Molten hydroxides synthesis of hierarchical cobalt oxide nanostructure and its application as anode material for lithium ion batteries
Minwei Xu,Fei Wang,Mingshu Zhao,Sen Yang,Xiaoping Song
DOI: https://doi.org/10.1016/j.electacta.2011.03.027
IF: 6.6
2011-01-01
Electrochimica Acta
Abstract:Hierarchical Co 3 O 4 nanostructure is synthesized via a self-assembled process in molten hydroxides. The morphologies, crystal structures and the phase transformation processes are analyzed by field-emission scanning electron microscopy, transmission electron microscopy, and X-ray diffraction. As an anode material for lithium ion batteries, the hierarchical Co 3 O 4 exhibit an initial capacity of 1336 mAh g −1 and a stable capacity of 680 mAh g −1 over 50 cycles. More importantly, high rate capability is obtained at different current densities between 140 and 1120 mA g −1 . The improved electrochemical performance of Co 3 O 4 could be attributed to the unique hierarchical nanostructure. Keywords Cobalt oxide Nanostructure Anode Lithium ion battery 1 Introduction Cobalt oxide (Co 3 O 4 ) has attracted increasing attention due to its unique properties and potential applications in diverse fields, such as catalysis, gas sensors and field-emission devices [1–4] . In addition, Co 3 O 4 is also regarded as a promising alternative anode material for rechargeable lithium ion batteries [5] , which exhibits a high theoretical capacity of 890 mAh g −1 . However, the severe volume expansion/contraction associated with Li + insertion and extraction processes causes the pulverization of electrode and leads to a rapid deterioration in capacity [6,7] . To overcome this intrinsical drawback, it is suggested that hybridizing Co 3 O 4 with carbon material is an effective approach [8,9] . Nevertheless, this strategy sacrifices the capacity of Co 3 O 4 due to the introduction of carbon. Moreover, the reliable synthesis of well-designed Co 3 O 4 /carbon nanocomposites remains a challenge. In general, it is well accepted that the morphology of Co 3 O 4 nanostructures can greatly affect their electrochemical properties [10,11] . Over the past few years, intensive researches have been devoted to the synthesis of novel Co 3 O 4 nanostructures, which reveals a promising way to improve the electrochemical performances of Co 3 O 4 anodes. For instance, various Co 3 O 4 nanostructures such as nanotubes [12,13] , octahedral cages [14] , mesoporous needles [15] , hollow structures [16,17] and pompon-like microspheres [18] have been reported and exhibit the enhanced electrochemical properties. However, there should be still much space for progress to achieve the satisfactory cycle performance and high rate capability for the practical application of Co 3 O 4 anodes, particularly in terms of novel morphology and controlled synthesis. In particular, hierarchical architectures assembled by low-dimensional building blocks have been considered to be the ideal nanostructures for enhanced electrochemical performances [19–21] . The improved properties could be mainly attributed to the loose structure, large surface area, and shortened Li + diffusion distance. The molten-salt synthesis method is one of the simple, versatile, and cost-effective approaches for obtaining oxide nanostructures [22] . Recently, Wang and co-workers demonstrated the feasibility of a composite-hydroxide-mediated (CHM) approach to synthesize oxide nanostructures [23] . This method is based on the reactions of raw materials in eutectic hydroxide melts and it provides a one-step, convenient, low cost, nontoxic and mass-production route for various oxide nanostructures. Up to now, a wide range of complex oxides, hydroxides and simple oxides has been synthesized by CHM approach, including BaTiO 3 , CoFe 2 O 4 , Pb 2 V 2 O 7 , Niobate, La(OH) 3 , CuO, CeO 2 , etc. [24–28] . However, to the best of our knowledge, there is few works to report the synthesis of Co 3 O 4 nanostructures via CHM approach. Herein, we adopt the so-called CHM approach to synthesize hierarchical Co 3 O 4 nanostructures. It is found that the as-obtained Co 3 O 4 nanostructure is assembled by extremely thin nanosheets. The reaction mechanism for the formation of Co 3 O 4 nanostructure in molten hydroxides is discussed. Motivated by the unique morphology, the electrochemical properties of the Co 3 O 4 nanostructure are investigated. In addition, the effect of the annealing temperature on the electrochemical performance is also presented. As anode material for lithium ion batteries, the hierarchical Co 3 O 4 nanostructure displays superior lithium storage properties with good cycle stability and high rate capability. 2 Experimental In a typical experiment, a teflon vessel filled with 20 g mixed hydroxides (NaOH:KOH = 51.5:48.5) was putted in a furnace and then heated up to 200 °C. When the hydroxides melted, 0.476 g CoCl 2 ·6H 2 O was added and the mixture was stirred until a uniform suspension was obtained. It is found that the black precipitates were formed immediately. After maintaining at 200 °C for a period of time, the vessel was taken out and cooled to room temperature naturally. Then, deionized water was added to dissolve the residual hydroxides. The precipitates were harvested by centrifugation and washed thoroughly with deionized water and ethanol. Finally, Co 3 O 4 samples were obtained by calcining the black precursors at 500 °C for 6 h. The heating rate was below 1 °C/min. The structure, morphology of the products were characterized with X-ray powder diffraction (XRD, Bruke D8-Advance, Cu-Kα, λ = 0.15406 nm), field-emission scanning electron microscope (FESEM, JEOL JSM-7100F) and transmission electron microscopy (TEM, JEOL JEM-2100). The N 2 adsorption and desorption isotherm was obtained at 77 K using Physisorption Analyzer (ASAP 2020). The BET surface area was estimated using adsorption data in a relative pressure ranging from 0.06 to 0.3. Electrochemical performance of the hierarchical Co 3 O 4 nanostructure was investigated with two-electrode Swagelok cells. For working electrodes, the Co 3 O 4 samples mixed with carbon black and polyvinylidene fluoride (PVDF) at a mass ratio of 70:20:10 were dispersed in N-methyl pyrrolidinone (NMP). Then, the slurry was coated uniformly onto copper foils ( Φ = 10 mm) and dried in vacuum at 100 °C for 12 h. Test cells were assembled in argon filled glove box. Metallic lithium foil was used as counter electrode. The electrolyte was made by dissolving 1 M LiPF 6 in the mixture of ethylene carbonate (EC) and diethylene carbonate (DEC) with the volume ratio of 1:1. Galvanostatical charge and discharge tests were carried out on a battery testing system (Arbin-BT2000) with the voltage range of 0.01–3.0 V (vs. Li/Li + ). Cyclic voltammograms were performed on Ametek VMC-4 electrochemical testing system between 3.0 V and 0 V at a scan rate of 0.5 mV s −1 . 3 Results and discussion In this work, the mixed hydroxides are employed not only as the solvent but also as the reactant for preparing the precursors. Fig. 1 a–d displays the morphological images of the precursors, which are obtained with a reaction time of 1 min (precursor A) and 8 h (precursor B). For precursor A obtained at the early stage, the XRD pattern ( Fig. 2 A) can be indexed to hexagonal β-Co(OH) 2 (JCPDS No. 30-0443). The formation of β-Co(OH) 2 is described as follows: (1) CoCl 2 + 2 NaOH/KOH → Co(OH) 2 + 2 NaCl/KCl It is well known that β-Co(OH) 2 nanocrystals are usually obtained in plate morphology due to its brucite-like layered structure [29] . As showed in Fig. 1 a–b, a large amount of β-Co(OH) 2 plates are observed. These plates are hexagonal. The size of the plates