Abstract:A family of highly ordered mesoporous (20-300 Angstrom) silica structures have been synthesized by the use of commercially available nonionic alkyl poly(ethylene oxide) (PEO) oligomeric surfactants and poly(alkylene oxide) block copolymers in acid media. Periodic arrangements of mescoscopically ordered pores with cubic 1m (3) over bar m, cubic Pm (3) over bar m (or others), 3-d hexagonal (P6(3)/mmc), 2-d hexagonal (p6mm), and lamellar (L-alpha) symmetries have been prepared. Under acidic conditions at room temperature, the nonionic oligomeric surfactants frequently form cubic or 3-d hexagonal mesoporous silica structures, while the nonionic triblock copolymers tend to form hexagonal (p6mm) mesoporous silica structures. A cubic mesoporous silica structure (SBA-11) with Pm (3) over bar m diffraction symmetry has been synthesized in the presence of C16H33(OCH2CH2)(10)OH (C16EO10) surfactant species, while a 3-d hexagonal (P6(3)/mmc) mesoporous silica structure (SBA-12) results when C18EO10 is used. Surfactants with short EO segments tend to form lamellar mesostructured silica at room temperature. Hexagonal mesoporous silica structures with d(100) spacings of 64-77 Angstrom can be synthesized at 100 degrees C by using oligomeric nonionic surfactants. Highly ordered hexagonal mesoporous silica structures (SBA-15) with unusually large d(100) spacings of 104-320 A have been synthesized in the presence of triblock poly(ethylene oxide)-poly(propylene oxide)-poly(ethylene oxide) (PEO-PPO-PEO) copolymers. SBA-15 mesoporous structures have been prepared with BET surface areas of 690-1040 m(2)/g, pore sizes of 46-300 Angstrom, silica wall thicknesses of 31-64 Angstrom, and pore volumes as large as 2.5 cm(3)/g. A novel cubic (Im (3) over bar m) cage-structured mesoporous silica structure (SBA-16) with a large cell parameter (a = 176 ii) has been synthesized using triblock copolymers with large PEO segments. The EO/PO ratio of the copolymers can be used to control the formation of the silica mesophase: lowering this ratio of the triblock copolymer moieties promotes the formation of lamellar mesostructured silica, while higher ratios favor cubic mesostructured silica. Cubic mesoporous structures are also obtained when star diblock copolymers are used as structure-directing agents. The calcined ordered mesoporous silicas reported in this paper an thermally stable in boiling water for at least 48 h. The assembly of the inorganic and organic periodic composite materials appears to lake place by a hydrogen bonding (S-0 H+)(X-I+) pathway. The assembly race r increases with increasing concentration of [H+] and [Cl-], according to the kinetic expression r = k[H+](0.31)[Cl-](0.31).

Triblock-Copolymer-Directed Syntheses of Large-Pore Mesoporous Silica Fibers

Triblock Copolymer Syntheses of Mesoporous Silica with Periodic 50 to 300 Angstrom Pores

Nonionic Triblock and Star Diblock Copolymer and Oligomeric Surfactant Syntheses of Highly Ordered, Hydrothermally Stable, Mesoporous Silica Structures

Synthesis of Mesoporous Silica from Poly(Ethylene Oxide)/Polystyrene Copolymers: Influence of Block Architecture and Each Copolymer Block on Porous Size

Synthesis of Mesoporous Silica from Commercial Poly(ethylene Oxide)/poly(butylene Oxide) Copolymers: Toward the Rational Design of Ordered Mesoporous Materials

Nonionic Block Copolymer and Anionic Mixed Surfactants Directed Synthesis of Highly Ordered Mesoporous Silica with Bicontinuous Cubic Structure

Ordered Mesoporous Silicas And Carbons With Large Accessible Pores Templated From Amphiphilic Diblock Copolymer Poly(Ethylene Oxide)-B-Polystyrene

Synthesis of mesoporous silica hollow spheres in supercritical CO2/water systems

Synthesis of siliceous hollow spheres with large mesopore wall structure by supercritical CO2-in-water interface templating.

Syntheses of High-Quality Mesoporous Materials Directed by Blends of Nonionic Amphiphiles under Nonaqueous Conditions

Continuous Mesoporous Silica Films with Highly Ordered Large Pore Structures

Triconstituent Co-Assembly to Ordered Mesostructured Polymer-Silica and Carbon-Silica Nanocomposites and Large-Pore Mesoporous Carbons with High Surface Areas.

Anionic Surfactant Induced Mesophase Transformation to Synthesize Highly Ordered Large-Pore Mesoporous Silica Structures

Highly Ordered Large Caged Cubic Mesoporous Silica Structures Templated by Triblock PEO–PBO–PEO Copolymer

Highly efficient synthesis of ordered mesoporous silica materials with controllable microporosity using surfactant mixtures as templates

Highly ordered mesoporous silica structures templated by poly(butylene oxide) segment di- and tri-block copolymers

Triblock Copolymer and Poly(Ethylene Glycol) As Templates for Monolithic Silica Material with Bimodal Pore Structure

A “teardown” method to create large mesotunnels on the pore walls of ordered mesoporous silica

Nonionic Block Copolymer Synthesis of Large-Pore Cubic Mesoporous Single Crystals by Use of Inorganic Salts

Synthesis of Ordered Cubic Periodic Mesoporous Organosilicas with Ultra-Large Pores

Design of Amphiphilic ABC Triblock Copolymer for Templating Synthesis of Large-Pore Ordered Mesoporous Carbons with Tunable Pore Wall Thickness