The Effects of La Doping on the Crystal Structure and Magnetic Properties of Ni2In-Type MnCoGe1−xLax (x = 0, 0.01, 0.03) Alloys
Yifei Bi,Wei He,Tonghan Yang,Weining Wu,Jingxian Wen,Xi Yu,Feikuo Chen
DOI: https://doi.org/10.3390/ma14143998
IF: 3.4
2021-07-16
Materials
Abstract:In this experiment, a series of MnCoGe1−xLax (x = 0, 0.01, 0.03) alloy samples were prepared using a vacuum arc melting method. The crystal structure and magnetic properties of alloys were investigated using X-ray diffraction (XRD), Rietveld method, physical property measurement system (PPMS), and vibrating sample magnetometer (VSM) analyses. The results show that all samples were of high-temperature Ni2In-type phases, belonging to space group P63/mmc (194) after 1373 K annealing. The results of Rietveld refinement revealed that the lattice constant and the volume of MnCoGe1−xLax increased along with the values of La constants. The magnetic measurement results show that the Curie temperatures (TC) of the MnCoGe1−xLax series alloys were 294, 281, and 278 K, respectively. The maximum magnetic entropy changes at 1.5T were 1.64, 1.53, and 1.56 J·kg−1·K−1, respectively. The respective refrigeration capacities (RC) were 60.68, 59.28, and 57.72J·kg−1, with a slight decrease along the series. The experimental results show that the doping of La results in decreased TC, basically unchanged magnetic entropy, and slightly decreased RC.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering