The Interface Magnetization of Ultrafine Ni Particles Coated by NiO and Ni/NiO Multilayers

WN Wang,GX Cheng,YW Du

DOI: https://doi.org/10.1016/0304-8853(95)00535-8

IF: 3.097

1996-01-01

Journal of Magnetism and Magnetic Materials

Abstract:Ultrafine Ni particles (Ni-UFPs) have been prepared by the gas condensation method. The surfaces of these particles were oxidized to form a layer of NiO. Ni/NiO multilayers (Ni/NiO-MLs), with a period of about 100 Angstrom, were produced by the Ar+ beam sputtering method. The magnetic properties of the MLs and UFPs were measured by means of an extracting sample magnetometer. For both UFPs and MLs, the experimental M-T curves (1.5 K < T < 300 K under H = 40 kOe) obey Bloch's law (T-3/2 relation), except for an extra enhancement at low temperatures. An irreversible magnetization from ZFC to FC was found in NiO-coated Ni-UFPs, which is attributed to surface (or interface) spin-pinning. The magnetization approach to saturation was measured at 1.5 K. The experimental M-H data were fitted to the empirical law of approach to magnetic saturation by the least-squares method. The results suggest that there is a great number of disorder-like spin structures at the interfaces of both NiO-coated Ni-UFPs and Ni/NiO-MLs.