Abstract:Well-defined porous Co3O4 nanodendrites have been synthesized by a simple one-pot hydrothermal method combined with subsequent calcination. Importantly, after thermal treatment, the dendritic morphology could be completely preserved. The as-obtained superstructures are characterized by several techniques, such as powder X-ray diffraction, Fourier transform infrared spectroscopy, X-ray photoemission spectroscopy, elemental analysis, transmission electron microscopy, high-resolution TEM and magnetometry. On the dendritic hierarchical structures, a number of nanorods with different lengths and widths are connected to the main trunk with a diameter of about 50 nm and length of several micrometers. Each branch is about 0.5-1.0 mm with a width ranging from 100 to 400 nm. The possible formation mechanism was proposed on the basis of the contrasting experiments. It demonstrated that trisodium citrate and acetone play important roles in the synthesis of Co3O4 nanodendrites, while the other reaction parameters, such as reaction temperature, concentration of trisodium citrate and reaction time, have close relationships with the final morphology of the Co3O4 products. Optical properties of Co3O4 nanodendrites were characterized by Raman and UV-vis spectroscopy. Magnetic property measurement shows that Co3O4 nanodendrites have a low Neel transition temperature of 35 K. The as-prepared mesoporous Co3O4 nanostructures are expected to have great applications in many fields.

Surfactant-Assisted Growth of Novel La2(MoO4)3 Dendritic Nanostructures Via Facile Hydrothermal Processes

Low-temperature chemical solution synthesis of dendrite-like La(OH) 3 nanostructures and their thermal conversion to La 2 O 3 nanostructures

Surfactant-Free Fabrication of Catio3 Butterfly-Like Dendrite Via A Simple One-Step Hydrothermal Route

Surfactant‐Assisted Growth of Novel PbS Dendritic Nanostructures Via Facile Hydrothermal Process

Controllable growth of dendrite-like CuO nanostructures by ethylene glycol assisted hydrothermal process

Shape-Controlled Synthesis of Mnwo4 Nanocrystals by A Surfactant-Free Hydrothermal Method

Hydrothermal Synthesis and Characterization of SrTiO3 Dendrites

Controlled Construction Of Uniform Pompon-Shaped Microarchitectures Self-Assembled From Single-Crystalline Lanthanum Molybdate Nanoflakes

Electrodeposition of high aspect ratio LaPO 4 and LaPO 4 :Ln 3+ (Ln 3 + =Ce 3+ , Tb 3+ ) nanostructures

Novel three-dimensional Co3O4 dendritic superstructures: Hydrothermal synthesis, formation mechanism and magnetic properties

Controlled synthesis of SrCO3 dendrites by a simple hydrothermal method

A simple mixed surfactant route for the preparation of noble metal dendrites

Various Self-Assembled Three-Dimensional Hierarchical Architectures of La2(MoO4)3: Controlled Synthesis, Growth Mechanisms, Luminescence Properties and Adsorption Activities.

Formation Of Single-Crystal Srtio3 Dendritic Nanostructures Via A Simple Hydrothermal Method

Synthesis of Ultrafine Lanthanum Hydroxide Nanorods by A Simple Hydrothermal Process

Synthesis and Characterization of Single Crystalline Mnooh and Mno2 Nanorods by Means of the Hydrothermal Process Assisted with Ctab

Generalized Synthesis of NaLn(MoO4)2 Nano/microcrystals (ln = La–Lu and Y): the Effects of Lanthanide Contraction, Structure, and Down-/Up-conversion Luminescence

Surfactant-assisted synthesis of lanthanide phosphates single-crystalline nanowires/nanorods

Controlled Construction of Uniform Flowerlike Lanthanide Molybdate Micro-/Nano-architectures and Photoluminescence Properties

AgLa (WO 4) 2 dendritic nanostructures: template-free hydrothermal synthesis and their

Hydrothermal Synthesis of Highly Ordered Micropompon of Lanthanum Molybdate Nanoflakes