Abstract:One multisilicon copolymer, i.e. a copolymer containing pendent siloxane and anhydride groups is prepared from the copolymerization of maleic anhydride (MA) and methacryloxypropyl trimethoxy silane (gamma-MPS). Thereafter, it is used for the preparation of hybrid membranes through in situ sol-gel process in poly(vinyl alcohol) (PVA) solution. The anhydride groups in MA are less hydrophilic as compared with acidic carboxylic acid (-COOH) groups. Hence the copolymerization process can be more easily controlled without formation of gel. During the sol-gel process, the anhydride groups hydrolyze to generate geminal -COOH groups, which provide the membranes with relatively high cation exchange capacities (CECs) that can be applied for the diffusion dialysis process to recover NaOH from the mixture of NaOH/Na2WO4. The membranes have the initial decomposition temperature (IDT) of 227-243 degrees C, tensile strength (TS) of 14.2-28.3 MPa and elongation at break (E-b) of 18.8-67.3%. In addition, water swelling decreases as the content of multisilicon copolymer increases despite the increasing of the IEC values, which is attributed to the gradually strengthened crosslinking between PVA and the copolymer components. At 20 degrees C, U-OH (the dialysis coefficients of OH- ions) are in the range of 0.0095-0.0123 m/h, and the separation factor (S) values are in the range of 28.4-54.4. The U-OH values are significantly higher than the values of the commercial membrane (0.00137 m/h) and other polymer based hybrid membranes (0.0014-0.0022 m/h). This is due to the unique membrane structure and the presence of different functional groups. PVA provides hydrophilic matrix and hence the membranes cannot be classified into the common "three-phase" structure membranes. The presence of -OH groups assists and enhances the transport of OH- ions. (C) 2012 Elsevier B.V. All rights reserved.

Preparation of Ion Exchange Hybrid Membranes Through Crosslinking of Multisilicon Copolymers with PVA

Bionic Multisilicon Copolymers Used As Novel Cross-Linking Agents for Preparing Anion Exchange Hybrid Membranes.

PVA-based Cation Exchange Hybrid Membranes with Multifunctional Groups Prepared from Ternary Multisilicon Copolymer

Cation exchange hybrid membranes prepared from PVA and multisilicon copolymer for application in alkali recovery

Pva-Based Hybrid Membranes From Cation Exchange Multisilicon Copolymer For Alkali Recovery

Zwitterionic Multisilicon Copolymer Used for Preparing PVA Based Hybrid Membranes for Alkali Recovery

PVA/SiO 2 anion exchange hybrid membranes from multisilicon copolymers with two types of molecular weights

PVA–silica anion-exchange hybrid membranes prepared through a copolymer crosslinking agent

Preparation of cation-exchange hybrid membranes with multi-functional groups and their performance on alkali recovery

Double Cross-Linking PVA-SiO2 Hybrid Membranes for Alkali Recovery

Novel Anion-Exchange Organic–inorganic Hybrid Membranes Prepared Through Sol–gel Reaction of Multi-Alkoxy Precursors

Anion exchange hybrid membranes from PVA and multi-alkoxy silicon copolymer tailored for diffusion dialysis process

The Effects of Multi-Functional Groups from PVA and Ternary Multisilicon Copolymer on Diffusion Dialysis

Carboxylic acid type PVA-based hybrid membranes for alkali recovery using diffusion dialysis

Cation Exchange PVA/SPPO/SiO2 Membranes with Double Organic Phases for Alkali Recovery

Crosslinked Pva-Based Hybrid Membranes Containing Di-Sulfonic Acid Groups for Alkali Recovery

Hybrid anion exchange hollow fiber membranes through sol–gel process of different organic silanes within BPPO matrix

A Simple and Green Preparation of Pva-Based Cation Exchange Hybrid Membranes for Alkali Recovery

Cation exchange hybrid membranes based on PVA for alkali recovery through diffusion dialysis

Preparation of Organic–inorganic Hybrid Cation-Exchange Membranes Via Blending Method and Their Electrochemical Characterization

Novel Hollow‐fiber Anion‐exchange Hybrid Membranes: Preparation and Characterization