Abstract:Nano polycrystalline ZnSe (np-ZnSe) have been synthesized by a hydrothermal elemental direct reaction of metal Zn with Se in ethylenediamine at 180 °C for 6 h, which shows an irregular structure and is characterized with nanobelts and nanowires. A broad Raman spectrum with a strong TO phonon peak has been observed, which can be decomposed into six peaks located at ∼143 cm−1, ∼175 cm−1, ∼207 cm−1, ∼233 cm−1, ∼253 cm−1 and ∼275 cm−1, respectively, are assigned to 2 TA mode, the interaction of two-phonon with disorder, TO mode, the scattering from the simple substance Se, LO mode and the interface of ZnSe–ZnO. The A band, B band and C band from photoluminescence (PL) at 300 K are attributed to bandgap, transition from Zn interstitials to the valence band and the nano polycrystalline structure, respectively. Compared with PL at 16 K, the emissions from bandgap show blueshift with the decreasing temperature. Redshift of B bands and C bands is due to the carrier scattering with LO phonon of np-ZnSe. From PL at 16 K, the emission of ∼701 nm is attributed to the recombination from oxygen-related states. It is believed that understanding of the structures, Raman and PL properties are beneficial to the application of np-ZnSe in the optoelectronic field.

Solvothermal synthesis and characterization of ZnSe nanoplates

Synthesis of Two-Dimensional Micron-Sized Single-Crystalline ZnS Thin Nanosheets and Their Photoluminescence Properties

Controlled Synthesis and Characterization of Znse Nanostructures Via A Solvothermal Approach in A Mixed Solution

A solvothermal method to novel metastable ZnSe nanoflakes

Nano polycrystalline structured ZnSe synthesized by the hydrothermal elemental-direct-reaction method: Structures, Raman and photoluminescence properties

Preparation, Growth Mechanisms and Characterizations of ZnSe Films Via the Solvothermal Method

Synthesis and characterization of ZnSe hollow nanospheres via a hydrothermal route

Synthesis and Properties of ZnSe Precursor and ZnSe Nanoribbon Arrays on Zn Substrates

Hydrothermal synthesis of ZnSe nanoparticle

Solvothermal synthesis and characterization of CdSe nanocrystals with controllable phase and morphology

Synthesis and Characteristics of ZnSe One-Dimension Nanocrystals

Synthesis and Characterization of ZnSe:Fe/ZnSe Core/shell Nanocrystals

Solvothermal Synthesis of ZnSe Nanospheres

A Solvothermal Route to Wurtzite ZnSe Nanoparticles

Formation of Cu2−xSe(en)2 in a Solvothermal Process and Conversion to Nanocrystalline Cu2−xSe

Large-scale synthesis of ZnSe nanoribbons on zinc substrate

Synthesis and Photocatalytic Property of ZnSe Flowerlike Hierarchical Structure

Synthesis and Characterization of Wurtzite ZnSe One-Dimensional Nanocrystals Through Molecular Precursor Decomposition by Solvothermal Method

Characterization of ZnSe microspheres synthesized under different hydrothermal conditions

Preparation and characterization of ZnSe/5B2O3-95SiO2 nanocomposites

Synthesis, Optical and Photocatalytic Properties of ZnSe Microspheres/Nanosheets