Abstract:By using pulse-microwave assisted chemical reduction, we prepared a Pt-Ni alloy supported on a cobalt-polypyrrole-carbon (Co-Ppy-C) catalyst. The catalyst microstructure and morphology were characterized by using transmission electron microscopy (TEM) and X-ray diffraction (XRD). The electrocatalytic performance and durability of the catalysts were measured with cyclic voltammetry (CV) and linear sweep voltammetry (LSV). The metal particles were well dispersed on the carbon support, and the particle size of PtNi/Co-PPy-C was about 1.77 nm. XRD showed that the Pt(111) diffraction peak was strongest, so the most of the Pt in the catalysts was in a face-centered cubic lattice. The electrochemical surface area (ECSA) of PtNi/Co-PPy-C (72.5 m(2).g(-1)) was higher than that of Pt/C(JM) (56.9 m(2).g(-1)). After an accelerated durability test for 5000 cycles, the particle size of PtNi/Co-PPy-C obviously increased. The degradation rate of ECSA and the mass activity (MA) of PtNi/Co-PPY-C were 38.2% and 63.9%, respectively. We applied the PtNi/Co-PPy-C catalyst after optimizing the membrane electrode assembly (MEA) with an area of 50 cm(2). The fuel cell could be suitably operated at 70 degrees C with a back pressure of 50 kPa. At these conditions, the maximum power density of MEA by PtNi/Co-PPy-C was 523 mW.cm(-2). The excellent performance of PtNi/Co-PPy-C makes it a promising catalyst for proton exchange membrane fuel cells (PEMFCs).

Investigation of PtNi/C anode electrocatalysts for direct borohydride fuel cell

Highly Active Nanoporous Pt-based Alloy As Anode and Cathode Catalyst for Direct Methanol Fuel Cells

Electrocatalysts for the Anodic Oxidation of Borohydrides

Anodic Oxidation of Alkali Borohydrides Catalyzed by Nickel

Carbon Supported Silver Nanowires with Enhanced Catalytic Activity and Stability Used As A Cathode in A Direct Borohydride Fuel Cell

An Effective Pd@Ni-B/C Anode Catalyst for Electro-Oxidation of Formic Acid

Hydrogen storage alloys as the anode materials of the direct borohydride fuel cell

Anode catalyst AuNi/C for direct sodium borohydride fuel cell

Investigation of Carbon-Supported Ni@Ag Core-Shell Nanoparticles As Electrocatalyst for Electrooxidation of Sodium Borohydride

From rotating disk electrode to single cell: Exploration of PtNi/C octahedral nanocrystal as practical proton exchange membrane fuel cell cathode catalyst

A new application of nickel-boron amorphous alloy nanoparticles: anode-catalyzed direct borohydride fuel cell

Pd Modified Mmni50.6co10.2mn5.4al1.2 Alloy As The Catalyst Of Nabh4 Electrooxidation

Preparation and Application of Pt-Ni Catalysts Supported on Cobalt-Polypyrrole-Carbon for Fuel Cells

Porous Ni–Cu Alloy Dendrite Anode Catalysts with High Activity and Selectivity for Direct Borohydride Fuel Cells

Evaluation of Co–Au Bimetallic Nanoparticles As Anode Electrocatalyst for Direct Borohydride-Hydrogen Peroxide Fuel Cell

Boosting borohydride oxidation kinetics by manipulating hydrogen evolution and oxidation through octahedral Pt–Ni/C for high-performance direct borohydride fuel cells

Amorphous NiB Alloy Decorated by Cu As the Anode Catalyst for a Direct Borohydride Fuel Cell

Carbon Supported Cu-Pd Nanoparticles As Anode Catalyst For Direct Borohydride-Hydrogen Peroxide Fuel Cells

An Efficient NiFe Binary Alloy Anode Catalyst for Direct Borohydride Fuel Cells

Efficient Nickel Catalyst with Preferred Orientation and Microsphere for Direct Borohydride Fuel Cell

Lattice Strain Controlled Ni@NiCu Efficient Anode Catalysts for Direct Borohydride Fuel Cells