Abstract:Preparation process and microstructure of CF/CNTs reinforcements and mechanical properties of their composites. Chemical vapor deposition (CVD) method was performed to grow carbon nanotubes (CNTs) on oxidized carbon fiber (CF). First, CF was oxidized by a simple and gentle way to increase the number of active groups and the optimal treatment time was determined. Then, effects of catalyst concentration and growth time on morphologies and loading amount of CNTs, the properties of CF/CNTs reinforcements, and the interlayer properties of CF/CNTs composites were explored. When the catalyst concentration and growth time were controlled at a reasonable level, CNTs can be uniformly grown on the CF surface. The interlaminar shear strength (ILSS) was characterized and the fracture surfaces of CF/CNTs composites were observed. The results demonstrated that when the catalyst precursor was kept at 0.05 mol/L and the growth time was controlled at 10 min, CNTs had the best strength effect and the ILSS increased by 30.25% compared to that of composites without CNTs. The fracture surface showed that CNTs can penetrate the matrix at the interface and enhance the interface through mechanical interlocking effect. The CNTs‐induced interphase allows the stress inside the composites to propagate continuously between resin and fibers, thereby heightening the load carrying capacity. Highlights A simple and gentle way was performed to activate CF without strength reduction. The influence mechanism of various parameters was revealed in detail. The mechanism of CNTs enhancing the interface was revealed.

In situ growth of carbon nanotubes on inorganic fibers with different surface properties

In situ growth of CNTs on carbon fiber by chemical vapor deposition

Non-destructive and controllable catalyst deposition of in situ growing carbon nanotubes onto the carbon fibre fabric

One‐step in‐situ growth of CNTs on oxidized carbon fiber: Effects of catalyst concentration and growth time on mechanical properties of carbon fiber

Substrate morphology induced self-organization into carbon nanotube arrays, ropes, and agglomerates.

Catalyst-Free in Situ Carbon Nanotube Growth in Confined Space Via High Temperature Gradient

In-situ growth of scaly carbon nanotube by Cu@Ni core-shell catalyst on continuous carbon fiber surface for multiply tenoned composite interphase

Facile growth of oriented SiC nanowires arrays on carbon fiber cloth via CVD

In situ growth of carbon nanotubes on graphene oxide fibers by thermal chemical vapor deposition

Growth of High Quality, High Density Single-Walled Carbon Nanotube Forests on Copper Foils

In situ growth of carbon nanotubes on fly ash substrates

Advanced Materials from Natural Materials: Synthesis of Aligned Carbon Nanotubes on Wollastonites.

Spatial confined growth of carbon nanotubes in pore channels of microporous ceramic supports with improved filtration efficiency

Facile manipulation of individual carbon nanotubes assisted by inorganic nanoparticles.

Direct growth of carbon nanotubes on basalt fiber for the application of electromagnetic interference shielding

Growth of Tall Vertical Carbon Nanotube Forests using Al-Fe Catalysts and Transfer to Flexible Substrates

Optimization of Electrical Intensity for Electrochemical Anodic Oxidation to Modify the Surface of Carbon Fibers and Preparation of Carbon Nanotubes/Carbon Fiber Multi-Scale Reinforcements

Carbon Nanotube As the Core of Conical Carbon Fiber: Fabrication, Characterization and Field Emission Property

Preparation of in-situ grown carbon nanotubes via dithiocarbamate in composites with excellent microstructure and mechanical performance

Selective Growth of Carbon Nanotube on Silicon Substrates

Carbon fiber-promoted activation of catalyst for efficient growth of single-walled carbon nanotubes