Abstract:In the past few decades, lithium hexafluorophosphate (LiPF6) is the most widely employed ionic component in organic electrolyte solutions for commercial lithium ion battery, which is manufactured using PCl5, LiF and HF as raw materials via the HF solvent method in the large scale production, and then it commonly contains LiF and LiCl impurities besides water and acid. However, the influence of LiF and LiCl on the performance of lithium ion battery is still not clear. Thus, in this paper, the influence of LiF and LiCl on the electrochemical performance of graphite electrode was investigated using charge-discharge test and cyclic voltammetry (CV) combining with scanning electron microscope (SEM) and electrochemical impedance spectrum (EIS). Charge-discharge test results showed that the electrochemical performance of graphite electrode such as reversible capacity and cycling stability were significantly improved in 1 mol/L LiPF6-EC:DEC:DMC electrolyte with the saturation of LiF. The initial charge capacity of graphite electrode in 1 mol/L LiPF6-EC:DEC:DMC electrolyte with the saturation of LiF is 331.0 mAh/g, which is higher than that in 1 mol/L LiPF6-EC:DEC:DMC electrolyte (307.9 mAh/g). After 65 charge-discharge cycles, the charge capacity of graphite electrode in 1 mol/L LiPF6-EC:DEC:DMC electrolyte with the saturation of LiF is 340.1 mAh/g, which is also higher than that in 1 mol/L LiPF6-EC:DEC:DMC electrolyte (297.0 mAh/g). However, although the first charging capacity of graphite electrode was enhanced in 1 mol/L LiPF6-EC:DEC:DMC electrolyte with the saturation of LiCl, the charge-discharge cycling stability was serious deteriorated. The initial charge capacity of graphite electrode in 1 mol/L LiPF6-EC:DEC:DMC electrolyte with the saturation of LiCl is 334.2 mAh/g, yet after 65 charge-discharge cycles, the charge capacity of graphite electrode in 1 mol/L LiPF6-EC:DEC:DMC electrolyte with the saturation of LiCl is 251.2 mAh/g. CV results showed that the influence of LiF and LiCl on the decomposition process of EC in electrolyte is small. SEM and EIS results stated that the SEI film which was formed on the graphite electrode is thinner and has a smaller resistance in 1 mol/L LiPF6-EC:DEC:DMC electrolyte with the saturation of LiF than that in 1 mol/L LiPF6-EC:DEC:DMC electrolyte. Thus the reversible cycle capacity of graphite electrode was increased and its cycle stability was improved. Nevertheless the SEI film which was formed on the graphite electrode is thicker and its resistance is higher in 1 mol/L LiPF6-EC:DEC:DMC electrolyte with the saturation of LiCl than that in 1 mol/L LiPF6-EC:DEC:DMC electrolyte, which leads to the deterioration of electrochemical performance of graphite electrode.

Electrochemical Properties of Natural Graphite Fluorinated by ClF[sub 3] and NF[sub 3] in Propylene Carbonate-Containing Solvent

Surface Structure and Electrochemical Characteristics of Natural Graphite Fluorinated by ClF3

Surface Fluorination and Electrochemical Behavior of Petroleum Cokes Graphitized at Medium and High Temperatures for Secondary Lithium Battery

Efficient Exfoliation of Graphite in Chloroform with a Pyrene-Containing Hyperbranched Polyethylene As Stabilizer to Render Pyrene-Functionalized High-Quality Graphene

Understanding the Improved Fast Charging Performance of Graphite Anodes with a Fluoroethylene Carbonate Additive by In Situ NMR and EPR

Enhanced thermal properties of the solid electrolyte interphase formed on graphite in an electrolyte with fluoroethylene carbonate

Evolutionary Chlorination of Graphene: from Charge-Transfer Complex to Covalent Bonding and Nonbonding

Influence of Electrochemical Performance of Lithium Ion Batteries with the Adding of Lif and Licl

Direct Synthesis of Fluorinated Carbon Materials via a Solid‐State Mechanochemical Reaction Between Graphite and PTFE

Electrolytic Conversion of Natural Graphite into Carbon Nanostructures with Enhanced Electrical Conductivity and Na-Storage Performance

Surface Structure and Electrochemical Properties of Surface-Fluorinated Petroleum Cokes for Lithium Ion Battery

Effects of propylene carbonate content in CsPF6-containing electrolytes on the enhanced performances of graphite electrode for lithium-ion batteries

Interplay among Hexafluorophosphate, Difluoro(oxalato)borate Anions and Ethylene Carbonate during Their Insertion into a Graphite Electrode

Quantification of the Carbon-Coating Effect on the Interfacial Behavior of Graphite Single Particles

The feasibility for natural graphite to replace artificial graphite in organic electrolyte with different film-forming additives

Hexafluorophosphate anion intercalation into graphite electrode from sulfolane/ethylmethyl carbonate solutions

Interface engineering with fluorine-doped amorphous carbon thin film coating on graphite anodes compatible with non-flammable sulfone-based electrolyte

Contact‐Electro‐Catalysis for Organic Pollutants Degradation Based on 2D Fluorinated Graphite

Enhancing electrochemical performance of fluorinated graphite by polydopamine−derived nitrogen−doped carbon coating

Simultaneous fluorination and purification of natural block coaly graphite into fluorinated graphene with tunable fluorination degree

Effect of Carbon Coating on Electrochemical Performance of Treated Natural Graphite as Lithium-Ion Battery Anode Material