Grain Boundary Energy of Twisted MgO Bicrystals on (100)
Eiichi Yasuda,Shiushichi Kimura,Minji Sakaki,Hyo Joon Kim,Yusuke Moriyoshi
DOI: https://doi.org/10.1007/978-1-4613-1933-7_23
1987-01-01
Abstract:In ceramic materials the boundaries between grains have a profound effect on many mechanical, chemical, and electrical properties, such as fracture strength, high-temperature creep, diffusion and electric conductivity, etc. However, their characterization has not been clarified yet because they are liable to be affected by the concentration or the precipitation of impurities at the grain boundaries. In general, the structures and properties of grain boundaries depend on the adjacent two crystals consisting of boundaries, and it is clear in metals that grain boundaries can be regarded as the region where atomic arrangement is disordered compared to that of the lattice in the grains. Therefore, atoms in the boundary region may relax their positions to minimize the total energy.1–3 Models for tilt boundaries have been proposed by Read-Shockley,4 R.W. Balluffi et al.,3 and many others. The structure of low-angle tilt boundaries has been confirmed to be an array of edge dislocations. The structure of high-angle tilt boundaries, because of the dislocation core overlapping, cannot be explained by the dislocation arrays. In the case of twist boundaries energy minima existing in the boundaries can be interpreted in terms of the coincidence site lattice (CSL) theory.5–9 Hitherto, for most studies on grain boundaries, polycrystalline materials or two pieces (bicrystals) cut from their blocks have often been used as specimens.