CATHODIC ELECTROCHEMICAL BEHAVIORS OF MILD STEEL IN SEAWATER

Zou Yan,Zheng Yingying,Wang Yanhua,Wang Jia

DOI: https://doi.org/10.3724/sp.j.1037.2009.00374

IF: 1.797

2010-01-01

ACTA METALLURGICA SINICA

Abstract:The cathodic electrochemical behavior of A3 mild steel in seawater was studied and the roles of the formed rust layers in cathodic process were analyzed by means of electrochemical tests and XRD.The results showed that the rust formed could be classified into outer layer and inner layer.The inner layer is mainly composed ofγ-FeOOH,α-FeOOH,β-FeOOH and Fe_3O_4/γ-Fe_2O_3, while the main phases in the outer layer changed with the increase of immersion time.During the initial immersion period of 126 d,the phase isγ-FeOOH,but after about 364 d immersion,the phases areγ-FeOOH,α-FeOOH and Fe_3O_4/γ-Fe_2O_3.These rust layers play different roles in the cathodic process.Both the outer and inner rust layers can prevent the dissolved oxygen from diffusing into the steel substrate,while the inner layer could also participate in reduction reaction which accelerated the cathodic reaction.A parameterαwas induced to evaluate the participation degree of rust in the reduction reaction.The value of parameterαobviously increased during the first 7 d immersion,and almost didn't change after 168 d immersion.Changes of components in outer and inner layers were discussed and the interactions of different components were analyzed.