Abstract:This work reports a new technique for scalable and low-temperature processing of nanostructured TiO2 thin films, allowing for practical manufacturing of TiO2-based devices such as perovskite solar cells at low-temperature or on flexible substrates. Dual layers of dense and mesoporous TiO2/graphitic oxide nanocomposite films are synthesized simultaneously using inkjet printing and pulsed photonic irradiation. Investigation of process parameters including precursor concentration (10-20 wt%) and exposure fluence (4.5-8.5 J cm-2) reveals control over crystalline quality, graphitic oxide phase, film thickness, dendrite density, and optical properties. Raman spectroscopy shows the E g peak, characteristic of anatase phase titania, increases in intensity with higher photonic irradiation fluence, suggesting increased crystallinity through higher fluence processing. Film thickness and dendrite density is shown to increase with precursor concentration in the printed ink. The dense base layer thickness was controlled between 20 and 80 nm. The refractive index of the films is determined by ellipsometry to be 1.92 ± 0.08 at 650 nm. Films exhibit an energy weighted optical transparency of 91.1%, in comparison to 91.3% of a thermally processed film, when in situ carbon materials were removed. Transmission and diffuse reflectance are used to determine optical band gaps of the films ranging from 2.98 to 3.38 eV in accordance with the photonic irradiation fluence and suggests tunability of TiO2 phase composition. The sheet resistance of the synthesized films is measured to be 14.54 ± 1.11 Ω/□ and 28.90 ± 2.24 Ω/□ for films as-processed and after carbon removal, respectively, which is comparable to high temperature processed TiO2 thin films. The studied electrical and optical properties of the light processed films show comparable results to traditionally processed TiO2 while offering the distinct advantages of scalable manufacturing, low-temperature processing, simultaneous bilayer fabrication, and in situ formation of removable carbon nanocomposites.

Room-temperature preparation of crystalline TiO2 thin films and their applications in polymer/TiO2 hybrid optoelectronic devices

Low-Temperature Preparation of Ag-TiO2 Composite Films and Their Properties

Study on Structural, Optical and Hydrophilic Properties of FTO/TiO2 Tandem Thin Film Prepared by Aerosol-Assisted Chemical Vapor Deposition Method

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Growth of Nanocrystalline Tio2 Films by Pulsed-Laser-Induced Liquid-Deposition Method and Preliminary Applications for Dye-Sensitized Solar Cells

TiO2 films prepared by DC reactive magnetron sputtering at room temperature: Phase control and photocatalytic properties

Enhanced Electrochromic Properties of Donor–acceptor Polymers Via TiO2 Composite

Low-temperature sol-gel synthesized TiO2 with different titanium tetraisopropoxide (TTIP) molarity for flexible emerging solar cell

Low‐Temperature in Situ Amino Functionalization of TiO2 Nanoparticles Sharpens Electron Management Achieving over 21% Efficient Planar Perovskite Solar Cells

Room-temperature preparation and formation mechanism of porous anatase TiO2 film

Conformal TiO2 Aerogel-Like Films by Plasma Deposition: from Omniphobic Antireflective Coatings to Perovskite Solar Cell Photoelectrodes

Pulsed photoinitiated fabrication of inkjet printed titanium dioxide/reduced graphene oxide nanocomposite thin films

Conformal TiO$_2$ aerogel-like films by plasma deposition: from omniphobic antireflective coatings to perovskite solar cells photoelectrodes

Room Temperature Synthesis of Rutile TiO_2 and Its Application in Dye-Sensitized Solar Cells

TEM Analysis of Photocatalytic TiO2 Thin Films Deposited on Polymer Substrates by Low-Temperature ICP-PECVD

Nanoscale Morphology Control of Polymer/Tio2 Nanocrystal Hybrids: Photophysics, Charge Generation, Charge Transport, and Photovoltaic Properties

A Simple and Efficient Method Using Polymer Dispersion to Prepare Controllable Nanoporous TiO2 Anodes for Dye-Sensitized Solar Cells

Highly Crystallized Mesoporous Tio2 Films and Their Applications in Dye Sensitized Solar Cells

Highly Efficient Ultraviolet Photodetectors Based on TiO2nanocrystal–polymer Composites Via Wet Processing

Nanostructured TiO 2 thin films sputtered at room temperature as electron transport layer for flexible perovskite solar cell applications: Impact of varying RF power

Room-temperature processed TiO2 to construct composite electron transport layers for efficient planar perovskite solar cells