Optimizing the aggregate structure and charge carrier transport performance of D‐A conjugated polymer films using nonpolar solvents
Yun Bai,Changhui Liu,Chunwei Xu,Yunyun Yang,Zhibang Shen,Yu Chen,Hao Zhou
DOI: https://doi.org/10.1002/pol.20240562
IF: 3.046
2024-10-12
Journal of Polymer Science
Abstract:Solution‐processed conjugated polymers have been widely used in the fields of electronic skin, wearable devices, and organic optoelectronic devices, due to their excellent optoelectronic properties, flexibility, and low cost. The aggregate structure of conjugated polymers determines the efficiency of charge carrier transport, thereby affecting the optoelectronic performance of the devices. In this work, we regulated the crystalline behavior and aggregated state structure of D‐A conjugated polymers by controlling the interaction between solvents and conjugated polymers. By using the Hansen solubility parameter radius (Ra) to screen different polar and nonpolar solvents, we found that in nonpolar solvents with a larger Ra, the polymer exhibited strong intermolecular aggregation, while in solvents with a smaller Ra, the polymer showed almost no ordered aggregation. During the subsequent film formation process, we extended the crystallization time of the conjugated polymer by controlling the solvent atmosphere. Films prepared in nonpolar solvents with a larger Ra showed the formation of large‐sized fibers, exhibiting a mixed orientation of face‐on and edge‐on. On the other hand, films prepared in solvents with a smaller Ra formed smaller fibers, mainly with an edge‐on orientation. In‐situ film absorption spectroscopy indicated that the aggregation state of the polymer in nonpolar solvents with a larger Ra could be maintained through a memory effect during the film formation process, while the aggregation behavior of the polymer in solvents with a smaller Ra underwent significant changes. Ultimately, the films prepared in solvents with a larger Ra exhibited higher charge carrier mobility.
polymer science