Abstract:Ultra-high nickel single-crystal cathode materials have become the most promising for lithium-ion batteries. However, the preparation of ultra-high nickel single-crystal precursors by a continuous coprecipitation method has the disadvantages of large particle size, wide distribution, poor morphology. The extent of the inhomogeneous reactions can be more severe in single-crystal cathodes with larger particle size. Herein, the coprecipitation method with a solid concentrator was adopted, and citrate sodium was used as a complexing agent to improve the physical properties of precursors and electrochemical performance of single-crystal cathode materials. By analyzing the morphology and agglomeration mechanism of the precursor nucleuses under different pH values, it was found that hexagonal nanosheets grew along the 101 direction, and the primary particles showed thicker at pH of 11.4. The hexagonal nanosheets grew along the 001 direction, and the primary particles showed finer at pH of 12.2. The morphology and particle size uniformity of the secondary particles formed by agglomeration at these two pH values showed poor. However, hexagonal nanosheets grew synergistically along the 001 and 101 directions at pH of 11.8, so the primary particles with uniform particle size gradually agglomerated, and then the secondary particles with ultra-small particle size and uniform distribution obtained. Compared to materials prepared by the traditional continuous coprecipitation method, the precursor displays a smaller particle size(D50 = 1.8 µm), higher sphericity, uniformity and denser internal structure. In order to evaluate the performance of Ni0.94Co0.04Mn0.02(OH)2 with ultra-small particle size, the sintering conditions of LiNi0.94Co0.04Mn0.02O2 need to be explored. It was found that the LiNi0.94Co0.04Mn0.02O2 cathode material prepared at 790 °C exhibited higher discharge capacity, cycle and rate performance, compared to materials prepared at 760 °C and 820 °C. We further utilized TEM, EPMA, and XPS to test the internal structure and valence state of LiNi0.94Co0.04Mn0.02O2 cathode material. The results show that the LiNi0.94Co0.04Mn0.02O2 calcined at 790 °C has a good single crystal structure. The LiNi0.94Co0.04Mn0.02O2 cathode materials inherited the structure and particle size of Ni0.94Co0.04Mn0.02(OH)2 precursors, and displayed discharge capacity of 194.7 mAh/g and capacity retention rate of 89.8 % after 100 cycles at 1 C. The microstructure and phase transition of the as-prepared cathode material are well-maintained after long-term cycling, without obvious inter-crystalline micro-crack. The results indicate that its electrochemical performance is better than that of cathode materials with precursors prepared by a continuous coprecipitation method. This work provides new insights for the preparation of small-particle-size precursor and single-crystal cathode materials.

Performance of Lini0.5mn1.5o4 Prepared by Solid-State Reaction

Preparation and Electrochemical Properties of Li[Ni1/3Co1/3Mn1−x/3Zrx/3]O2 Cathode Materials for Li-ion Batteries

Preparation of Submicrocrystal LiMn2O4 Used Mn3O4 As Precursor and Its Electrochemical Performance for Lithium Ion Battery

The Effect of Precursors on Performance of LiNi0.5Co0.2Mn0.3O2 Cathode Material

Investigation on LiNi0.5Mn1.5O4 cathode material based on the precursor of nickel-manganese compound for lithium-ion battery

Synthesis of LiNi0.5Mn1.5O4 by Solid-State Reaction with Improved Electrochemical Performance

Electrochemical Performance Ni Doped Spinel LiMn2O4 Cathode for Lithium Ion Batteries

Application of precursor with ultra-small particle size and uniform particle distribution for ultra-high nickel single-crystal cathode materials by coprecipitation method

Precise Preparation Of High Performance Spherical Hierarchical Lini0.5mn1.5o4 For 5 V Lithium Ion Secondary Batteries

Study of LiNi0.5Mn1.5O4 Synthesized Via a Chloride-Ammonia Co-Precipitation Method: Electrochemical Performance, Diffusion Coefficient and Capacity Loss Mechanism

Preparation of Spinel LiMn2O4 from Manganese Oxide and Its Electrochemical Performance

LiNi_(0.5-x)Mg_xMn_(1.5)O_4(x=0,0.05) SYNTHESIZED BY LOW TEMPERATURE MOLTEN-SALT COMBUSTION METHOD AND ITS ELECTROCHEMICAL PERFORMANCE

Physical Properties and Electrochemical Performance of LiNi X Mn 2-X O 4 Cathode Materials Prepared Using a Precipitation Method

Synthesis and performance study of Li_(1.1)Ni_(0.35)Mn_(0.55)O_2 cathode material of lithium-ion batteries

Effect of precursor particle size and morphology on lithiation of Ni0.6Mn0.2Co0.2(OH)2

The Effects of a Mixed Precipitant on the Morphology and Electrochemical Performance of LiNi0.5Mn1.5O4 Cathode Materials

Preparation of Positive Material LiNi1/6Co1/6Mn2/3O2 for Li Ion Battery

Synthesis of cathode material LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2 and its electrochemical performances

Synthesis and Electrochemical Performance of LiNi0.5Mn1.5O4 Spinel Compound

Preparation and electrochemical performance of LiNi0.5Mn1.5O4 spinels with different particle sizes and surface orientations as cathode materials for lithium-ion battery

One-step Synthesis and Effect of Heat-Treatment on the Structure and Electrochemical Properties of LiNi0.5Mn1.5O4 Cathode Material for Lithium-Ion Batteries