Study on Preparation and Corrosion Resistance of Micro-Arc Oxidation Coating on ZE10 Magnesium Alloy

BIN Yuan-hong,LIU Ying,LI Wei,ZHENG Yang

2011-01-01

Abstract:A micro-arc oxidation(MAO) coating was successfully prepared on ZE10 alloy by micro-arc oxidation in a bath containing sodium silicate 14 g/L,sodium fluoride 14 g/L,sodium hydroxide 2 g/L,and glycerin 5 mL/L.The effects of voltage and oxidation time on the thickness,morphology and corrosion resistance of the micro-arc oxidation coating were studied by using eddy current coating thickness gauge,scanning electron microscopy,X-ray diffraction and electrochemical workstation.The results indicated that the MAO coating is composed of MgO,MgF2,Mg2SiO4 and a small amount of amorphous compounds.The thickness of MAO coating is increased with increasing anodic voltage and increased obviously with increasing oxidation time at the beginning,and then basically becomes stable after 20 min.The corrosion resistance of MAO coating is increased firstly,and then decreased with increasing applied voltage and time.The duty ratio and frequency also affect the corrosion resistance of MAO coating.