Influence of Lanthanum Chloride on the Osteogenesis of Dog Tissue Engineering Bone

王小平,易敏,林娟,刘海江,周曾同,张秀丽,余优成
DOI: https://doi.org/10.3969/j.issn.1674-1366.2008.04.002
2008-01-01
Abstract:Objective To observe the effects of lanthanum chloride(La3+) on the osteogenesis of tissue-engineering bone implanted into the autologous bony defects in dog jaws. Methods Bone marrow stromal cells(BMSCs) from femoral bone marrow of 9 dogs were separated by density gradient centrifugation, cultured in vitro and induced to be osteoblast. The third generation BMSCs were interfered with La3+ of 5.564 μg/ml and combined with the pig freeze-dried demineralize bone matrix(fdDBM), incubated in vitro for 7 days and then grafted into the autologous bony defects (2 cm × 1 cm × 0.8 cm) of dog jaws. BMSCs-fdDBM, unseeded fdDBM and empty defects served as control groups. At 3 and 6 monthes after operation,the dogs were sacrificed and the implanted site of the jaws were harvested. The specimens were processed for morphological observation and radiographic bone-density analysis. The data was analyzed by SAS 6.12 software for ANOVA. Results New osteoid structure could be observed through histological exam of all the specimen of all groups. The density values of new bone in the implanting area treated with La3+ was higher but there was no obvious statistic significance as compared with that of the control groups. 6 monthes later, the density values of new bone in BMSCs-fdDBM group and fdDBM group had no obvious difference (P > 0.05) but were significantly higher than that of empty control groups(P < 0.05). Conclusion La3+ at the concentation of 5.564 μg/ml has no obvious negative effect on osteogenesis of tissue engineering bone.
What problem does this paper attempt to address?