Abstract:In this paper, we present a novel approach for the synthesis of carbon microspheres via the polymerization of a high internal phase emulsion (HIPE). By using Span 80 and Tween 80 as emulsifiers, 1iquid paraffin as oil phase, and the mixture of resorcinol/formaldehyde (R/F) solution as aqueous phase, an O/W emulsion was obtained. This emulsion phase inverted to a W/O HIPE induced by ammonia which served as the polymerization catalyst. Carbon microspheres (CMs) were prepared by polymerization of the HIPE, followed by drying and carbonization. Scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Brunauer-Emmett-Teller (BET) analyzer were used to characterize as-prepared CMs. The results indicate that, in case of 0.25 wt% ammonia of the HIPE, the diameters of CMs decreased from about 2 to 1 μm when the mass fraction of aqueous R/F decreased from 0.714 to 0.357; the apparent density and the specific surface areas of the CMs, however, did not change obviously, which are about 0.6 g/cm3and 200 m2/g, respectively. The dosage of ammonia has a significant influence on the morphology and properties of CMs. With increasing of the ammonia mass to 1 wt% of the HIPE, the resultant carbon materials comprise not only CMs, but also some carbon sheets; the apparent density of which increased to 0.9 g/cm3and the specific surface areas of which decreased to below 100 m2/g. In addition, the other parameters for CMs preparation were also investigated. It was found that the proper conditions were controlling the temperature of 303-333 K and the oil/aqueous phase mass ratio of 2.5:7.

Synthesis of carbon hollow particles by a simple inverse-emulsion method

One-step Syntheses and Properties of Carbon Microspheres with Amino Groups

Formation of resorcinol-formaldehyde hollow nanoshells through a dissolution-regrowth process

Facile synthesis of hollow carbon nanospheres from hollow chitosan nanospheres.

Engineering Hollow Covalent Organic Framework Particle Through Self‐templated Crystallization

Synthesis of mesoporous silica hollow spheres in supercritical CO2/water systems

A facile and environmentally friendly method for the synthesis of hollow silica particles in a self-stable dispersion

Hollow Carbon Nanospheres Prepared by Carbonizing Polymethylmethacrylate/polyacrylonitrile Core/shell Polymer Particles

Facile Fabrication of Carbon Spheres with Tunable Morphologies from Novel Polymeric Carbon Precursors.

A Facile Soft-Template Synthesis of Mesoporous Polymeric and Carbonaceous Nanospheres

Interfacial Fabrication of Silica Hollow Particles in a Reverse Emulsion System

Porous carbon/silica composite monoliths derived from resorcinol–formaldehyde/TEOS

One-step synthesis of silica hollow particles in a W/O inverse emulsion

Phenolic Resin and Derived Carbon Hollow Spheres

Scalable preparation of hollow polymer and carbon microspheres by spray drying and their application in low-density syntactic foam

Direct Preparation of Silica Hollow Spheres in a Water in Oil Emulsion System: the Effect of Ph and Viscosity

Highly Tunable and Facile Synthesis of Uniform Carbon Flower Particles

Synthesis of size-controlled carbon microspheres from resorcinol/formaldehyde for high electrochemical performance

A Facile Approach for the Synthesis of Uniform Hollow Carbon Nanospheres

Carbon Microspheres Prepared by High Internal Phase Emulsion Polymerization

Preparation of hundred-micron carbon spheres using solvent extraction in a simple microchannel device