is several hundreds nanometers and the thickness is estimated to be less than 50 nm. Increasing the reaction time to 8 h (precursor B), biggish nanosheets instead of nanoplates is obtained ( Fig. 1 c–d). More interestingly, these nanosheets vertically assemble into hierarchical nanostructure in large-scale. The nanosheets are convolute spontaneously and present a large free space naturally. Fig. 2 B shows the XRD pattern of precursor B, the broad and weak peaks indicate that it is poorly crystallized. Moreover, some diffraction peaks of cubic Co 3 O 4 are also found. These results indicate the oxidation from Co (II) to Co (III) in molten hydroxides by the uptake of oxygen [30] : (2) 6 Co(OH) 2 + O 2 → 2 Co 3 O 4 + 6 H 2 O In addition, it should be pointed out that a trace of flower-like spheres can also be found in Fig. 1 c. The details of the self-assembled processes are still not clear and further works on it is underway. Fig. 1 e–f shows the SEM images of Co 3 O 4 nanostructure, which was obtained by calcining precursor B in air at 500 °C for 6 h. From it we can see that no substantial change is observed and the morphology of precursor B is preserved after the heat treatment. The thickness is estimated to be about 40 nm. Due to the thermal decomposition, the obtained Co 3 O 4 exhibits flawed nanosheet morphology. The XRD curve, as shown in Fig. 2 C, indicates that the hierarchical nanostructure consists of well-crystallized Co 3 O 4 . All the diffraction peaks can be indexed to a cubic structure of Co 3 O 4 (JCPDS No. 74-2120). Fig. 3 a shows the TEM images of Co 3 O 4 nanostructures. The SAED pattern ( Fig. 3 b) demonstrates that the Co 3 O 4 nanostructures are polycrystalline. The diffraction rings pointed out by white lines can be indexed as (1 1 1), (2 2 0), (3 1 1) and (4 4 0) planes of cubic Co 3 O 4 , respectively. HRTEM image exhibits the clear lattice fringes with a spacing of 0.467 nm, which corresponds to the (1 1 1) planes of cubic Co 3 O 4 . The surface area of the hierarchical Co 3 O 4 nanostructure is measured by Brunauer–Emmett–Teller (BET) method. The N 2 adsorption–desorption isotherms at 77 K are shown in Fig. 4 , with the insets showing the pore size distribution by Barrett–Joyner–Halenda (BJH) method. It is found that the overall hierarchical Co 3 O 4 have a BET surface area of 45.6 m 2 g −1 and a pore volume of 0.153 cm 3 g −1 . The isotherm is characteristic of a type IV with a type H3 hysteresis loop, revealing that the Co 3 O 4 sample is composed of aggregates of sheet-like particles forming slit-like pores [31] . It is well correspondence with the previous microscopy findings in Fig. 1 e–f. The electrochemical reaction processes are investigated by cyclic voltammograms. Fig. 5 a shows the CV curves of the hierarchical Co 3 O 4 at a scan rate of 0.5 mV s −1 . During the first cathodic scan, only one broad peak near 0.66 V could be observed. Compared to the initial cycle, a decrease of peak intensity and a shift of the potential to the positive direction are revealed in the subsequent cycles. This cathodic peak corresponds to a multistep electrochemical reaction, which is generally attributed to the reduction of Co (III) to Co (II) and metal Co [32] . In the anodic scans, one peak in the range of 1.9–2.5 V is recorded, which are ascribed to the reversible oxidation of metal Co to cobalt oxide. Except for the first cycle, the following CV curves are similar, which demonstrate the good cycle stability of the electrode during the discharge–charge cycles. The electrochemical reaction of Li with Co 3 O 4 can be expressed as follows [33,34] : (3) Co 3 O 4 + 8 Li + + 8e − ↔ 4 Li 2 O + 3 Co Fig. 5 b displays the discharge–charge curves of the hierarchical Co 3 O 4 nanostructure measured between 0.01 and 3.0 V at a current density of 180 mA g −1 . The discharge–charge