, 800 °C, 900 °C for 1 h, respectively. TEM observations show that thin nano-structured Ta layers were obtained in the as-deposited samples. Mixture of microcrystallite (approx. 40 nm) and large-size crystal (approx. 150 nm) α-phase tantalum was formed in the film after annealing at 700 °C. When annealed at 900 °C, the film is composed of dominantly uniform large-size α-phase tantalum. The results of XPS survey and high resolution spectra show that a thin oxide film with Ta2O5 in the outmost layer and tantalum suboxides in the inner layer, are formed inside tantalum coating as a result of natural passivation of Ta in the atmosphere. The corrosion resistance was determined by electrochemical methods in 0.9% NaCl solution at 37 °C. Both the as-deposited and annealed samples exhibit excellent corrosion resistance property. Compared to the untreated coating samples, the annealed Ta coating samples exhibit higher open-circuit corrosion potential (Ecorr), breakdown potential (Ebr), and lower passive current density (Ip). The results indicate that the annealing treatment can improve the corrosion resistance property.

Surface modification of TiNi alloy through tantalum immersion ion implantation

Corrosion behavior and surface characterization of tantalum implanted TiNi alloy

Effect of Ta2O5/TiO2 thin film on mechanical properties, corrosion and cell behavior of the NiTi alloy implanted with tantalum

Tantalum Coated NiTi Alloy by PIIID for Biomedical Application

Surface Modification of Ti−49.8at%Ni Alloy by Ti Ion Implantation: Phase Transformation, Corrosion, and Cell Behavior

Surface Characteristics and Corrosion Resistance Properties of TiNi Shape Memory Alloy Coated with Ta

Surface Characterization and Electrochemical Studies of Biomedical Niti Alloy Coated with Tin by Piiid

Surface characterization and immersion tests of TiNi alloy coated with Ta

The Effect of N+ Ion-Implantation on the Corrosion Resistance of HiPIMS-TiN Coatings Sealed by ALD-layers

Improvement on surface properties of titanium alloy by plasma immersion ion implantation technique

Effective Inhibition of Nickel Release by Tantalum-Implanted TiNi Alloy and Its Cyto-Compatibility Evaluation in Vitro

Role of tantalum and nickel ion implantation on corrosion resistance properties of a Ti–Al–Zr alloy

Surface Composition and Corrosion Property of TiNi Alloys Coated with Tantalum Films

Surface Characteristics, Nano-Indentation and Corrosion Behavior of Nb Implanted Niti Alloy

Electrochemical properties and structure of TiNi alloy subjected by ion implantation with titanium and niobium

Characterization of TiN, TiC and TiCN coatings on Ti–50.6 at.% Ni alloy deposited by PIII and deposition technique

Surface modification of steel by metal plasma immersion ion implantation using vacuum arc plasma source

Hemocompatibility investigation of the NiTi alloy implanted with tantalum

Effect on Surface Property of Hard Alloy by Ta Ion Implantation under Different Atmosphere

Biomedical Properties of Tantalum Coatings Prepared by Multi Arc Ion-Plating

Study on surface properties of Ti6Al4V alloy by oxygen plasma immersion ion implantation