Abstract:For the first time, N-(2-hydroxyl) propyl-3-trimethyl ammonium chitosan chloride (HTCC) was prepared through a fast, easy and efficient method with the assistance of microwave irradiation, and the quaternized chitosan was also degraded via the microwave irradiation. A comparative study was performed by using the conventional heating method to prepare HTCC. The structure and property of the quaternized chitosan obtained by these two methods were characterized by GPC, XRD, FTIR, NMR, TG and elemental analysis. It was shown that quaternized chitosan was successfully prepared within 50 min via microwave irradiation method, while a much longer time of 6-7 h was needed with the conventional heating method. The substitutions both occurred on the C2 position of chitosan with the two different methods, and their HTCC products had weight average similar molecular weight (Mw), structure and thermal stability. The HTCC prepared by the microwave irradiation method had a little lower degree of substitution (DS) than those prepared via conventional heating with the same mole ratio (6: 1) of the intermediate to chitosan. The degradation study showed that the Mw of HTCC decreased rapidly from 4.6 x 10(5) to 1.1 x 10(5) in 1 h under microwave irradiation, while it only decreased from 4.6 x 10(5) to 2.1 x 10(5) in 1 h through conventional heating degradation. These results revealed that microwave irradiation is a more efficient and environment-friendly way to obtain the water-soluble chitosan derivatives and their degraded products.

Preparation and Characterization of Quaternized Chitosan Under Microwave Irradiation

Ultrasound-assisted Synthesis of Chitosan from Fungal Precursors for Biomedical Applications

Three Dimensional Chitosan Rods Reinforced by Microwave Irradiation

Preparation and Characterization of N-succinyl-chitosan

Studies on Radiation Degradation of Chitosan in Aqueous Solutions

Synergetic Degradation of Chitosan with Gamma Radiation and Hydrogen Peroxide

Preparation and Structure of Chitosan Swellable in Alkali Solution by Ultrasonic Treatment

Effect of Conventional and Microwave Heating Treatment on Antioxidant Activity of Quinoa Protein after Simulated Gastrointestinal Digestion.

γ-ray degradation of chitosan to prepare water-soluble oligomers

Radiation Degradation of Chitosan in the Presence of H2o2

Study on the Water-Solubility of Chitosan Degraded with Gamma Radiation

Preparation and structure of chitosan soluble in wide pH range

Effect of 60Co irradiation on the properties of chitosan rod

Physicochemical modifications in microwave-irradiated chitosan: biopharmaceutical and medical applications

Discuss on the Craft of Quickly Make Lobster Chitosan by Microwave Radiation Method

Intervention of Microwave Irradiation on Structure and Quality Characteristics of Quinoa Protein Aggregates

Irradiation and sensitizing effects on chitosan degradation

Radical adducts formation mechanism of CH3CO2∙ and CH3CO3∙ realized decomposition of chitosan by plasma catalyzed peracetic acid

Radiation-induced Degradation of Carboxymethylated Chitosan in Aqueous Solution

Preparation and Characterization of Poly(ethylene Glycol)-G-chitosan with Water- and Organosolubility

Preparation of water-soluble oligochitosan by radiation degradation (1):Study on degradation method