CTAB-assisted microemulsion synthesis of unique 3D network nanostructured polypyrrole presenting significantly diverse capacitance performances in different electrolytes
Caixia Li,Ping He,Zhen Tang,Mingqian He,Faqin Dong,Xiaojuan Zhang,Huanhuan Liu,Shuai Wang
DOI: https://doi.org/10.1007/s10854-018-9857-7
2018-01-01
Abstract:In this work, the unique 3D network nanostructured polypyrrole (PPy) has been successfully synthesized in cetyltrimethylammonium bromide/butyl alcohol/hexane/water microemulsion system. The composition, crystalline characteristic and morphology of as-prepared PPy materials are characterized by Fourier transform infrared spectrometer, X-ray diffractometer and field emission scanning electron microscope. It is shown that as-prepared PPy materials possess unique 3D network nanostructure stacked by PPy nanospheres with an average diameter of 100 nm. Furthermore, the electrochemical performances of PPy based electrodes are investigated by cyclic voltammetry, galvanostatic charge/discharge and electrochemical impedance spectrum in 1.0 M H 2 SO 4 , 1.0 M Na 2 SO 4 and 1.0 M KCl electrolytes, respectively. At a current density of 1.0 A g −1 , as-prepared PPy based electrode exhibits the highest specific capacitance (329.0 F g −1 ) in 1.0 M H 2 SO 4 electrolyte, much higher than that in 1.0 M Na 2 SO 4 (156.6 F g −1 ) or 1.0 M KCl (153.2 F g −1 ) electrolyte. However, the specific capacitance of PPy based electrode in 1.0 M H 2 SO 4 electrolyte retains only 40.6% of the initial specific capacitance after 5000 continuous charge/discharge cycles and, interestingly, 83.9% and 81.3% in 1.0 M Na 2 SO 4 and 1.0 M KCl electrolytes, respectively. It is reasonable that the process of deoxidation and reoxidation of PPy nanomaterials is accompanied by the intercalation and deintercalation of massive H 3 O + in 1.0 M H 2 SO 4 electrolyte, which might result in the collapsed structure of as-prepared PPy nanomaterials and the relative instability during the cycling process.