Abstract:Inspired by a Chinese cultural relic known as Plain Gauze Gown, this work develops a fibrous structure consisting of two layers of porous fibers aligned in warp and weft directions by electrospinning. A unique Cassie–Baxter‐"restoring" wetting contributing to a stable Cassie–Baxter state is unveiled. Remarkably, the developed structure is not only superhydrophobic, but also breathable, waterproof, and semi‐transparent. Electrospun fibrous structures can be developed superhydrophobic while remaining breathable. However, current electrospinning‐based methods for developing superhydrophobicity require complex fabrication processes and multiple raw materials, lacking a facile approach to superhydrophobicity using electrospun fibers. Inspired by a cultural relic known as Plain Gauze Gown, a fibrous structure consisting two layers of porous fibers aligned in warp and weft directions by simple electrospinning is developed. Through investigation of wetting behavior, an unique Cassie–Baxter‐"restoring" (CaRe) wetting contributing to a stable Cassie–Baxter state is unveiled in the developed structure. The CaRe wetting ensures that droplet stays on the upper‐layer fibers even at a sparse inter‐fiber distance, enabling strategically reaching superhydrophobicity by lowering structure solidity. Remarkably, the developed structure with water contact angle between 159° and 162° and roll‐off angle from 10° to 3° has a water vapor transmission rate of 20.8 kg m−2 d−1, which is the highest value among all superhydrophobic electrospun structures reported, and it is also waterproof and semi‐transparent. These features make the structure suitable for a wide range of applications, including developing waterproof, breathable, and superhydrophobic membrane with simple preparation and low cost, and as a surface layer for wearable electronics that facilitates sweat evaporation and prevents water intrusion.

Superhydrophobic Electrospun Poss-Pmma Copolymer Fibres With Highly Ordered Nanofibrillar And Surface Structures

The Preparation and Characterization of PMMA/POSS-OH Hybrid Fiber

Mesoporous Silica Fibers Prepared by Electroblowing of A Poly(Methyl Methacrylate)/Tetraethoxysilane Mixture in N,N-Dimethylformamide

Nonaligned carbon nanotubes partially embedded in polymer matrixes: a novel route to superhydrophobic conductive surfaces.

Poly(Methyl Methacrylate)/Silica Nanocomposite Fibers by Electrospinning

Synergistic effect of electric field and polymer structures acting on fabricating beads-free robust superhydrophobic electrospun fibers

Biomimetic Nanofiber Patterns with Controlled Wettability

Hybrid nanofibrous mats with remarkable solvent and temperature resistance produced by electrospinning technique

The enhanced encapsulation capacity of polyhedral oligomeric silsesquioxane-based copolymers for the fabrication of electrospun core/shell fibers

Novel fluoroalkyl polyhedral oligomeric silsesquioxane (FPOSS) macromers for fabricating diblock copolymer as self-cleaning coatings

Nanoporous Structured Submicrometer Carbon Fibers Prepared Via Solution Electrospinning of Polymer Blends.

A Facile and Strategic Approach to Superhydrophobic Fibrous Structure with Biaxially Aligned Electrospun Porous Fibers

Fabrication of Liquid Crystalline Polyurethane/Polyhedral Oligomeric Silsesquioxane Nanofibers via Electrospinning

Preparation of SiO2/PS superhydrophobic fibers with bionic controllable micro–nano structure via centrifugal spinning

Fabrication of Continuous Aligned Polyvinylpyrrolidone Fibers Via Electrospinning by Elimination of the Jet Bending Instability

Fabrication of biomimetic superhydrophobic surfaces inspired by lotus leaf and silver ragwort leaf.

Fabrication and Property Optimization of Electrostatic Spinning PVDF/PDMS Waterproof and Moisture Permeable Membrane

Supramolecular Polymer Nanofibers Via Electrospinning of a Heteroditopic Monomer.

Preparation of bead-free pmda-oda polyimide nanofiber fabrics from electro-spinning

PDMS-Based Hierarchical Superhydrophobic Fabric Coating Fabricated by Thermal Treatment and Electrostatic Flocking Technology

From Trans to Cis Conformation: Further Understanding the Surface Properties of Poly(m-phenylene isophthalamide)