Effect of fluoropolymer antidripping agent on the microstructure and properties of polyesters

Xinsheng Zhu,Hansong Xu,Jianmei Lu,Juying Wang,Shunhua Zhou
DOI: https://doi.org/10.1007/s10965-007-9170-2
IF: 3.061
2008-01-01
Journal of Polymer Research
Abstract:Poly(ethylene terephthalate) (PET) is of excellent mechanical properties and melt processability and is widely used as raw material for textile fibers. However, the flame retardant properties of PET were rather poor, and both reactive and additive phosphorus- and halogen-containing compounds have been employed to enhance the reaction-to-fire properties while the meltdripping behaviour during burning hasn’t been handled properly with the flame retardants. In this work, fluoropolymer was blended with both pure PET (pPET) and reactive phosphorus-containing flame retarded copolyester (fPET), and the flame retardance and char formation and mechanical properties of the resulted pPET and fPET blends were investigated. The tensile strengths of modified pPET samples were worsen whereas those of modified fPET samples were improved at low concentrations. The initial thermal degradation in nitrogen was accelerated remarkably for the two polyesters with fluoropolymer. The oxygen indices of the all modified samples were reduced while char formation and meltdripping suppression were encouraged. The apparent melt viscosity and elasticity for the two polyesters were gained much with antidripping agent. Therefore, fluoropolymer improved char formation of the two polyesters based on the gaseous phase mechanism while the partial suppression of meltdripping behavior and the decrease of mechanical properties mainly originated from the increase of melt viscosity via fibrillation for pPET.
What problem does this paper attempt to address?