behaviors and the curve plateaus are corresponding well with the cathodic and anodic peaks in Fig. 5 a. Since the second cycle, the curves are similar with a gradually decrease in capacity. Usually, Li-driven formation of nanoscale Co dispersed into Li 2 O matrix goes with a series of irreversible reactions during the first discharge process such as the decomposition of electrolyte and the formation of solid electrolyte interphase (SEI) films [35] . These irreversible reactions result in large initial irreversible capacity and low coulombic efficiency. In present case, the Co 3 O 4 electrode exhibits the discharge capacity of 1336 mAh g −1 and the charge capacity of 800 mAh g −1 in the first cycle. The cycle performances of the hierarchical Co 3 O 4 nanostructure prepared at different temperature are shown in Fig. 6 . The result shows that the annealed Co 3 O 4 nanostructures exhibit the similar cycle performances. However, the precursor B exhibits the poor cycle performance with obvious capacity fade. It is believed that the oxidation from Co (II) to Co (III) in molten hydroxides is a complex reaction process. The side products, such as amorphous CoOOH, Co(OH) 3 may be formed in precursor B. Hence, the thermal-treatment ensures the good phase purity of the hierarchical Co 3 O 4 nanostructures, which is significant for their electrochemical performance. Compared to other samples, the hierarchical Co 3 O 4 nanostructure annealed at 500 °C exhibits a higher discharge capacity. Moreover, the electrode reveals a slow capacity fading and achieves a stable reversible capacity above 680 mAh g −1 over 50 cycles. Motivated by the extremely thin thickness of single Co 3 O 4 nanosheet, the rate capability of the hierarchical Co 3 O 4 nanostructure obtained at 500 °C is studied and presented in Fig. 7 . The Initial charge capacities of 885 mAh g −1 , 832 mAh g −1 , 757 mAh g −1 and 680 mAh g −1 are observed at the different current densities of 140 mA g −1 , 280 mA g −1 , 560 mA g −1 and 1120 mA g −1 , respectively. The coulomb efficiency rises rapidly from 65.1% to 94.2% within five cycles. Then, it remains above 97.0% in the following cycles even at high current density. When the current density returns to 140 mA g −1 after 20 cycles, the electrode recovers its original capacity. As compared to many reported Co 3 O 4 nanoparticles, nanocubes and porous microspheres [18,33,36,37] , the hierarchical Co 3 O 4 nanostructure exhibit better electrochemical performance. The improved performance may be attributed to the unique hierarchical feature of Co 3 O 4 nanostructure. On the one hand, the large area between the Co 3 O 4 nanosheets can alleviate the influence of the volume change during lithiation/delithiation processes, which generate good capacity retention. Fig. 8 shows the SEM image of the hierarchical Co 3 O 4 nanostructures after 50 cycles. Compared with Fig. 1 f, it can be see that the morphology of Co 3 O 4 nanosheet partially remained after the lithiation/delithiation cycles. On the other hand, the primary Co 3 O 4 nanosheet, which is extremely thin in thickness, can effectively shorten the diffusion distance of Li + . Therefore, the rate capability is improved and the large specific capacities are achieved at high current densities. The enhanced cycle performance as well as the high rate capability of the obtained Co 3 O 4 nanostructure demonstrated that the synthesis of hierarchical architectures is an effective way to improve the electrochemical performance of Co 3 O 4 anode materials. 