Abstract:A novel layered zirconium phosphate crystal with organic di-protonated 1,6-hexyldiamine (HDA) cation, 0.5 [Zr(PO 4)(HPO 4)]·1 5H 2O (abbreviated to γ-(HDA)ZrP), was synthesized under hydrothermal conditions and characterized by single-crystal and powder XRD, IR and TG-DTA. The crystal is in orthorhombic space group Imm2 with a= 3 433?8 nm, b= 0 533?8 nm, c= 0 662?0 nm, V= 1 213?42 nm3, Z=2, R= 0 055?4 and R W= 0 075?4. The title compound was of γ-type layered structure which was formed by corner-sharing ZrO 6 octahedron and PO 4, PO 3(OH) tetrahedron units, and the layer-to-layer distance was about 1 77 nm. The HDA molecule, which was perpendicular to the zirconium phosphate layer and bent a little like a bow, supported and connected the zirconium phosphate layer by the hydrogen bonds between the two end nitrogen atoms of HDA molecule and one of the two oxygen atoms stretching out of the zirconium phosphate layers. The water molecules occupied two positions between the layers. One was the cavities formed by HPO 2- 4 tetrahedrons on the surface of the zirconium phosphate layer, and the other was amid HDA molecules with four water molecules in one group. The XRD pattern simulated from the single crystal structure analysis result was in accordance with that collected from the powder sample synthesized. The absorption bands of organic amine and water appeared in the IR spectrum of γ-(HDA)ZrP, corroborated the crystal structure determined by XRD analysis. On heating, one and a half water molecules were lost at 180 ℃ and the HDA began to decompose at 250 ℃. After getting rid of the water molecules by heating at 220 ℃ for 3 h, no obvious change in the crystal structure was observed.

Hydrothermal Synthesis and Characterization of Two Organically Templated Trivalent Metal-Containing Zirconium Phosphates

Ionothermal Synthesis and Characterization of Crystalline Zirconium Phosphate from Oxalic Acid/Tetrapropyl Ammonium Bromide System

Synthesis, Characterization and Crystal Structure Analysis of an Open-Framework Zirconium Phosphate

Hydrothermal Synthesis and Thermal Stability Oflayered Compound of Tetravalent Metal Phosphate

Synthesis, Structure, and Characterization of Two Photoluminescent Zirconium Phosphate-Quinoline Compounds

Solvothermal Synthesis and Characterization of the Layered Compound of Α-Zirconium Hydrophosphate

Hydrothermal Synthesis and Structural Characterization of Two Organically Templated Zincophosphites with Three-Dimensional Frameworks, (c6h14n2)·[zn3(hpo3)4] and (C4h12n2)·[zn3(hpo3)4]

Hydrothermal Synthesis and Characterization of Organically Templated Zincophosphites with Two- and Three-Dimensional Structures, [ch3ch(nh3)ch2nh3]·[zn2(hpo3)3]·h2o and [H3n(ch2)6nh3]·[zn3(hpo3)4]

Synthesis of Highly Ordered Thermally Stable Cubic Mesostructured Zirconium Oxophosphate Templated by Tri-Headgroup Quaternary Ammonium Surfactants

Hydrothermal Synthesis and Structural Characterization of Novel Organically Templated Zincophosphites: [c6h4(ch2nh3)2]·[zn3(hpo3)4] and [Ch3ch2ch2nh3]2·[zn3(hpo3)4]

Hydrothermal Synthesis and Structural Characterization of Two New Three-Dimensional Oxyfluorinated Titanium PhosphatesTi4(HPO4)2(PO4)4F2·C4N2H12·H2O and Ti4(HPO4)2(PO4)4F2·C2N2H10·H2O

Ionothermal synthesis of zirconium phosphates and their catalytic behavior in the selective oxidation of cyclohexane.

Synthesis, Structure and Characterization of ZrPOF-DEA, a Microporous Zirconium Phosphate Framework Material

Hydrothermal Synthesis and Structural Characterization of Organically Templated Zincophosphites: [c6h22n4]0.5⋅[zn2(hpo3)3] and [C3n2h5]⋅[zn1.5(hpo3)2]

Hydrothermal Synthesis and Characterization of Phosphor Doped Tetragonal Zirconia Nanocrystallites

Ionothermal Synthesis, Structure and Characterization of Three-Dimensional Zinc Phosphates.

Microwave-Assisted Synthesis of A Thermally Stable Zn-Containing Aluminophosphate with Eri-Zeotype Structure Templated by Diquaternary Alkylammonium

Synthesis and Characterization of A New-Type of Zirconium-Phosphate Crystal from Alcohol System

Hydrothermal Synthesis and Structural Characterization of Organically Templated Zincophosphites: [C6H22N4]0.5× [Zn2(HPO3)3] and [C3N2H5]× [Zn1.5(HPO3)2].

Studies on Synthesis and Properties of Layered Zirconium Phosphate

Synthesis and Characterization of Layered Zirconium Phosphate Crystal with 1,6-Hexyldiamine As Template