Efficient abatement of NOx emitted from automotive engines via adsorption on the Ba-CMK-3 adsorbents
Runping Wu,Qing Ye,Kai Wu,Hongxing Dai
DOI: https://doi.org/10.1007/s11356-020-12077-0
IF: 5.8
2021-01-07
Environmental Science and Pollution Research
Abstract:The Ba-CMK-3(<i>x</i>) (<i>x</i> was the Ba(NO<sub>3</sub>)<sub>2</sub>:CMK-3 mass ratio and equals to 5, 10, and 15 wt%) samples were prepared by the incipient impregnation method, which were used for the adsorption of NO + O<sub>2</sub> at room temperature. The samples were characterized by the XRD, BET, TEM, TPD, TG, and DRIFTS techniques. The results showed that the CMK-3 and Ba-CMK-3(<i>x</i>) samples possessed an ordered two-dimensional hexagonal mesoporous structure, and Ba was uniformly dispersed on the surface of CMK-3. After Ba doping, the surface areas and pore size distributions of the Ba-CMK-3(<i>x</i>) samples were altered due to the synergistic effect of partial blocking of the channels by Ba and partial etching of the carbon materials by O<sub>2</sub> produced from Ba(NO<sub>2</sub>)<sub>3</sub> decomposition at high temperatures. The sequence in NO adsorption capacity was Ba-CMK-3(10) (108.1 ± 0.55 mg/g) > Ba-CMK-3(15) (106.2 ± 0.72 mg/g) > Ba-CMK-3(5) (102.3 ± 1.33 mg/g) > CMK-3(88.8 ± 1.15 mg/g), with the Ba-CMK-3(10) sample showing the best (NO + O<sub>2</sub>) adsorption performance. We proposed the two main adsorption pathways in the process of NO adsorption: (i) NO reacted with O<sub>2</sub> to form NO<sub>2</sub>, part of NO<sub>2</sub> were weakly adsorbed on the surface hydroxyl groups, part of NO<sub>2</sub> were adsorbed to form the nitrite and nitrate species, and the left NO<sub>2</sub> was disproportionated to the NO, NO<sub>2</sub><sup>−</sup>, and NO<sub>3</sub><sup>−</sup> species; and (ii) NO was directly oxidized to the NO<sub>2</sub><sup>−</sup> species by the oxygen-containing functional groups in carbon, and then some of the NO<sub>2</sub><sup>−</sup> species were transformed to the NO<sub>3</sub><sup>−</sup> species directly or via disproportionation. The regeneration efficiencies of the Ba-CMK-3(<i>x</i>) samples were slightly inferior to that of the CMK-3 sample.
environmental sciences