Effect of various Ni plating layers and aging on microstructure and shear strength of Sn–2.5Ag–2.0Ni solder joint

Mao Wu,Xinbo He,Rafi-ud-din,Shubin Ren,Mingli Qin,Xuanhui Qu

DOI: https://doi.org/10.1016/j.surfcoat.2009.03.014

IF: 4.865

2009-01-01

Surface and Coatings Technology

Abstract:Sn–2.5Ag–2.0Ni alloy is used to solder silicon carbide reinforced aluminum matrix (SiCp/Al) composites substrate with various Ni coatings. An experimental study is carried out to assess the effects of various Ni coatings on the microstructure and reliability of solder joint. Three electroless Ni layers, including Ni–5 wt.%P, Ni–10 wt.%P and Ni–B, are investigated. The electroless Ni–B layer is found to have good wettability with solder and gives the lowest growth rate of Ni3Sn4 IMCs during aging. The formation of Ni2SnP, which significantly affects the reliability of solder joints, is suppressed by using the low P content Ni–5 wt.%P layer. The electroless Ni–B layer has given the highest shear strength of solder joint while Ni–5 wt.%P layer yields the higher shear strength as compared to Ni–10 wt.%P layer. Growth of Ni3Sn4 IMCs and formation of crack are observed to be the major sources of failure for the solder joint with Ni–5 wt.%P, whereas, the failure of Ni–10 wt.%P solder joint is accounted for the formation of Ni2SnP, P-rich Ni layer and Kirkendall voids after long term aging.