4 Conclusions In summary, novel Co 3 O 4 nanostructures with a hierarchical architecture have been prepared via self-assemble of nanosheet blocks in molten hydroxides. It is believed that the reaction mechanism includes the following processes: (1) the formation of β-Co(OH) 2 nanoplates; (2) the morphology evolution and self-assemble of nanoplates to hierarchical architecture going with the oxidation of Co(OH) 2 ; and (3) the transformation of the precursor to well crystallized Co 3 O 4 nanostructures by heat treatment. When tested as anode materials for lithium ion battery, the hierarchical Co 3 O 4 exhibited high reversible capacity, good cycle performance, and high rate capability. Acknowledgements This work was supported by National Natural Science Foundation of China ( 51002117 and 51071117 ), the National Basic Research Program of China ( 2010CB635101 ) and Fundamental Research Funds for the Central Universities ( 0109-08141012 ). References [1] H. Tuysuz M. Comotti F. Schuth Chem. Commun. 34 2008 4022 [2] C.Y. Ma Z. Mu J.J. Li Y.G. Jin J. Cheng G.Q. Lu Z.P. Hao S.Z. Qiao J. Am. Chem. Soc. 132 2010 2608 [3] B.Y. Geng F.M. Zhan C.H. Fang N. Yu J. Mater. Chem. 18 2008 4977 [4] T. Yu Y.W. Zhu X.J. Xu Z.X. Shen P. Chen C.T. Lim J.T.L. Thong C.H. Sow Adv. Mater. 17 2005 1595 [5] P. Poizot S. Laruelle S. Grugeon L. Dupont J.M. Tarascon Nature 407 2000 496 [6] Y.M. Kanga M.S. Songa J.H. Kim H.S. Kima M.S. Park J.Y. Lee H.K. Liu S.X. Dou Electrochim. Acta 50 2005 3667 [7] Y. Lu Y. Wang Y.Q. Zou Z. Jiao B. Zhao Y.Q. He M.H. Wu Electrochem. Commun. 12 2010 101 [8] Z.S. Wu W.C. Ren L. Wen L.B. Gao J.P. Zhao Z.P. Chen G.M. Zhou F. Li H.M. Cheng ACS Nano 4 2010 3187 [9] G.X. Wang X.P. Shen J.N. Yao D. Wexler J.H. Ahn Electrochem. Commun. 11 2009 546 [10] T. Zhu J.S. Chen X.W. Lou J. Mater. Chem. 20 2010 7015 [11] J.S. Chen T. Zhu Q.H. Hu J.J. Gao F.B. Su S.Z. Qiao X.W. Lou ACS Appl. Mater. Interfaces 2 2010 3628 [12] W.Y. Li L.N. Xu J. Chen Adv. Mater. 15 2005 851 [13] N. Du H. Zhang B.D. Chen J.B. Wu X.Y. Ma Z.H. Liu Y.Q. Zhang D.R. Yang X.H. Huang J.P. Tu Adv. Mater. 19 2007 4505 [14] X. Wang L.J. Yu X.L. Wu F.L. Yuan Y.G. Guo Y. Ma J.N. Yao J. Phys. Chem. C 113 2009 15553 [15] X.W. Lou D. Deng J.Y. Lee L.A. Archer J. Mater. Chem. 18 2008 4397 [16] S.L. Chou J.Z. Wang H.K. Liu S.X. Dou J. Power Sources 182 2008 359 [17] Y. Sun X.Y. Feng C.H. Chen J. Power Sources 196 2011 784 [18] B. Guo C.S. Li Z.Y. Yuan J. Phys. Chem. C 114 2010 12805 [19] Y.G. Li B. Tan Y.Y. Wu Nano Lett. 8 2008 265 [20] X. Wang X.L. Wu Y.G. Guo Y.T. Zhong X.Q. Cao Y. Ma J.N. Yao Adv. Funct. Mater. 20 2010 1680 [21] X.H. Xia J.P. Tu J.Y. Xiang X.H. Huang X.L. Wang X.B. Zhao J. Power Sources 195 2010 2014 [22] Y.B. Mao T.J. Park F. Zhang H.J. Zhou S.S. Wong Small 3 2007 1122 [23] C.G. Hu Y. Xi H. Liu Z.L. Wang J. Mater. Chem. 19 2009 858 [24] H. Liu C.G. Hu Z.L. Wang Nano Lett. 6 2006 1535 [25] C.Y. Xu L. Zhen R.S. Yang Z.L. Wang J. Am. Chem. Soc. 129 2007 15444 [26] C.G. Hu H. Liu W.T. Dong Y.Y. Zhang G. Bao C.S. Lao Z.L. Wang Adv. Mater. 19 2007 470 [27] X. Wang C.G. Hu H. Liu G.J. Du X.S. He Y. Xi Sens. Actuators B: Chem. 144 2010 220 [28] C.G. Hu Z.W. Zhang H. Liu P.X. Gao Z.L. Wang Nanotechnology 17 2006 5983 [29] X.W. Lou D. Deng J.Y. Lee J. Feng L.A. Archer Adv. Mater. 20 2008 258 [30] J.Q. Wang G.D. Du R. Zeng B. Niu Z.X. Chen Z.P. Guo S.X. Dou Electrochim. Acta 55 2010 4805 [31] C. Wang Y. Zhou M.Y. Ge X.B. Xu Z.L. Zhang J.Z. Jiang J. Am. Chem. Soc. 132 2010 46 [32] D. Larcher G. Sudant J.B. Leriche Y. Chabre J.M. Tarascon J. Electrochem. Soc. 149 2002 A234 [33] D. Barreca M. Cruz-Yusta A. Gasparotto C. Maccato J. Morales A. Pozza C. Sada L. Sanchez E. Tondello J. Phys. Chem. C 114 2010 10054 [34] L. Tian H.L. Zou J.X. Fu X.F. Yang Y. Wang H.L. Guo X.H. Fu C.L. Liang M.W. Wu P.K. Shen Q.M. Gao Adv. Funct. Mater. 20 2010 617 [35] P. Poizot S. Laruelle S. Grugeon L. Dupont J.-M. Tarascon J. Power Sources 97/98 2001 235 [36] J. Zheng J. Liu D.P. Lv Q. Kuang Z.Y. Jiang Z.X. Xie R.B. Huang L.S. Zheng J. Solid State Chem. 183 2010 600 [37] M.M. Rahman J.Z. Wang X.L. Deng Y. Li H.K. Liu Electrochim. Acta 55 2009 504