First-order Magnetization Process in Nd(Fe,M)12Zy (m=mo, Ti, V, Z=C, N)

KH Muller,D Eckert,F Fischer,A Handstein,D Hinz,R Kratz,H Krug,P Oleinek,S Siegel,P Verges,M Wolf,JB Yang

DOI: https://doi.org/10.1016/s0921-4526(00)00640-2

IF: 2.988

2001-01-01

Physica B Condensed Matter

Abstract:The magnetic properties of textured samples of Nd(Fe,M)(12)Z(y) (M = Mo, Ti, V, Z = C, N) with ThMn12-type structure have been investigated using a superconducting solenoid with fields up to 16 T and a pulsed-field solenoid with fields up to 40T. A field-induced transition in the magnetization curves of the carbide samples was detected for fields applied perpendicular to the alignment direction. This transition was identified as a first-order magnetization process (FOMP). The FOMPs depend on carbon concentration, temperature and the type of M element. They appear at a certain carbon concentration and at temperatures below 150-100 K. The FOMP held of NdFe10.5Mo1.5Cy is much higher than that of NdFe10.5V1.5C and NdFe11TiCy. Transitions found in the DC magnetization measurements up to 16 T an the carburized samples could be confirmed by the pulse-field measurements. Contrary to theoretical suggestions, no FOMP could be found in the nitrides for fields up to 40 T. The temperature dependence of the FOMPs is due to the thermal evolution of the anisotropy constants K-i (i = 1, 2, 3) of the carbides related to the corresponding crystalline-electric-field (CEF) parameters. (C) 2001 Elsevier Science B.V. All rights reserved.